A water-based composition and hard coating technology, applied in coatings, layered products, instruments, etc., can solve problems such as easy injury, achieve high hardness, excellent optical properties, and inhibit the rise of haze.

Active Publication Date: 2015-07-15
FUJIFILM CORP
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surfaces of these displays are prone to injury due to contact with various objects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous composition and hard coat layer
  • Aqueous composition and hard coat layer
  • Aqueous composition and hard coat layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0110] (Preparation of an aqueous solution for an easily bonding layer)

[0111] The aqueous solution for an easily bonding layer was prepared by the following mix|blending.

[0112] 8 parts by mass of tin oxide particle dispersion

[0113] (Ishihara Sangyo Co., Ltd., FS-10D)

[0114] 2.8 parts by mass of polyurethane

[0115] (Mitsui Chemicals Co., Ltd., Takelac WS-5100)

[0116] 4.2 parts by mass of crosslinking agent

[0117] (manufactured by Nisshinbo Chemical Co., Ltd., 10% dilution of Carbodilite V-02-L2)

[0118] Surfactant A 0.2 parts by mass

[0119] (manufactured by Sanyo Chemical Industry Co., Ltd., Sanded BL 10% aqueous solution, anionic)

[0120] Surfactant B 0.2 parts by mass

[0121] (Sanyo Chemical Industry Co., Ltd., a 10% dilution of Naroacti CL-95, non-ionic)

[0122] 84.6 parts by mass of water

[0123] (Preparation of Aqueous Composition for Hard Coating)

[0124] The preparation of the aqueous hard-coat composition was performed so that the foll...

Embodiment 2～8 and comparative example 1～4

[0145] An easily bonding layer was formed in the same manner as in Example 1, and the aqueous solution for a hard coat layer prepared so as to achieve the combination in Table 1 was applied in the same manner as in Example 1 to prepare a sample.

[0146] (Evaluation)

[0147] Alkali treatment

[0148] The samples of Examples 1 to 8 and Comparative Examples 1 to 4 were immersed in a 5% NaOH aqueous solution at 30° C. for 10 minutes, and the haze values ​​before and after the treatment were measured. The haze measurement machine NDH5000 by Nippon Denshoku Industries Co., Ltd. was used for the measurement of haze. The increase in haze value is shown in Table 1. The evaluation that the increase of the haze value is 0.1 or less is A, the evaluation of more than 0.1 and 0.5 or less is B, and the evaluation of more than 0.5 is C.

[0149] Table 1

[0150]

[0151] As shown in Table 1, in Comparative Examples 1 to 4, since the content of the aluminum chelate complex was low, th...

Embodiment 9

[0156] (Preparation of an aqueous solution for an easily bonding layer)

[0157] The aqueous solution for an easily bonding layer was prepared according to the following mix|blending.

[0158] Tin oxide particle dispersion 8 parts by mass

[0159] (Mitsubishi Materials Co., Ltd., SDL-2)

[0160] Polyolefin 9 parts by mass

[0161] (Manufactured by UNITIKA Co., Ltd., AROBES SE-1013N)

[0162] Cross-linking agent 2 parts by mass

[0163] (manufactured by Nisshinbo Chemical Co., Ltd., 10% dilution of Carbodilite V-02-L2)

[0164] Surfactant A 2 parts by mass

[0165] (manufactured by Sanyo Chemical Industry Co., Ltd., Sanded BL 10% aqueous solution, anionic)

[0166] Surfactant B 2 parts by mass

[0167] (Sanyo Chemical Industry Co., Ltd., a 10% dilution of Naroacti CL-95, non-ionic)

[0168] 77 parts by mass of water

[0169] (Formation of easy bonding layer and hard coat layer)

[0170] The corona treatment was given to the PET base material, the said aqueous solution f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hazeaaaaaaaaaa
Login to view more

Abstract

The objective of the present invention is to provide: an aqueous composition for forming a hard coat layer that has high alkali resistance; and a hard coat layer. The present invention relates to an aqueous composition which is obtained by mixing an epoxy group-containing alkoxysilane, an epoxy group-free alkoxysilane and a metal complex. The ratio of the epoxy group-containing alkoxysilane relative to the total alkoxysilane consisting of the epoxy group-containing alkoxysilane and the epoxy group-free alkoxysilane is 20-85% by mass. The ratio of the metal complex relative to the epoxy group-containing alkoxysilane is 17-70% by mole.

Description

technical field [0001] The present invention relates to aqueous compositions and hardcoats. Specifically, the present invention relates to an aqueous composition comprising an epoxy group-containing alkoxysilane, an epoxy group-free alkoxysilane, and a metal complex, and a hard coat layer formed using the aqueous composition. Background technique [0002] In recent years, display devices such as liquid crystal displays, plasma displays, and touch panel displays have spread rapidly. The surfaces of these display devices are susceptible to injury due to contact with various objects. In addition, resistance to heat and humidity may also be required. Therefore, the surface of a display device is required to have high scratch resistance and high heat and humidity resistance. [0003] In order to provide the surface of the display device with high scratch resistance and high heat and humidity resistance, a hard coat layer is often provided on the surface layer of the display de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/20B32B9/00C08G59/70C08G77/14C08K3/08C08K3/22C08K3/36C08L63/00C09D5/02C09D7/12C09D183/02C09D183/06G06F3/041C09D7/61
CPCC08G59/70C08L63/00C08L83/06C08K2003/2237C08G59/20B32B9/00C09D183/06C08K2003/2227C09D7/12C09D5/02C08G77/14C08G65/22C09D7/61C08L83/00C08K5/5415C08K5/56
Inventor 塚本直树
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap