Wastewater absorbing material for chemical enterprise

An adsorption material and enterprise technology, applied in adsorption water/sewage treatment, other chemical processes, chemical instruments and methods, etc., can solve the problems of incomplete removal of pollutants, high working pressure, frequent cleaning, etc., to achieve good social benefits and Economic value, good water quality purification, easy cleaning effect

Inactive Publication Date: 2016-01-27
王璐
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most domestic industrial enterprises use reverse osmosis membrane (RO) technology for process wastewater reuse treatment, but existing RO treatmen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A waste water adsorption material used in chemical enterprises, made of the following raw materials in parts by weight:

[0011] 9 parts of sodium fatty alcohol polyoxyethylene ether sulfonate, 3 parts of sodium citrate, 4 parts of pectinase, 5 parts of aliphatic polyoxyethylene ether, 2 parts of carboxylate, 5 parts of ammonium oxide salt, and 4 parts of hollow glass microspheres 3 parts of diatomite, 4 parts of citric acid, 7 parts of wood fiber, 5 parts of graphite powder, 4 parts of nano-calcium sulfate, 2 parts of titanate coupling agent, 2 parts of stearic acid, 4 parts of high-density polyethylene , 2 parts of n-pentanol.

Embodiment 2

[0013] A waste water adsorption material used in chemical enterprises, made of the following raw materials in parts by weight:

[0014] 14 parts of sodium fatty alcohol polyoxyethylene ether sulfonate, 8 parts of sodium citrate, 8 parts of pectinase, 10 parts of aliphatic polyoxyethylene ether, 6 parts of carboxylate, 7 parts of ammonium oxide salt, and 6 parts of hollow glass microspheres 8 parts of diatomite, 9 parts of citric acid, 11 parts of wood fiber, 10 parts of graphite powder, 10 parts of nano-calcium sulfate, 6 parts of titanate coupling agent, 5 parts of stearic acid, 8 parts of high-density polyethylene , 7 parts of n-pentanol.

Embodiment 3

[0016] A waste water adsorption material used in chemical enterprises, made of the following raw materials in parts by weight:

[0017] 11 parts of sodium fatty alcohol polyoxyethylene ether sulfonate, 5 parts of sodium citrate, 6 parts of pectinase, 8 parts of aliphatic polyoxyethylene ether, 4 parts of carboxylate, 6 parts of ammonium oxide salt, and 5 parts of hollow glass microspheres 6 parts of diatomite, 7 parts of citric acid, 9 parts of wood fiber, 7 parts of graphite powder, 7 parts of nano-calcium sulfate, 4 parts of titanate coupling agent, 3 parts of stearic acid, 6 parts of high-density polyethylene , 4 parts of n-pentanol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wastewater absorbing material for a chemical enterprise. The wastewater absorbing material is prepared from the following raw materials in parts by weight: 9 to 14 parts of sodium fatty alcohol polyoxyethylene ether sulfonate, 3 to 8 parts of sodium citrate, 4 to 8 parts of pectinase, 5 to 10 parts of aliphatic polyoxyethylene ether, 2 to 6 parts of carboxylate, 5 to 7 parts of ammonium oxide, 4 to 6 parts of hollow glass microspheres, 3 to 8 parts of diatomite, 4 to 9 parts of citric acid, 7 to 11 parts of wood fiber, 5 to 10 parts of graphite powder, 4 to 10 parts of nanometer calcium sulphate, 2 to 6 parts of titanate coupling agent, 2 to 5 parts of stearic acid, 4 to 8 parts of high-density polyethylene and 2 to 7 parts of n-pentyl alcohol. The wastewater absorbing material has the beneficial effects that toxic chemicals in wastewater can be well absorbed; meanwhile, the wastewater absorbing material is easy to clean; water quality can be well purified; the social benefit and the economic value are very good.

Description

technical field [0001] The invention relates to a waste water adsorption material used in chemical enterprises. Background technique [0002] At present, most domestic industrial enterprises use reverse osmosis membrane (RO) technology for process wastewater reuse treatment, but existing RO treatment processes generally have disadvantages such as easy clogging, frequent cleaning, incomplete removal of pollutants, low water production, and high working pressure. . At the same time, for the discharged wastewater, a reducing agent is generally added to remove those metal ions present in the wastewater without reducing the heavy metal ions, and iron powder is used as a reducing agent. There is a need for a simple and convenient material that can effectively treat sewage at the same time. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the technical problem to be solved by the present invention is to provide a waste water adsorption material us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/26B01J20/30C02F1/28
Inventor 王璐
Owner 王璐
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap