Polyvinyl chloride plastic with toughening effect

A polyvinyl chloride and plastic technology, which is applied in the field of modified plastics and plastics, can solve the problems of short use time, insufficient toughness, and damage, and achieve the effect of reducing costs and increasing service life.

Inactive Publication Date: 2016-06-08
SUZHOU NEW DISTRICT HUASHIDA ENG PLASTICS
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing polyvinyl chloride plastics are not tough enough, tend to be brittle, and will break if they are not used for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Provide a kind of polyvinyl chloride plastic with toughening effect, the component that comprises has polyvinyl chloride, MBS resin, basic magnesium sulfate whisker, tribasic lead sulfate, dibasic lead phosphite and talcum powder, described The polyvinyl chloride plastic with toughening effect is calculated in parts by weight, and the components included are: 100 parts of polyvinyl chloride, 8 parts of MBS resin, 10 parts of basic magnesium sulfate whiskers, 3 parts of tribasic lead sulfate, dibasic Formula lead phosphite 4 parts, talcum powder 0.8 part. The MBS resin is a terpolymer of methyl methacrylate, butadiene and styrene. The tensile strength of the polyvinyl chloride plastic is 40MPa.

Embodiment 2

[0013] Provide a kind of polyvinyl chloride plastic with toughening effect, the component that comprises has polyvinyl chloride, MBS resin, basic magnesium sulfate whisker, tribasic lead sulfate, dibasic lead phosphite and talcum powder, described The polyvinyl chloride plastic with toughening effect includes the following components in parts by weight: 100 parts of polyvinyl chloride, 6 parts of MBS resin, 8 parts of basic magnesium sulfate whiskers, 4 parts of tribasic lead sulfate, dibasic Formula lead phosphite 5 parts, talcum powder 0.5 part. The MBS resin is a terpolymer of methyl methacrylate, butadiene and styrene. The tensile strength of the polyvinyl chloride plastic is 45MPa.

Embodiment 3

[0015] Provide a kind of polyvinyl chloride plastic with toughening effect, the component that comprises has polyvinyl chloride, MBS resin, basic magnesium sulfate whisker, tribasic lead sulfate, dibasic lead phosphite and talcum powder, described The polyvinyl chloride plastic with toughening effect includes the following components in parts by weight: 100 parts of polyvinyl chloride, 9 parts of MBS resin, 12 parts of basic magnesium sulfate whiskers, 2 parts of tribasic lead sulfate, dibasic Formula lead phosphite 3 parts, talcum powder 1 part. The MBS resin is a terpolymer of methyl methacrylate, butadiene and styrene. The tensile strength of the polyvinyl chloride plastic is 35MPa.

[0016] The beneficial effects of the present invention are:

[0017] 1. The polyvinyl chloride plastic with toughening effect can prevent the plastic from being brittle when used at room temperature or low temperature for a long time, ensuring the use value of the plastic;

[0018] 2. The p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyvinyl chloride plastic with a toughening effect, which comprises the following components in parts by weight: 100 parts of polyvinyl chloride, 6 to 9 parts of MBS (methyl methacrylate) resin, 8 to 12 parts of basic magnesium sulfate whisker, 2 to 4 parts of tribasic lead sulfate, 3 to 5 parts of dibasic lead phosphite, and 0.5 to 1 part of talcum powder. In the mode, the polyvinyl chloride plastic with the toughening effect, which is disclosed by the invention, is prevented from showing brittle when used for a long time in a room-temperature or low-temperature environment, so that the plastic always has a use value, the service life of the plastic can be prolonged, the plastic does not need to be replaced continuously, and accordingly, the cost is lowered.

Description

technical field [0001] The invention relates to the field of modified plastics, in particular to a polyvinyl chloride plastic with a toughening effect. Background technique [0002] Polyvinyl chloride plastic is polymerized from vinyl chloride monomer and is one of the most commonly used thermoplastics. Pure polyvinyl chloride resin is a hard thermoplastic substance, its decomposition temperature is very close to the plasticizing temperature, and its mechanical strength is poor. Therefore, polyvinyl chloride resin cannot be used to mold products, and plasticizers, stabilizers, fillers, etc. must be added to improve performance to make polyvinyl chloride plastics, and then processed into various products. Existing polyvinyl chloride plastics are not tough enough, tend to be brittle, and will break if they are not used for a long time. Contents of the invention [0003] The main technical problem to be solved by the invention is to provide a polyvinyl chloride plastic with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08K13/04C08K7/08C08K3/30C08K3/32C08K3/34
CPCC08L27/06
Inventor 徐春华
Owner SUZHOU NEW DISTRICT HUASHIDA ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap