Waterborne acrylic wood coating and preparation method thereof

A technology of water-based acrylic and wood coatings, which is applied in coatings and other directions, can solve problems such as lack of air purification and general adhesion, and achieve the effects of reducing production costs, good compatibility, and good affinity

Inactive Publication Date: 2016-06-15
HUZHOU GUOXIN MATERIALS
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the paint has some shortcomings: the adhesion is relatively general, and it does not have the function of purifying the air

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne acrylic wood coating and preparation method thereof
  • Waterborne acrylic wood coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Water-based acrylic wood coatings, including the following components by weight: 41 parts of water-based pure acrylic emulsion, 24 parts of starch emulsion, 2 parts of dipropylene glycol methyl ether, 1 part of silicone leveling agent, 1.2 parts of associative polyurethane thickener 2.4 parts of calcium naphthenate, 15 parts of water, 4.2 parts of tributyl phosphate, 0.1 part of Cathone, 9 parts of filler diatomaceous earth, and 0.7 parts of sodium polyacrylate.

[0030] The preparation method of this wood coating is:

[0031] (1) sweet potato starch, potato starch, purple potato starch that mass ratio is 3:3:1 is added in the phosphoric acid solution that mass concentration is 3%, the total weight of sweet potato starch, potato starch, purple potato starch and the weight of phosphoric acid solution The ratio is 1:3, stir the starch solution evenly into a slurry, move it into a constant temperature water bath, heat it to 50°C, stir and react at a constant temperature fo...

Embodiment 2

[0036] Water-based acrylic wood coatings, including the following components by weight: 43 parts of water-based pure acrylic emulsion, 22 parts of starch emulsion, 4 parts of dipropylene glycol methyl ether, 0.5 part of silicone leveling agent, 1.4 parts of associative polyurethane thickener 2.7 parts of calcium naphthenate, 17 parts of water, 4.4 parts of tributyl phosphate, 0.2 parts of Cathone, 11 parts of filler colloidal calcium carbonate, and 0.9 parts of sodium polyacrylate.

[0037] Its preparation method is identical with embodiment 1.

Embodiment 3

[0039] Water-based acrylic wood coatings, including the following components by weight: 45 parts of water-based pure acrylic emulsion, 20 parts of starch emulsion, 2.5 parts of dipropylene glycol methyl ether, 0.7 parts of silicone leveling agent, 1.1 parts of associative polyurethane thickener 2.5 parts of calcium naphthenate, 19 parts of water, 4.8 parts of tributyl phosphate, 0.1 part of Cathone, 13 parts of filler colloidal calcium carbonate, and 1 part of sodium polyacrylate.

[0040] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waterborne acrylic wood coating. The waterborne acrylic wood coating comprises, by weight, 40-45 parts of acrylic emulsion, 20-25 parts of starch emulsion, 2-4 parts of coalescing agent, 0.5-1 part of leveling agent, 1-1.5 parts of thickener, 2-3 parts of drier, 15-20 parts of water, 4-5 parts of fire retardant, 0.1-0.2 part of mildew-proof agent, 9-14 parts of filler and 0.5-1 part of sodium polyacrylate. The invention further provides a preparation method of the waterborne acrylic wood coating. The waterborne acrylic wood coating is high in adhesive force and capable of purifying air effectively.

Description

technical field [0001] The invention relates to a coating, in particular to a water-based acrylic wood coating and a preparation method thereof. Background technique [0002] Water-based wood coatings are water-based wood coatings that use water as the main solvent or can be diluted with water. They can be called water-based wood coatings. They have the same or similar functions as solvent-based wood coatings. They mainly protect and decorate wood. Water-based wood coatings The biggest difference between paints and solvent-based wood coatings is that they can be diluted with water. Due to the large amount of VOC (organic solvents) in solvent-based wood coatings, they participate in the oxidation reaction to form ozone under the action of sunlight and heat, resulting in poor air quality and summer smog, which is harmful to the earth's organisms. At the same time, VOC also causes great harm to the human body, mainly in the following ways: one is that the smell stimulates the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D151/02C09D7/12C08F251/00C08F220/06C08F220/14C08F220/18C08F212/08
CPCC08F251/00C08L2205/035C09D7/65C09D133/04C08L51/02C08L33/02C08K13/02C08K3/36C08K5/521C08K5/098C08F220/1804
Inventor 董芬芳
Owner HUZHOU GUOXIN MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com