Flame-retardant coating adhesive for textiles, method for finishing flame-retardant fabric thereof, and flame-retardant fabric thereof

A technology of flame retardant coating and flame retardant fabric, which is applied in the field of flame retardant fabric, can solve the problems of large amount of flame retardant, unsatisfactory flame retardant effect, non-ideal flame retardant durability, complicated process, etc., and achieve good flame retardant and flame retardant Combustion durability, excellent anti-dripping effect, and the effect of extending the diffusion channel

Active Publication Date: 2016-09-14
EASTERN LIAONING UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, Chinese patents CN200810104239.8 and 200810063134.2 both use composite flame-retardant coating glue on polyester fabrics, but halogen-containing flame retardants are more and more restricted or even banned due to the problems of harming the human body and being unfriendly to the environment. In addition, the flame retardant performance achieved is limited, and the actual amount of flame retardant is also relatively large, which makes the fabric heavier.
Another Chinese patent: 2012105785875 also adopts the method of composite flame retardant coating glue, which is prepared from bisphenol F diglycidyl ether, epoxy resin, 2-phenylimidazole, and triglycidyl isocyanurate. Resin flame retardant, this technical solution is not ideal in terms of flame retardant efficiency, and the process is complicated and the cycle is long
[0005] In the article "Preparation and Application of Ammonium Polyphosphate Flame-Retardant Coating Adhesive", Mr. Liu Duokui added a char-forming agent to the ammonium polyphosphate flame-retardant coating adhesive system to overcome the problem of polyester droplet, but its flame-retardant effect and flame-retardant Durability, etc. are still not ideal, and there are also problems of ammonium polyphosphate absorbing moisture and causing moisture and heat migration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant coating adhesive for textiles, method for finishing flame-retardant fabric thereof, and flame-retardant fabric thereof
  • Flame-retardant coating adhesive for textiles, method for finishing flame-retardant fabric thereof, and flame-retardant fabric thereof
  • Flame-retardant coating adhesive for textiles, method for finishing flame-retardant fabric thereof, and flame-retardant fabric thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This textile is prepared by using the halogen-free environmentally friendly flame retardant through the following method, and the amount of each material mentioned in it is based on 1000g of ammonium polyphosphate APP as the standard unit:

[0026] ①. Mix 1000g of APP and absolute ethanol at a mass ratio of 1:10, and implement it until fully dispersed by a high-shear stirring device to obtain an APP dispersion;

[0027] ②. Add 0.2L methyl orthosilicate dropwise to the APP dispersion in step ①. Under magnetic stirring, add 20ml of oxalic acid with a concentration of 0.5 g / L, and stir for 2 hours in a water bath at 80°C to obtain an intermediate solution ;

[0028] ③. Add 200ml of ammonia water with a concentration of 0.05g / L to the intermediate solution in step ②. After the gel reacts in a water bath at 60°C, add absolute ethanol, exchange the water in the gel for 3 times, and then exchange the ethanol in the gel for 3 times. Surface-modified the aged wet gel at 60°C, d...

Embodiment 2

[0031] The application of halogen-free environmentally friendly flame retardants in this textile is prepared by the following method, and the amount of each material mentioned in it is based on 1000g of ammonium polyphosphate APP as the benchmark unit of measurement:

[0032] ① Put 1000g of APP into anhydrous propanol, the mass ratio of the two is 1:20, and fully disperse it by a high-shear stirring device to obtain an APP dispersion;

[0033]②. Add 0.2L tetraethyl orthosilicate dropwise to the APP dispersion in step ①, add 20ml of citric acid with a concentration of 0.8 g / L to the magnetic stirring, and stir in a water bath at 80°C for 2 hours;

[0034] ③. Add 200ml of sodium hydroxide with a concentration of 0.05g / L to the intermediate solution in step ②, and react with gel in a water bath at 60°C. After the reaction, add absolute ethanol, exchange the water in the gel for 3 times, and then exchange the gel Ethanol was used for 3 times, and the aged wet gel was subjected to ...

Embodiment 3

[0037] The application of halogen-free environmentally friendly flame retardants in this textile is prepared by the following method, and the amount of each material mentioned in it is based on 1000g of ammonium polyphosphate APP as the benchmark unit of measurement:

[0038] ① Put 1000g of APP into absolute ethanol, the mass ratio of the two is 1:50, and fully disperse it by a high-shear stirring device to obtain an APP dispersion;

[0039] ②. Add dropwise 0.2L butyl orthosilicate to the APP dispersion in step ①, then add 20ml of propionic acid with a concentration of 0.5 g / L under magnetic stirring, and stir in a water bath at 80°C for 2 hours;

[0040] ③. Add 200ml of potassium hydroxide with a concentration of 0.05g / L to the intermediate solution in step ②. After the gelation reaction in a water bath at 60°C, add absolute ethanol, exchange the water in the gel for 3 times, and then exchange the ethanol in the gel 3 times, surface-modified the aged wet gel at 60°C, dried an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a flame-retardant coating adhesive for textile, a finishing method of flame-retardant fabric with the flame-retardant coating adhesive and the flame-retardant fabric with the flame-retardant coating adhesive. The flame-retardant coating adhesive for the textile is prepared through steps as follows: a microcapsule flame retardant DCAPP is added to a polyurethane coating adhesive, the viscosity of the mixture is adjusted to 5,000-6,500 cps, and the mixture is uniformly stirred and compounded to form the flame-retardant coating adhesive. The finishing method of flame-retardant fabric with the flame-retardant coating adhesive comprises the steps of at least two times of coating and baking. The flame-retardant fabric has the technical advantages as follows: the flame-retardant fabric has good flame retardance and flame-retardant durability, high flame retardant efficiency, low smoke amount as well as an excellent anti-dripping effect on polyester fiber fabric, and the finishing process is simple, meets the environmental protection requirement and is low in cost.

Description

technical field [0001] The application of the present invention relates to a flame-retardant coating adhesive for textiles, a fabric flame-retardant finishing method thereof, and a flame-retardant fabric. Background technique [0002] To endow textiles with flame retardant properties, due to different types of fabrics, different flame retardants, and different flame retardant treatment methods for fabrics, the flame retardant properties of the obtained flame retardant fabrics vary widely, and the flame retardant effects have their own advantages; and in The technical design also needs to meet the increasingly strict dual technical index requirements including fire safety standards and environmental protection standards. [0003] Among many fiber fabrics, polyester fabric itself has remarkable characteristics such as good elasticity, not easy to deform, strong and durable, corrosion resistance, insulation, and low price. It is widely used in textiles and industrial products, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/564D06M11/71D06M11/79
Inventor 路艳华张迎春程德红林杰李金华
Owner EASTERN LIAONING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com