Blended yarn

A blended yarn, fully mixed technology, used in textiles and papermaking, fiber processing, biochemical fiber processing and other directions, can solve the problems of unable to meet customer requirements, single performance of blended yarn, etc., to achieve excellent anti-mildew effect.

Inactive Publication Date: 2016-03-09
常熟市明达腈纺有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The performance of the existing blended yarn is single, which cannot meet the requirements of customers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of blended yarn, it is through padding treatment, and this padding treatment comprises the steps:

[0021] 1) Add 1-2 parts by weight of alkanolamide polyoxyethylene ether, 1.8 parts by weight of sodium pyrophosphate, 2.6 parts by weight of bamboo acetic acid, and 1.9 parts by weight of benzoic acid into 18.3 parts by weight of deionized water, and stir evenly;

[0022] 2) At the same time, slowly add 0.8 parts by weight of aluminum hydroxide, 0.9 parts by weight of honeysuckle extract, 1.1 parts by weight of tea polyphenols, and 1.4 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully Mix evenly to prepare finishing liquid;

[0023] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 2

[0025] Blended yarn, it is through padding treatment, and this padding treatment comprises the steps:

[0026] 1) Add 1 part by weight of alkanolamide polyoxyethylene ether, 1.8 parts by weight of sodium pyrophosphate, 2.6 parts by weight of bamboo acetic acid, and 1.9 parts by weight of benzoic acid into 18.3 parts by weight of deionized water, and stir evenly;

[0027] 2) At the same time, slowly add 0.8 parts by weight of aluminum hydroxide, 0.9 parts by weight of honeysuckle extract, 1.1 parts by weight of tea polyphenols, and 1.4 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully Mix evenly to prepare finishing liquid;

[0028] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 3

[0030] Blended yarn, it is through padding treatment, and this padding treatment comprises the steps:

[0031] 1) Put 2 parts by weight of alkanolamide polyoxyethylene ether, 1.8 parts by weight of sodium pyrophosphate, 2.6 parts by weight of bamboo acetic acid, and 1.9 parts by weight of benzoic acid into 18.3 parts by weight of deionized water, and stir evenly;

[0032] 2) At the same time, slowly add 0.8 parts by weight of aluminum hydroxide, 0.9 parts by weight of honeysuckle extract, 1.1 parts by weight of tea polyphenols, and 1.4 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully Mix evenly to prepare finishing liquid;

[0033] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses blended yarn. The blended yarn is treated in a padding mode, and the padding treatment includes the following steps that firstly, by weight, 1-2 parts of alkylolamide polyoxy ethane ether, 1.8 parts of sodium pyrophosphate, 2.6 parts of bamboo vinegar and 1.9 parts of benzoic acid are thrown into 18.3 parts of deionized water, and the mixture is stirred uniformly; secondly, by weight, 0.8 part of aluminum hydroxide, 0.9 part of honeysuckle extract, 1.1 parts of tea polyphenol and 1.4 parts of octadecyl dimethyl ethoxyl ammonium nitrate are added slowly at the same time, and the mixture continues to be stirred to be fully and uniformly mixed to prepare finishing liquid; thirdly, the blended yarn is treated in the padding mode in the finishing liquid, taken out and then dried at the constant temperature. The blended yarn has excellent mould-proof, mothproof, antibacterial, flame-retardant and anti-static performance.

Description

technical field [0001] This invention relates to blended yarns. Background technique [0002] The performance of the existing blended yarn is single, which cannot meet the requirements of customers. Contents of the invention [0003] The object of the present invention is to provide a blended yarn with excellent mildewproof, mothproof, antibacterial, flame retardant and antistatic properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of blended yarn, which is processed through padding, and the padding process includes the following steps: [0005] 1) Add 1-2 parts by weight of alkanolamide polyoxyethylene ether, 1.8 parts by weight of sodium pyrophosphate, 2.6 parts by weight of bamboo acetic acid, and 1.9 parts by weight of benzoic acid into 18.3 parts by weight of deionized water, and stir evenly; [0006] 2) At the same time, slowly add 0.8 parts by weight of aluminum hydroxide, 0.9 parts by weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/45D06M11/72D06M13/00D06M13/152D06M13/17D06M13/188D06M13/46D06M15/00D06M15/53
CPCD06M15/53D06M11/45D06M11/72D06M13/00D06M13/152D06M13/17D06M13/1845D06M13/188D06M13/46D06M15/00D06M16/00D06M16/006D06M2200/30
Inventor 缪栋华
Owner 常熟市明达腈纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More