A kind of bismuth yttrium oxide nanorod and its preparation method and application

A technology of nanorods and bismuth yttrium oxide, which is applied in the field of bismuth yttrium oxide nanorods and its preparation, can solve problems such as poor morphology of bismuth yttrium oxide, achieve high practical application ability, good reproducibility, and facilitate mass production Effect

Active Publication Date: 2016-08-31
JIANGSU UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The researchers found that it is difficult for yttrium to enter the crystal lattice of bismuth oxide in general reactions, and only bismuth yttrium oxide was synthesized by the solid-phase method, but the high temperature of the solid-phase method has a great influence on the morphology, so the solid-phase method synthesized The morphology of bismuth yttrium oxide is very bad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bismuth yttrium oxide nanorod and its preparation method and application
  • A kind of bismuth yttrium oxide nanorod and its preparation method and application
  • A kind of bismuth yttrium oxide nanorod and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Weigh bismuth nitrate and yttrium nitrate and dissolve in 10ml, 0.1mol / L -1 In dilute nitric acid, the masses of the bismuth nitrate and yttrium nitrate are 0.2425g and 0.1916g respectively.

[0027] (2) The mixed solution in step 1 was ultrasonically stirred for 1 h to obtain a clear and transparent liquid.

[0028] (3) Transfer the liquid obtained in step 2 to a polytetrafluoroethylene-lined reactor, and 4 ∙ H 2 O to adjust the pH value to 8; add water to 80% of the reactor volume.

[0029] (4) The reaction kettle in step 3 was kept in a temperature range of 180ºC, and reacted at a constant temperature for 48 hours to obtain a precipitate.

[0030] (5) Wash the precipitate obtained in step 4 alternately with water and ethanol, and centrifuge.

[0031] (6) Calcining the centrifuged product in step 5 at a high temperature to remove impurities to obtain pure-phase bismuth yttrium nanorods. The high-temperature calcination temperature is 450°C, the calcination tim...

Embodiment 2

[0033] (1) Weigh bismuth nitrate and yttrium nitrate and dissolve in 10ml, 0.1mol / L -1 In dilute nitric acid, the masses of the bismuth nitrate and yttrium nitrate are 0.2425g and 0.1916g respectively.

[0034] (2) The mixed solution in step 1 was ultrasonically stirred for 1 h to obtain a clear and transparent liquid.

[0035] (3) Transfer the liquid obtained in step 2 to a polytetrafluoroethylene-lined reactor, and 4 ∙ H 2 O to adjust the pH value to 8.5; add water to 80% of the reactor volume.

[0036] (4) The reaction kettle in step 3 was kept in a temperature range of 200 ºC for 24 hours at a constant temperature to obtain a precipitate.

[0037] (5) Wash the precipitate obtained in step 4 alternately with water and ethanol, and centrifuge.

[0038] (6) The centrifuged product in step 5 is calcined at high temperature to remove impurities, so as to obtain pure phase bismuth yttrium nanorods. The temperature of high-temperature calcination is 550°C, the calcination tim...

Embodiment 3

[0040] (1) Weigh bismuth nitrate and yttrium nitrate and dissolve in 10ml, 0.1mol / L -1 In dilute nitric acid, the masses of the bismuth nitrate and yttrium nitrate are 0.2425g and 0.1916g respectively.

[0041] (2) The mixed solution in step 1 was ultrasonically stirred for 1 h to obtain a clear and transparent liquid.

[0042] (3) Transfer the liquid obtained in step 2 to a polytetrafluoroethylene-lined reactor, and 4 ∙ H 2 O to adjust the pH value to 9; add water to 80% of the reactor volume.

[0043] (4) The reaction kettle in step 3 was kept in a temperature range of 240 ºC for 16 hours at a constant temperature to obtain a precipitate.

[0044] (5) Wash the precipitate obtained in step 4 alternately with water and ethanol, and centrifuge.

[0045] (6) Calcining the centrifuged product in step 5 at a high temperature to remove impurities to obtain pure-phase bismuth yttrium nanorods. The high-temperature calcination temperature is 650°C, the calcination time is 2h, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of nanomaterial synthesis, and particularly relates to a bismuth yttrate nanorod as well as a preparation method and application thereof. The bismuth yttrate nanorod with a uniform morphology is prepared by adopting a hydrothermal synthesis method. According to the technical scheme, the method comprises the following steps: firstly, mixing Bi(NO3)3.5H2O (bismuth nitrate) and Y(NO3)3.6H2O (yttrium nitrate) into nitric acid, stirring evenly, then adjusting the pH value with NH4.H2O, and preparing a bismuth yttrate nanorod precursor solution by virtue of a hydrothermal method; and burning the precursor solution at a high temperature, so as to obtain the bismuth yttrate nanorod. A bismuth yttrate nanorod photocatalyst is synthesized by using a simple hydrothermal synthesis method; the morphology is a two-dimensional nanorod; and the bismuth yttrate nanorod has the advantages of chemical stability, no toxicity and the like as a novel photocatalytic material.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial synthesis, and in particular relates to a bismuth yttrium nanorod and its preparation method and application. The nanorod can be used in the field of visible light degradation of antibiotics. Background technique [0002] Environmental pollution and energy depletion have made solar energy, a green, pollution-free and recyclable energy, a research hotspot in recent years. Most photocatalytic semiconductor materials can degrade organic matter under UV light. Scholars at home and abroad have done a lot of research in order to make photocatalysts more fully utilize the spectrum. Bismuth yttrium oxide has an energy band of 2.14 EV, and it is a photocatalyst that responds to visible light. The researchers found that it is difficult for yttrium to enter the crystal lattice of bismuth oxide in general reactions, and only bismuth yttrium oxide was synthesized by the solid-phase method, but the high t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G29/00B01J23/18B82Y30/00B82Y40/00C02F1/30
Inventor 施伟东吴苗苗王超张超蔡凡朋余小强陈超
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap