Abrasion-resistant flexible transparent conductive film and preparation method thereof

A transparent conductive film, flexible technology, applied in the direction of cable/conductor manufacturing, conductive layer on insulating carrier, conductive material dispersed in non-conductive inorganic materials, etc., can solve the problem of poor wear resistance of flexible transparent conductive film, silver grid The etching process is complicated, the production conditions are harsh, etc., to achieve the effects of short time-consuming, good wear resistance, and improved electrical conductivity

Inactive Publication Date: 2015-03-25
SUZHOU SIDIKE NEW MATERIALS SCI & TECH
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, there are mainly the following two deficiencies: 1) Some well-known foreign companies have adopted different technologies in trial production or mass production of flexible transparent conductive films, such as silver grid etching, copper evaporation, Evaporation, silver grid etching process is complicated, production conditions are harsh, and equipment investment is too high; 2) flexible transparent conductive films generally have the disadvantage of poor wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion-resistant flexible transparent conductive film and preparation method thereof
  • Abrasion-resistant flexible transparent conductive film and preparation method thereof
  • Abrasion-resistant flexible transparent conductive film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the wear-resistant flexible conductive film comprises the following steps:

[0033] Step 1): Take silver nitrate, glycerol, ammonium chloride or ammonium fluoride, and polyvinylpyrrolidone by weighing respectively according to the above formula to form a mixed solution;

[0034] Step 2): stirring and heating the obtained mixed solution at 200° C. for 20-30 minutes to obtain a nano-silver wire suspension;

[0035] Step 3): Pass the suspension of silver nanowires through a 400-mesh filter to separate the silver nanowires;

[0036] Step 4): Weigh the oleoresin, leveling agent, dispersant, nano-silver wire, additive powder and an appropriate amount of organic solvent according to the above formula. And they were put into the reaction vessel and stirred for 30min to obtain the coating of the novel wear-resistant flexible transparent conductive film;

[0037] Step 5): uniformly coating the coating on the PET film, and adjusting its thickness to 0.5...

Embodiment 1

[0040] Weigh 10g of silver nitrate, 100g of glycerol, 10g of ammonium chloride, and 20g of polyvinylpyrrolidone to make a mixed solution, and stir and heat the mixed solution at 200°C for 30min. Pass the suspension of the prepared silver nanowires through a 400-mesh filter screen to separate the silver nanowires.

[0041] A new type of wear-resistant transparent conductive film, which is prepared by coating the surface of PET with paint and drying it. The formula of the paint is composed of the following materials:

[0042]

[0043] After testing, the surface resistance of the film is 45Ω, the light transmittance is 80%, and the haze is 2.0%, and the abrasion is reduced by 50% through a comparative test.

Embodiment 2

[0045] The preparation of silver nanowires is shown in Example 1.

[0046] A new type of wear-resistant transparent conductive film, which is prepared by coating the surface of PET with paint and drying it. The formula of the paint is composed of the following materials:

[0047]

[0048] After testing, the surface resistance of the film is 40Ω, the light transmittance is 86%, and the haze is 1.7%, and the abrasion is reduced by 45% through a comparative test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
hazeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an abrasion-resistant flexible transparent conductive film and a preparation method of the film. The surface of PET is coated with coating, and then the film is prepared after being dried. According to the formula of a sizing material, the sizing material is composed of nanometer silver wires, oleoresin, additive powder, flatting agents and a proper quantity of organic solvents. The nanometer silver wires excellent in electrical conductivity are adopted and nanometer oxide and fiber-phase materials are mixed with the additive powder to serve as additives so that the electrical conductivity and the abrasion resistance of the film can be improved. The abrasion-resistant flexible transparent conductive film is suitable for reel-to-reel continuous production, production efficiency is improved, and transportation is facilitated. The abrasion-resistant flexible transparent conductive film is reasonable in design, simple and low in cost.

Description

technical field [0001] The invention relates to a film, in particular to a wear-resistant flexible transparent conductive film and a preparation method thereof. Background technique [0002] Since the 1960s, transparent conductive films and some other transparent conductive materials have emerged. However, the most widely used transparent conductive film is prepared on hard materials such as glass and ceramics, which has the disadvantages of being brittle, not easily deformed, and heavy, and hard materials such as large-sized glass are not easy to prepare, which limits the transparent conductive film. Applications. In contrast, the flexible transparent conductive film prepared on the organic flexible substrate not only has the same photoelectric characteristics, but also has many unique advantages, such as bendable, unbreakable, light weight, and can be prepared in various sizes, shapes and It can be produced continuously in roll-to-roll mode, which improves production eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22H01B5/14H01B13/00
Inventor 金闯杨晓明曾金栋
Owner SUZHOU SIDIKE NEW MATERIALS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com