A kind of preparation method of textured non-slip glove fabric

A fabric and anti-skid technology, applied in the field of textile materials, can solve the problems of complex preparation method of anti-skid gloves, low market share and high friction resistance, and achieve the effects of being beneficial to market promotion, low production cost and strong grip.

Active Publication Date: 2016-12-07
广西康信德医疗科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the above technology that the concave-convex ellipse and corrugated texture similar to fingerprints have high friction resistance. Compared with particle-type non-slip gloves, texture-type gloves have excellent gripping ability and are more in line with ergonomic design. The preparation method of the anti-skid gloves of the type is relatively complicated, the process is relatively immature, and the market share is not high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of textured non-slip glove fabric
  • A kind of preparation method of textured non-slip glove fabric
  • A kind of preparation method of textured non-slip glove fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Randomly distribute thread shapes with a diameter of 0.5cm in the hollowed out mold. The hollowed out part in the mold is threaded, and the area of ​​the figure reaches 95% of the total area of ​​the mold. The width of the lines in the hollowed out part is 1mm. The spacing is 3mm.

[0032] (2) Place the hollow mold on an improved flat screen printing machine, add nitrile latex with a viscosity PVI value of 1.3 on the upper surface of the hollow mold, then place the fabric under the hollow mold, and move the scraper at a speed of 23m / min , so that the nitrile latex falls on the surface of the fabric through the hollowed out position to obtain a coated fabric.

[0033] (3) The coated fabric was immersed in a coagulant for 50 seconds to solidify the nitrile latex on the surface of the fabric, then washed with water, and dried at 45° C. to obtain a textured non-slip glove fabric with a coating thickness of 0.1 cm.

Embodiment 2

[0035] (1) Randomly distribute ellipses with a diameter of 0.5-3cm in the hollowed out mold. The hollowed out part in the mold is elliptical, and the area of ​​the figure reaches 5% of the total area of ​​the mold. The width of the lines in the hollowed out part is 2mm. The spacing between the ellipses is 4mm.

[0036] (2) Place the hollow mold on an improved flat screen printing machine, add nitrile latex with a viscosity PVI value of 1.3 on the upper surface of the hollow mold, then place the fabric under the hollow mold, and move the scraper at a speed of 23m / min , so that the nitrile latex falls on the surface of the fabric through the hollowed out position to obtain a coated fabric.

[0037] (3) The coated fabric was immersed in a coagulant for 60 seconds to solidify the nitrile latex on the surface of the fabric, then washed with water, and dried at 60° C. to obtain a textured non-slip glove fabric with a coating thickness of 0.3 cm.

Embodiment 3

[0039] (1) Randomly distribute thread shapes with a diameter of 1.0cm in the hollowed out mold. The hollowed out part in the mold is threaded. The area of ​​the figure reaches 50% of the total area of ​​the mold. The width of the lines in the hollowed out part is 1.5mm. The pitch is 3.8mm.

[0040] (2) Place the hollow mold on an improved flat screen printing machine, add nitrile latex with a viscosity PVI value of 1.4 on the upper surface of the hollow mold, then place the fabric under the hollow mold, and move the scraper at a speed of 25m / min , so that the nitrile latex falls on the surface of the fabric through the hollowed out position to obtain a coated fabric.

[0041] (3) Immerse the coated fabric in a coagulant for 55 seconds to solidify the nitrile latex on the surface of the fabric, then wash it with water, and dry it at 50° C. to obtain a textured non-slip glove fabric with a coating thickness of 0.5 cm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a grain type slip-proof glove fabric. A threaded or oval slip-proof coating is imprinted on the surface of the glove fabric by employing a template method, so as to obtain the grain type slip-proof glove fabric. The friction coefficient of the glove fabric prepared by the method is controllable and can be adjusted according to the density and the thickness of the slip-proof coating on the fabric surface, so that the fabric adapts to the daily and special production protection requirements; the coating structure conforms to the human engineering and is relatively high in holding power and relatively good in holding power uniformity; the slip-proof glove fabric can be applied to the fields of decoration and protection, and is especially suitable for preparation of the glove fabric; and the preparation method is simple, convenient, high in efficiency, low in cost, suitable for continuous industrialized production, and beneficial to market popularization.

Description

technical field [0001] The invention belongs to the technical field of textile materials, and in particular relates to a method for preparing a textured non-slip glove fabric. Background technique [0002] Gloves are used in all aspects of people's lives, and are used in fields such as decoration, daily protection and special protection. Gloves are made of textile fibers and new materials through sewing, knitting and dipping. The material and processing methods determine the protective performance of gloves. Gloves are divided into cotton yarn, plush, leather, microfiber, rubber, etc. according to the material, and are divided into high temperature resistance, insulation, anti-skid, anti-stab, anti-chemical reagent and anti-vibration according to the protective performance. It is widely used in daily life and production. [0003] Chinese patent CN 100427219C (disclosure date 2007.5.16) discloses a net-like anti-slip coating processing method for anti-slip gloves. The silk ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N7/04B05D1/28
Inventor 倪勇
Owner 广西康信德医疗科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com