Memory fabric manufacturing technique

A production process and memory fabric technology, applied in the field of spinning, can solve problems such as improper process control, low production efficiency of looms, and uneven tension

Inactive Publication Date: 2015-09-30
NANTONG YUEDA KNITTING GARMENT
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chinese patent CN101220536, a high-shrinkage polyester low-stretch yarn with PTT performance and its production process, using the orthogonal experimental statistical method to obtain a group or array of process parameters and related product data, from which the most reasonable process can be obtained Parameters and product performance indicators are continuously optimized on this basis to obtain process parameters and produce related products. This invention patent is suitable for the production process of high-shrinkage polyester low-elastic yarn with PTT performance, and the PTT produced The product has a high defect rate, large loss of raw materials, low loom production efficiency, improper process control, easy to produce uneven tension, rough dyeing and finishing treatment, and severely damaged fabric memory function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A production process of a memory fabric, which uses PPT silk as a raw material, and is produced through the steps of warping, shrinking, sizing, paralleling, splitting, drafting, weaving and desizing. The specific steps are as follows:

[0017] The first step, warping: warp the PTT silk in batches, wind it into a PTT silk pulp shaft, the warping speed is 220 m / min, and the hardness of the pulp shaft is 70%; The pressure is 0.15Mpa;

[0018] The second step, zooming: store the paddle shaft in an air-conditioned cold room, and zoom in and out for 40 hours;

[0019] The third step, sizing yarn: the PTT yarn after warping is passed through the size tank to soak the slurry, the slurry concentration is 10%, the temperature is 41°C, and the sizing rate is 5%; then it is dried in a drying room to make PTT coated with a size film Shaft, drying room temperature is 120°C, PTT shaft hardness is 70%; sizing and drying continuous processing speed is 240 m / min, PTT wire elongation is...

Embodiment 2

[0026] A production process of a memory fabric, which uses PPT silk as a raw material, and is produced through the steps of warping, shrinking, sizing, paralleling, splitting, drafting, weaving and desizing. The specific steps are as follows:

[0027] The first step, warping: warp the PTT silk in batches, wind it into a PTT silk pulp shaft, the warping speed is 360 m / min, and the hardness of the pulp shaft is 78%; The pressure is 0.25Mpa;

[0028] The second step, zooming: store the paddle shaft in an air-conditioned cold room, and zoom in and out for 50 hours;

[0029] The third step, sizing yarn: the PTT yarn after warping is soaked in the slurry through the size tank, the slurry concentration is 16%, the temperature is 48°C, and the sizing rate is 7%; then it is dried in a drying room to make PTT coated with a size film Shaft, drying room temperature is 129°C, PTT shaft hardness is 79%; sizing and drying continuous processing speed is 270 m / min, PTT wire elongation is con...

Embodiment 3

[0036] A production process of a memory fabric, which uses PPT silk as a raw material, and is produced through the steps of warping, shrinking, sizing, paralleling, splitting, drafting, weaving and desizing. The specific steps are as follows:

[0037] The first step, warping: the PTT silk is warped in batches, wound into a PTT silk slurry shaft, the warping speed is 260 m / min, and the hardness of the slurry shaft is 74%; The pressure is 0.2Mpa;

[0038] The second step, zooming: store the paddle shaft in an air-conditioned cold room, and zoom in and out for 45 hours;

[0039] The third step, sizing yarn: the PTT yarn after the warping is passed through the size tank to pad the slurry, the slurry concentration is 13%, the temperature is 44°C, and the sizing rate is 6%; then it is dried in a drying room to make PTT coated with a size film Shaft, drying room temperature is 124°C, PTT shaft hardness is 74%; sizing and drying continuous processing speed is 250 m / min, PTT wire elon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a memory fabric manufacturing technique. PPT silk is used and serves as a raw material, the memory fabric manufacturing technique comprises the steps of beam warping, scaling, silk sizing, re-beaming, leasing, drafting, weaving and desizing, and memory fabric is obtained. The memory fabric manufacturing technique has the advantages that the memory fabric manufacturing technique is provided, and the complete no-iron effect is achieved.

Description

technical field [0001] The invention relates to the technical field of spinning, in particular to a production process of a memory fabric. Background technique [0002] Chinese patent CN101220536, a high-shrinkage polyester low-stretch yarn with PTT performance and its production process, using the orthogonal experimental statistical method to obtain a group or array of process parameters and related product data, from which the most reasonable process can be obtained Parameters and product performance indicators are continuously optimized on this basis to obtain process parameters and produce related products. This invention patent is suitable for the production process of high-shrinkage polyester low-elastic yarn with PTT performance, and the PTT produced The product has a high defect rate, a large loss of raw materials, low loom production efficiency, improper process control, easy to produce uneven tension, rough dyeing and finishing treatment, and severely damaged fabri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02H3/00D06B3/04D02H9/00
Inventor 卢兵
Owner NANTONG YUEDA KNITTING GARMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com