A kind of nano-graphite modified powder release agent for valve body casting

A technology of nano-graphite powder and nano-graphite, which is applied in the direction of casting molding equipment, casting molds, casting mold components, etc., can solve the problems of affecting the quality of valve body blanks, increasing production input costs, short service life, etc., and achieves good demoulding effect , Long service life, easy to use

Active Publication Date: 2017-08-25
HEXIAN KEJIA VALVE CASTING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The valve body release agent currently used has the characteristics of poor release effect and short service life, which will not only affect the quality of the valve body blank, but also increase the production input cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A nano-graphite modified powder release agent for valve body casting, made of the following raw materials in parts by mass:

[0026] 60 parts of polyethylene wax powder, 15 parts of nano-graphite powder, 12 parts of calcined kaolin, 11 parts of cork powder, 8 parts of titanium dioxide, 7 parts of butter, 5 parts of silicon micropowder, 4 parts of carboxymethyl chitosan, 3 parts of concentrated hydrochloric acid 2 parts, 2 parts of lauric acid, 40 parts of n-heptane, 25 parts of toluene, 65 parts of water;

[0027] Its preparation method comprises the following steps:

[0028] (1) First place the nano-graphite powder at 45-50°C for 2 hours in vacuum, then calcinate at 350-400°C for 3 hours to obtain calcined nano-graphite powder;

[0029] (2) Fully dissolve polyethylene wax powder in a mixed solvent of n-heptane and toluene, then add calcined nano-graphite powder and concentrated hydrochloric acid, disperse evenly, and microwave at a microwave frequency of 2450MHz and a...

Embodiment 2

[0034] A nano-graphite modified powder release agent for valve body casting, made of the following raw materials in parts by mass:

[0035] 65 parts of polyethylene wax powder, 15 parts of nano-graphite powder, 13 parts of calcined kaolin, 11 parts of cork powder, 9 parts of titanium dioxide, 8 parts of butter, 6 parts of silicon micropowder, 5 parts of carboxymethyl chitosan, 3 parts of concentrated hydrochloric acid parts, 2 parts of lauric acid, 45 parts of n-heptane, 30 parts of toluene, and 65 parts of water.

[0036] The preparation method of the release agent of this embodiment is the same as that of Example 1.

Embodiment 3

[0038] A nano-graphite modified powder release agent for valve body casting, made of the following raw materials in parts by mass:

[0039] 70 parts of polyethylene wax powder, 18 parts of nano-graphite powder, 15 parts of calcined kaolin, 13 parts of cork powder, 10 parts of titanium dioxide, 9 parts of butter, 7 parts of silicon micropowder, 6 parts of carboxymethyl chitosan, 4 parts of concentrated hydrochloric acid parts, 3 parts of lauric acid, 45 parts of n-heptane, 30 parts of toluene, and 70 parts of water.

[0040] The preparation method of the release agent of this embodiment is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nano-graphite modified powder release agent for valve body casting, relates to the technical field of release agent production, and is made of the following raw materials in parts by mass: 60-70 parts of polyethylene wax powder, nano-graphite powder 15‑18 parts, calcined kaolin 12‑15 parts, cork powder 10‑13 parts, titanium dioxide 8‑10 parts, butter 6‑9 parts, silicon micropowder 5‑7 parts, carboxymethyl chitosan 4‑6 parts , 3-4 parts of concentrated hydrochloric acid, 2-3 parts of lauric acid, 40-45 parts of n-heptane, 25-30 parts of toluene, and 60-70 parts of water. The mold release agent prepared by the invention has good demoulding effect, can be demoulded after the valve body is fully cooled and shaped, does not affect the dimensional accuracy and surface quality of the valve body, and has a long service life.

Description

[0001] Technical field: [0002] The invention relates to the technical field of release agent production, in particular to a nano-graphite modified powder release agent for valve body casting. [0003] Background technique: [0004] The valve body is a major part of the valve. There are different mechanical manufacturing methods according to the pressure level, such as casting and forging. Generally, the valve body of the medium and low pressure specifications is usually produced by the casting process. Casting is one of the basic processes of the modern device manufacturing industry. It is a process in which metals are melted into liquids that meet certain requirements and poured into molds, cooled and solidified, and cleaned to obtain castings with predetermined shapes, sizes and properties. Because the casting blank is almost shaped, it achieves the purpose of free machining or a small amount of machining, which reduces the cost and reduces the production time to a certain ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00
Inventor 黎宏
Owner HEXIAN KEJIA VALVE CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap