Polyolefin resin porous film

A polyolefin-based resin and porous film technology, which is applied in the direction of separators/films/diaphragms/spacers, structural parts, battery pack parts, etc., can solve the problem of coatings that cannot be coated in a thick thickness and do not meet the requirements of coating adaptation Sex and other issues, to achieve the effect of full battery performance

Active Publication Date: 2015-02-04
MITSUBISHI CHEM CORP
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the spacer is stretched in the direction of conveyance, it will shrink in the direction perpendicular to the direction of conveyance to cause wrinkles, and it will not be possible to coat the coating with a uniform thickness, causing a problem of so-called unsatisfactory coating adaptability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyolefin resin porous film
  • Polyolefin resin porous film
  • Polyolefin resin porous film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0144] Examples and comparative examples are shown below, and the polyolefin-based resin porous film of the present invention will be described in detail, but the present invention is not limited to these examples.

[0145] The obtained polyolefin-based resin porous membrane was measured and evaluated for various characteristics as follows, and the results are summarized in Table 1.

[0146] (1) Thickness

[0147] The measurement was performed at 10 positions in an unspecified plane with a dial gauge of 1 / 1000 mm, and the average value was taken as the thickness.

[0148] (2) Air permeability

[0149] The air permeability (sec / 100ml) was measured in a 20°C environment based on JIS P8117.

[0150] (3) 1% modulus in flow direction at 90°C

[0151] Based on JIS K7127, the tensile force at 1% elongation in the flow direction at 90°C was measured, and the 1% modulus in the flow direction at 90°C was calculated based on the following formula. In addition, the results of evaluati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkage stressaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The purpose of the present invention is to provide a polyolefin resin porous film that maintains pore interconnectivity, has superior air permeability, and that, due to having a high shrinkage stress, is resistant to wrinkling during conveyance processes in high-temperature environments, therefore having a superior coating suitability. The present invention is characterized in that, at 90°C, the 1% modulus in the flow direction is equal to or greater than 4.5MPa, and the air permeability is equal to or less than 800s / 100ml.

Description

technical field [0001] The present invention relates to a polyolefin-based resin porous film, which can be used as a packaging, sanitation, livestock, agricultural, construction, medical, separation film, light diffusion plate, battery separator, and is particularly suitable as a coating Separator for layered lithium-ion batteries. Background technique [0002] Lithium-ion secondary batteries have been used in batteries for portable devices such as OA, FA, home appliances, and communication equipment in the past, and research has also been carried out in the field of large-scale batteries that involve environmental issues such as electric vehicles and emergency power supplies. develop. [0003] In these large-scale battery applications, higher safety, larger capacity, higher output power, and higher voltage than small-sized batteries are required, and improvement of each battery component is being studied. In order to use batteries for electric vehicles, which have attract...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/00H01M2/16H01M50/403H01M50/406H01M50/417H01M50/449H01M50/457H01M50/489
CPCC08J2323/02C08J5/18H01M2/16H01M10/05H01M10/052B29K2023/12B29K2105/04B29L2031/3468Y02E60/10H01M50/403H01M50/449H01M50/411C08J5/2231C08J9/00H01M50/417H01M50/489H01M50/406H01M50/457H01M50/491B29C55/143C08J2323/12
Inventor 山田刚干宇佐见康竹川浩司
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com