Propylene polymer and preparation method thereof
A technology of propylene polymers and compounds, applied in the field of propylene polymers, can solve the problems of increasing the cost of polypropylene resins, problems in product separation, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0028] The present invention also provides a method for preparing a propylene polymer, the method comprising: under olefin polymerization conditions, in the presence of a catalyst, propylene or propylene and ethylene and / or selected from C 4 -C 8 A mixture of α-olefins is polymerized, the catalyst contains a solid component, an alkylaluminum compound and optionally an external electron donor compound, the solid component comprising the reaction product of the following components:
[0029] (i) magnesium compound, described magnesium compound is the magnesium compound shown in formula (1) or formula (2);
[0030] (ii) at least one titanium compound;
[0031] (iii) at least one internal electron donor; and
[0032] (iv) oxirane compounds represented by formula (3),
[0033] (R 1 O) m MgT n Formula (1), MgX k (R 4 Oh) p (H 2 O) q Formula (2),
[0034] Formula (3),
[0035] Among them, T is
[0036] R 1 and R 4 the same or different, each independently as C 1 ...
preparation example 1
[0140] This preparation example is used to illustrate the catalyst component for olefin polymerization provided by the present invention and its preparation method.
[0141] (1) In a 1.6L reactor, add 200mL No. 5 white oil (Sigma-Aldrich Company), 8.0g (0.084mol) magnesium chloride, 6g surfactant span80 (Sigma-Aldrich Company), 100mL (1.70mol) ethanol in sequence , under stirring, the temperature was raised to 90°C. After reacting at constant temperature for 1 hour, the resulting mixture was stirred and dispersed for 30 minutes for emulsification. And add 25mL (0.32mol) epichlorohydrin in the obtained emulsification product, maintain temperature reaction 0.5 hour, carry out pressure filtration then, filter off liquid, wash 5 times with hexane, vacuum-dry, obtain magnesium compound A1, through infrared spectrum Law and 1 H-NMR method is measured, and magnesium compound A1 structural formula is as follows formula (8) expression (R 1 is ethyl, R 2 for hydrogen, R 3 is chloro...
preparation example 2
[0145] This preparation example is used to illustrate the catalyst component for olefin polymerization provided by the present invention and its preparation method.
[0146] (1) The magnesium-containing compound is prepared according to the disclosed method of Example 1 in CN1718595A, specifically as follows:
[0147] In a stirred 150L reactor, 10kg (105mol) of magnesium chloride and 12.6kg (273mol) of ethanol were added into 60L of white oil with a viscosity of 30 centipoise (20°C) and reacted at 125°C for 2 hours. Then transfer the mixture of molten adduct and white oil to the medium of methyl silicone oil which has been preheated to 125°C; the viscosity of methyl silicone oil is 300 centipoise (20°C), and the amount of methyl silicone oil is 120L ; Stir at a speed of 200 rpm for 10-30 minutes to obtain a mixed solution. Introduce the mixed solution into a high-gravity rotating bed for dispersion, and introduce the dispersed mixed solution into a hexane medium that has been...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com