Environment-friendly concrete sidewalk brick

An environment-friendly concrete and sidewalk technology, applied in ceramic molding machines, sustainable waste treatment, solid waste management, etc., can solve the problems of insufficient strength of sidewalk bricks, impact on the ecological environment, unfavorable ecological balance, etc., and achieve convenient construction and high water seepage rate Heightening, strength-increasing effect

Inactive Publication Date: 2016-05-04
周琴霞
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, with the increasing scale of urban residential renewal and municipal relocation, many concrete buildings and structures need to be demolished for redesign and construction, and these demolished waste concrete are often stacked in the wild without rational use, affecting the ecology environment, not conducive to ecological balance
In addition, due to the characteristics of sidewalk bricks, it is required to be able to seep water quickly and have a certain strength. However, the environmental protection concrete sidewalk bricks of the prior art all use gravel or sand or cinder as aggregates, while quarrying and sand mining are damaged. The ecological environment is damaged, and the strength of sidewalk bricks prepared from cinders is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] (1) Crush the waste concrete as the waste concrete aggregate, requiring the crushing value to be less than 20%, the mud content to be less than 3%, and the particle size to be single-graded from 20mm to 40mm;

[0013] (2) 65% of diatomite, 20% of zeolite, and 15% of Echinacea purpurea extract are mixed to make concrete alkaline neutralizer;

[0014] (3) According to water: cement: waste concrete aggregate or tailings is 0.4:1:4, water, ordinary portland cement labeled as 52.5R, waste concrete aggregate of step (1) and step (2) Mix the concrete alkaline neutralizer with a mixer and stir evenly. The concrete alkaline neutralizer is 25% of the amount of cement;

[0015] (4) Pouring and pounding the prefabricated mold with the stirred material;

[0016] (5) Carry out maintenance, maintenance condition: temperature is 25 ℃, and humidity is 45%;

[0017] (6) After the mold is removed, it is the finished product.

Embodiment 2

[0019] (1) Crush the tailings as the aggregate, requiring the crushing value to be less than 20%, the mud content to be less than 3%, the particle size to be 20mm to 40mm in a single grade, and 30% of the tailings to be used as expanded pearls rock mixture, the particle size of expanded perlite is less than 30mm;

[0020] (2) 55% of diatomite, 40% of zeolite, and 5% of Echinacea purpurea extract are mixed to make concrete alkaline neutralizer;

[0021] (3) According to water: cement: waste concrete aggregate or tailings is 0.43:1:4, water, ordinary portland cement labeled as 52.5R, waste concrete aggregate of step (1) and step (2) Mix the concrete alkaline neutralizer with a mixer and stir evenly. The concrete alkaline neutralizer is 23% of the amount of cement;

[0022] (4) Pouring and pounding the prefabricated mold with the stirred material;

[0023] (5) Carry out maintenance, maintenance condition: temperature is 25 ℃, and humidity is 45%;

[0024] (6) After the mold is...

Embodiment 3

[0026] (1) Crush the tailings as the aggregate, requiring the crushing value to be less than 20%, the mud content to be less than 3%, the particle size to be 20mm to 40mm in a single grade, and 20% of the amount of tailings to be expanded pearls rock mixture, the particle size of expanded perlite is less than 30mm;

[0027] (2) 60% of diatomite, 30% of zeolite, and 10% of Echinacea purpurea extract are mixed to make concrete alkaline neutralizer;

[0028] (3) According to water: cement: waste concrete aggregate or tailings is 0.46:1:4, water, ordinary portland cement labeled as 52.5R, waste concrete aggregate of step (1) and step (2) Mix with the concrete alkaline neutralizer, stir evenly with a mixer, the concrete alkaline neutralizer is 22% of the cement dosage;

[0029] (4) Pouring and pounding the prefabricated mold with the stirred material;

[0030] (5) Carry out maintenance, maintenance condition: temperature is 25 ℃, and humidity is 45%;

[0031] (6) After the mold ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly concrete sidewalk brick. The brick is prepared from water, cement, waste concrete aggregate or tailings, and a concrete antalkali, wherein the specific mix proportion is that water to cement to waste concrete aggregate or tailings is (0.4 to 0.46) to 1 to 4; the using amount of the concrete antalkali is 22 to 25 percent of that of the cement; the concrete antalkali is prepared from 55 to 65 percent by weight of kieselguhr, 20 to 40 percent by weight of zeolite, and 5 to 15 percent of echinacea extract, the cement is ordinary portland cement with a mark number of 52.5R. Compared with the prior art, the brick provided by the invention has the characteristics that the overall performance is good and environmental friendliness is realized and protective effect is realized.

Description

Technical field: [0001] The invention relates to an environment-friendly concrete sidewalk brick. Background technique: [0002] At present, with the increasing scale of urban residential renewal and municipal relocation, many concrete buildings and structures need to be demolished for redesign and construction, and these demolished waste concrete are often stacked in the wild without rational use, affecting the ecology The environment is not conducive to ecological balance. In addition, due to the characteristics of sidewalk bricks, it is required to be able to seep water quickly and have a certain strength. However, the environmental protection concrete sidewalk bricks of the prior art all use crushed stones or sandstone or cinder as aggregates, while quarrying and sand mining are destroyed. The ecological environment is damaged, and the strength of sidewalk bricks prepared from cinders is not enough. Invention content: [0003] The object of the present invention is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/16C04B18/12B28B11/24
CPCB28B11/247C04B18/12C04B18/16C04B28/04C04B2111/00017C04B2111/0075C04B14/08C04B14/047C04B2103/69C04B14/185Y02W30/91
Inventor 周琴霞
Owner 周琴霞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com