Production process of aluminum-titanium alloy AlTi10

A production process, aluminum-titanium alloy technology, applied in the field of aluminum alloy production, can solve the problems of large power consumption, slow production efficiency, high production cost, etc., and achieve the effect of reducing labor intensity, reducing production cost and shortening the production cycle

Inactive Publication Date: 2015-07-08
铜山县超特有色金属添加剂厂
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This production process is outdated, consumes a lot of electric energy, and the production cost is high. Moreover, manual stirring is used, which has high operating intensity, slow production efficiency, and the product is easy to segregate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] An aluminum-titanium alloy AlTi 10 The specific production process is as follows: (1) put the aluminum ingot with a content greater than 99.70% into the electric furnace, and slowly raise the temperature until the aluminum ingot is completely melted; (2) continue to heat up to 1250°C, and then add the aluminum ingot with a content greater than 99.98% until the sponge titanium is completely melted, the mass ratio of aluminum ingot to titanium sponge is 100:11; (3) Stir the alloy liquid with a magnetic stirrer for 20 minutes; (5) After the reaction, add a homogenizing agent before sampling and carry out static reaction for 1520 minutes, then perform low-magnification analysis and component analysis; (6) After passing the inspection, cast the alloy liquid.

Embodiment 2

[0013] An aluminum-titanium alloy AlTi 10 The specific production process is as follows: (1) put the aluminum ingot with a content greater than 99.70% into the electric furnace, and slowly heat up until the aluminum ingot is completely melted; (2) continue to heat up to 1250°C, and then add the aluminum ingot with a content greater than 90% until the titanium chips are completely melted, the mass ratio of aluminum ingots to titanium chips is 100:11; (3) Stir the alloy liquid for 20 minutes with a magnetic stirrer; (5) After the reaction, add a homogenizing agent before sampling and carry out static reaction for 1520 minutes, then perform low-magnification analysis and component analysis; (6) After passing the inspection, cast the alloy liquid.

[0014] The advantages of the production process of the present invention: the electric furnace is a high-consumption equipment, and this process adopts low-power operation (8-12h electricity cost 1.38 yuan / h, 12-17h electricity cost 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process of aluminum-titanium alloy AlTi10. The production process comprises the steps of placing an aluminum ingot with the content of larger than 99.70% into an electric furnace, and heating to 1250 DEG C; adding sponge titanium or titanium scraps until the aluminum ingot is completely molten, wherein the mass ratio of the aluminum ingot to the sponge titanium or the titanium scraps is 100:11; uniformly stirring through a magnetic stirrer; adding lithium aluminum tetrahydride, and standing for reacting; adding a leveling agent to stand before sampling, and then, carrying out low-power analysis and component analysis; and casting and molding after the assay is approved. Power low-ebb operation is adopted in the production process disclosed by the invention, so that energy sources are saved, and the production cost is reduced; manpower work can be replaced with magnetic stirring equipment, so that materials can be sufficiently and uniformly stirred, the labor intensity of a worker can be reduced, the production period can be shortened, and the production efficiency can be increased; and the titanium content of the casting product AlTi10 can be up to 9-11% which is twice as much as the content of titanium produced by using the old national standard, and no segregation is caused.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy production, in particular to an aluminum-titanium alloy AlTi 10 production process. Background technique [0002] At present, the national standard aluminum-titanium alloy on the market is only AlTi 5 , and the production process of this aluminum-titanium alloy is old, the process is as follows: add aluminum ingot (content>99.70%) and sponge titanium (content>99.98%) into the electric furnace according to the mass ratio of 100:11, first add aluminum ingot , and then heated to the smelting temperature of adding titanium and then adding titanium sponge. At this time, artificial stirring was used, and the stirring was fully uniform. Finally, low-power analysis was carried out. After passing the inspection, the casting operation was carried out. This production process is outdated, consumes a lot of electric energy, and the production cost is high. Moreover, manual stirring is used, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/02C22C21/00
Inventor 苏伟
Owner 铜山县超特有色金属添加剂厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap