Preparation method of plate for building

A technology for construction and board materials, which is applied in the field of construction material manufacturing, and can solve the problems of cracking and water seepage of building materials, accelerated corrosion and damage of steel bars, etc.

Inactive Publication Date: 2015-05-20
南通升环木业有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction, while accelerating the corrosion of steel bars, resulting in cracking and water seepage of building materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing building boards, which is mixed with composite minerals, is characterized in that:

[0029] Weigh raw materials: cement 282g, cement composite mineral additive 18g, sand 750g, polypropylene fiber 4g, naphthalene-based water reducer 3g; put the above raw materials into a conical double-helix mixer and stir evenly for 50 minutes. After stirring Casting into the mold; static curing, the time is 8 hours; after static curing, enter the autoclave for the first autoclaving curing, the temperature of the first autoclaving curing is 220 ° C, and the time is 10 hours; after that Cool naturally, place at room temperature for 4 hours, carry out the second autoclaving curing, the temperature of the second autoclaving curing is 160 ° C, and the time is 20 hours; obtain the building board mixed with composite minerals,

[0030] The preparation method steps of the cement composite mineral additive are:

[0031] Step (1): According to 22 parts of alumina clinker,...

Embodiment 5

[0036] A method for preparing building boards, which is mixed with composite minerals, is characterized in that:

[0037] Weigh raw materials: cement 282g, cement composite mineral additive 18g, sand 750g, polypropylene fiber 4g, naphthalene-based water reducer 3g; put the above raw materials into a conical double-helix mixer and stir evenly for 50 minutes. After stirring Casting into the mold; static curing, the time is 8 hours; after static curing, enter the autoclave for the first autoclaving curing, the temperature of the first autoclaving curing is 220 ° C, and the time is 10 hours; after that Cool naturally, place at room temperature for 4 hours, carry out the second autoclaving curing, the temperature of the second autoclaving curing is 160 ° C, and the time is 20 hours; obtain the building board mixed with composite minerals,

[0038] The preparation method steps of the cement composite mineral additive are:

[0039] Step (1): According to 24 parts of alumina clinker, 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a plate for a building. The plate for the building is doped with composite minerals. The preparation method of the plate for the building is characterized by comprising the following steps: weighing raw materials, namely cement, the prepared cement composite mineral additive, sand, polypropylene fibers and a naphthalene water reducer, in ratio; and putting the raw materials into a conical double helix stirring machine in the ratio, and uniformly stirring for 50 minutes. The composite-mineral-doped plate for the building has efficient waterproof, dampproof, expansion, crack-proof and impervious functions and also has no rusting effect on reinforcing steel.

Description

technical field [0001] The invention relates to a building plate mixed with composite minerals, namely a preparation method of the building plate, which belongs to the field of building material manufacturing. Background technique [0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction also accelerates the corrosion of steel bars, resulting in cracking and water seepage of building materials. Contents of the invention [0003] The purpose of the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/38
Inventor 黄小仙
Owner 南通升环木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com