Nano composite diatom ooze coating and preparation method thereof

A composite diatom mud and nano technology, applied in the direction of coating, etc., can solve the problems of easy secondary agglomeration, inability to fully decompose formaldehyde, and ineffective reduction of formaldehyde content, etc., to achieve strong ion exchange, prevent agglomeration effect, strong adsorption effect

Inactive Publication Date: 2016-03-16
上海源由纳米科技有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nano-precious metal powder of this kind of diatom mud product is difficult to disperse in the product, and it is easy to agglomerate for the second time, so it cannot fully exert the effect of decomposing formaldehyde
[0004] The existing diatom mud coating adopts the gradual addition of nano-metal powder and nano-metal oxide powder, which is prone to agglomeration effect and cannot effectively reduce the content of formaldehyde in the air.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a nanocomposite diatom mud coating, and its specific formula is: 1% cellulose, 8% tourmaline, 8% titanium dioxide, 5% kaolin, 5% sepiolite powder, 50% diatomite, Nano precious metal supported catalyst 5%, nano activated carbon 4%, leveling agent 0.5%, thickener 4%, redispersible latex powder 9%, pigment 0.5%, and add 25% ingredients (above components) total Quality water for thorough mixing.

[0034] Wherein, the above-mentioned nano-noble metal supported catalyst is 1% Pt / CeO 2 Catalyst (purchased from Sinopharm Group Chemical Reagent Co., Ltd.), the leveling agent is polyether modified polydimethylsiloxane (specifically polyether modified dimethylsiloxane BKY-300), and the leveling agent The thickener is hydroxypropyl methylcellulose, the redispersible latex powder is an ethylene / vinyl acetate copolymer (specifically ethylene / vinyl acetate copolymer MS-6090N), and the pigment is iron red.

Embodiment 2

[0036] This embodiment provides a nanocomposite diatom mud coating, and its specific formula is: 1% cellulose, 5% tourmaline, 10% titanium dioxide, 10% kaolin, 8% sepiolite powder, 45% diatomite, Nano-precious metal-supported catalyst 7%, nano-activated carbon 3%, leveling agent 0.5%, thickener 4%, redispersible latex powder 6%, pigment 0.5%, and add 25% of the total mass of ingredients in water for thorough mixing , get the product.

[0037] Wherein, the above-mentioned nanometer noble metal supported catalyst is 1% Pt / TiO 2 Catalyst (purchased from Sinopharm Chemical Reagent Co., Ltd.), the leveling agent is polyether modified dimethyl siloxane (specifically polyether modified dimethyl siloxane BKY-300), the thickener The agent is hydroxypropyl methylcellulose, the redispersible latex powder is an ethylene / vinyl acetate copolymer (specifically ethylene / vinyl acetate copolymer MS-6090N), and the pigment is iron red.

Embodiment 3

[0039] This embodiment provides a nanocomposite diatom mud coating, its specific formula is: 1.5% of cellulose, 10% of tourmaline, 5% of titanium dioxide, 10% of kaolin, 8% of sepiolite powder, 35.7% of diatomite, 10% of nano precious metal supported catalyst, 5% of nano activated carbon, 0.8% of leveling agent, 3% of thickener, 10% of redispersible latex powder, 1% of pigment, and add 25% of the total weight of ingredients to mix thoroughly , get the product.

[0040] Wherein, the above-mentioned nano-noble metal supported catalyst is 5% Pt / TiO 2Catalyst (purchased from Sinopharm Chemical Reagent Co., Ltd.), the leveling agent is polyether modified dimethyl siloxane (specifically polyether modified dimethyl siloxane BKY-300), the thickener The agent is hydroxypropyl methylcellulose, the redispersible latex powder is an ethylene / vinyl acetate copolymer (specifically ethylene / vinyl acetate copolymer MS-6090N), and the pigment is iron oxide yellow.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nano composite diatom ooze coating including a solvent and the following components with the total mass of 100%: 0.5-1.8% of cellulose, 5-18% of tourmaline, 5-15% of titanium dioxide, 4-18% of kaolin, 5-12% of a sepiolite powder, 35-55% of diatomite, 5-12% of a nano noble metal loaded type catalyst, 1-6% of nano activated carbon, 0.5-0.8% of a levelling agent, 1.5-5% of a thickener, 7-16% of a re-dispersible latex powder, and 0-5% of a pigment. The solvent is preferably water, and the amount of the water is 20-30%, preferably 25%, of the total mass of all the components. Nano noble metal particles are loaded on a carrier firstly and then mixed with other powders, so as to prevent an agglomeration effect of the nano noble metal particles. The prepared nano composite diatom ooze coating has extremely strong adsorption and ion exchange, can adsorb formaldehyde in air, and decomposes formaldehyde and other harmful gases under the action of the catalyst.

Description

technical field [0001] The invention relates to a coating, in particular to a nano-composite diatom mud coating and a preparation method thereof. Background technique [0002] In recent years, the wide application of coatings has attracted more and more researchers. With the improvement of people's living standards, environmental protection, low carbon, energy saving, etc. have become the trend of modern home decoration. [0003] Diatom mud has a unique molecular sieve and adsorption function, which can effectively absorb free formaldehyde, benzene, ammonia and other harmful substances in the air. By releasing water and negative oxygen ions, it can keep the indoor air fresh for a long time. However, it is difficult to disperse the nano-precious metal powder of this type of diatom mud product in the product, and it is easy to agglomerate for the second time, so it cannot fully exert the effect of decomposing formaldehyde. [0004] The existing diatom mud coating adopts the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/08C09D7/12
Inventor 高源黎慧茹爱华
Owner 上海源由纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com