Environment-friendly nail-free glue and preparation method thereof

An environmentally friendly, nail-free adhesive technology, used in adhesives, adhesive types, polyether adhesives, etc., can solve problems such as low toxicity, toxic and harmful, health and environmental hazards, and achieve easy dehydration and good adhesion. Connectivity, the effect of reducing energy consumption

Active Publication Date: 2015-03-25
GUANGZHOU BAIYUN CHEM IND
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the existing nail-free adhesives can meet the mandatory regulations of the national standard GB18583 "Limits of Hazardous Substances in Adhesives for Interior Decoration Materials", these adhesives still contain toxic, harmful or low-toxic solvents, and the total solvent content is more than 10%. , and some even reach 50%, the existence of these solvents is not negligible to the harm of people's health and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly nail-free glue and preparation method thereof
  • Environment-friendly nail-free glue and preparation method thereof
  • Environment-friendly nail-free glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] In this embodiment, an environment-friendly nail-free glue comprises the following raw materials in parts by weight:

[0037] in,

[0038] Described silane-modified polyether polymer is:

[0039] The viscosity is 7Pa.s;

[0040] The structure of the methyl MQ silicone resin is (Me 3 SiO 0.5 ) a (SiO 2 ) b , where a / b=0.5.

[0041] The preparation method of the above-mentioned environment-friendly nail-free glue comprises the following steps:

[0042] Add 10 parts of silane-modified polyether polymer, 15 parts of dioctyl phthalate, 10 parts of methyl MQ silicone resin, 5 parts of white carbon black, 2 parts of polyamide wax, and 39 parts of heavy calcium carbonate into the kneader Heating and vacuum kneading for 1 hour, the heating temperature is 130°C, the vacuum degree is -0.09MPa, and the discharged material is used as the base material.

[0043] After the base material is cooled to a temperature lower than 50°C, transfer it to a planetary mixer, add the ...

Embodiment 2

[0045] In this embodiment, an environment-friendly nail-free glue comprises the following raw materials in parts by weight:

[0046]

[0047] in,

[0048] Described silane-modified polyether polymer is:

[0049] 10 parts of polymer with viscosity of 6pa.s, 15 parts of polymer with viscosity of 13pa.s;

[0050] The structure of the methyl MQ silicone resin is (Me 3 SiO 0.5 ) a (SiO 2 ) b , where a / b=1.0.

[0051] The preparation method of the above-mentioned environment-friendly nail-free glue comprises the following steps:

[0052] Add 25 parts of silane-modified polyether polymer, 10 parts of diisodecyl adipate, 10 parts of methyl MQ silicone resin, 3 parts of white carbon black, 5 parts of polyamide wax, and 31 parts of light calcium carbonate into the kneader Heating and vacuum kneading for 3 hours, the heating temperature is 110°C, the vacuum degree is -0.1MPa, and the discharged material is used as the base material.

[0053] After the base material is coo...

Embodiment 3

[0055] In this embodiment, an environment-friendly nail-free glue comprises the following raw materials in parts by weight:

[0056] in,

[0057] Described silane-modified polyether polymer is:

[0058] 45 parts of polymers whose viscosity is 8pa.s, and 5 parts of polymers whose viscosity is 82pa.s;

[0059] The structure of the methyl MQ silicone resin is (Me 3 SiO 0.5 ) a (SiO 2 ) b , where a / b=0.8.

[0060] The preparation method of the above-mentioned environment-friendly nail-free glue comprises the following steps:

[0061] Add 50 parts of silane-modified polyether polymer, 2 parts of PPG1000, 5 parts of methyl MQ silicone resin, 10 parts of white carbon black, and 24 parts of light calcium carbonate into the kneader, heat and knead under vacuum for 2 hours, and the heating temperature is 120°C , the vacuum degree is -0.095MPa, and the output is used as the base material.

[0062] After the base material is cooled to a temperature below 50°C, transfer it to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly nail-free glue and a preparation method of the environment-friendly nail-free glue. The environment-friendly nail-free glue comprises, by weight, 10-50 parts of silane-modified polyether polymers, 5-30 parts of plasticizer, 5-10 parts of methyl MQ silicon resin, 3-10 parts of white carbon black, 0-8 parts of thixotropic agents, 24-60 parts of reinforcing filler, 0.5-4 parts of dewatering agents and 0.2-3 parts of catalysts. The environment-friendly nail-free glue is good in comprehensive performance, high in construction efficiency, free of solvent, environmentally friendly and capable of replacing traditional iron nails to achieve a good bonding and fixing effect, and has very broad application prospect along with enhancement of the safety and environmental protection sense of people.

Description

technical field [0001] The invention relates to an adhesive, in particular to an environment-friendly nail-free glue and a preparation method thereof. Background technique [0002] Nail-free glue, also known as liquid nails, is a multifunctional decorative adhesive, mainly used for bonding and fixing various wood lines, door casing lines, plaster lines, floor tiles, various decorative pendants and various wallboard projects. In recent years, nail-free glue has gradually replaced the previous fixing methods such as nailing and drilling used in indoor and outdoor decoration, effectively avoiding noise and dust pollution, and also reducing damage to the structure of the house, and has been more and more widely used. [0003] Most of the existing nail-free adhesives use solvent-based neoprene rubber, solvent-based SBS rubber, solvent-based styrene rubber, etc. as adhesive materials, and solvents are inevitably used. For example, the prior art discloses: a kind of nail-free glue...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J171/00C09J183/04C09J11/04C09J11/06C09J11/08
Inventor 陈建军陈何国蒋金博陈弘黄恒超高敏华
Owner GUANGZHOU BAIYUN CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com