Conductive polymer composite material with dendritic cell structure and preparation method thereof

A conductive polymer and composite material technology, applied in the field of conductive polymer composite materials, can solve problems such as hindering popularization and application, strong polymer selectivity, complex operation process, etc., and achieve easy popularization and application, stable electrical performance, and wide sources Effect

Active Publication Date: 2017-09-01
ZHENGZHOU UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the inherent disadvantages of these methods, such as high cost, low efficiency, complex operation process, and strong selectivity to polymers, hinder their promotion and application in polymer material processing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive polymer composite material with dendritic cell structure and preparation method thereof
  • Conductive polymer composite material with dendritic cell structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The second technical problem to be solved in the present invention is to provide the preparation method of the above-mentioned conductive polymer composite material, the steps include:

[0044] a. Preparation of the mixed solution: dissolving and mixing the thermoplastic elastomer material, thermosetting resin, curing agent and conductive particles in a solvent to obtain a mixed solution;

[0045] b. Freeze-drying: the mixed solution obtained in step a is freeze-dried to obtain the conductive polymer composite material;

[0046] Wherein, the solvent is at least one of dioxane, water, acetone, toluene, xylene, tetrahydrofuran, dimethylformamide, methanol, ethanol, formic acid or methylene chloride; the amount of solvent is: per weight 20-100ml of solvent is added to one part of raw materials, namely thermoplastic elastomer material, thermosetting resin, curing agent and conductive particles.

[0047] Further, in the preparation method of the above-mentioned conductive c...

Embodiment 1

[0056] Example 1 Preparation of Conductive Polymer Composite Material with Dendritic Cell Structure

[0057] Concrete preparation steps are:

[0058] (1) Drying of raw materials: Dry TPU and MWCNTs in a vacuum oven for 8 hours at 80°C;

[0059] (2) Preparation of mixed solution: 1.2g epoxy resin (model: epoxy resin LT5078A), 0.4g curing agent (model: curing agent LT5078B), and 0.44g MWCNTs were added to 40ml of dioxane in sequence respectively. In a 100ml beaker, stir mechanically at room temperature for about 10 minutes, then ultrasonically disperse in a water bath at room temperature for 30 minutes to obtain a mixed solution a; at the same time, mix 2.4g of TPU pellets and 40ml of dioxane in a 100ml beaker, and heat Stir, the temperature is at 50°C, stir magnetically for about 1 hour, cool to room temperature, and obtain mixed solution b; then pour mixed solution b into mixed solution a, and magnetically stir for 30 minutes to obtain the final MWCNTs / TPU / epoxy resin / Curin...

Embodiment 2-6

[0063] Example 2-6 Preparation of Conductive Polymer Composite Material with Dendritic Cell Structure

[0064] Each raw material ratio of embodiment 2-6 is as shown in table 1. The specific preparation methods are all the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of conductive polymer materials, and in particular relates to a conductive polymer composite material with a dendritic cell structure. The present invention provides a conductive polymer composite material. The raw materials and their proportions are: thermoplastic elastomer material: thermosetting resin: curing agent: conductive particles = 1-5 parts by weight: 1-4 parts by weight: 0.1-2 parts by weight : 0.01-1 part by weight; the conductive polymer composite material has a dendritic cell structure. The conductive polymer material obtained in the invention has a dendritic cell structure, its electrical performance is improved and stable, and its percolation value is low.

Description

technical field [0001] The invention belongs to the field of conductive polymer materials, and in particular relates to a conductive polymer composite material with a dendritic cell structure. Background technique [0002] Since the discovery of the first conductive polymer polyacetylene in 1977, the science of conductive polymer materials (CPCs) has been a rapidly developing field in recent years. Conductive polymer materials can be divided into structural conductive polymer materials and composite conductive polymer materials according to different structures and preparation methods. Among them, the composite conductive polymer composite material refers to a conductive filler (such as graphite, carbon black, carbon nanotubes, graphene, metal powder, metal nanowires, etc.) Polymer composite material with conductive function. It has the conductivity endowed by conductive fillers and the good processability of polymer materials. Compared with ordinary CPCs, CPCs with cell ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08L63/00C08K9/04C08K7/24C08J9/28
Inventor 代坤曹晓瀚蓝艳李勇赵帅翔郑国强刘春太
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com