A Process to Solve Wrinkle in Aluminum Foil Gravure Printing

A technology of gravure printing and aluminum foil, which is applied in the field of printing ink, can solve the problems of poor shape of incoming materials, incorrect adjustment of plate shape, and wrong roll shape, etc., and achieve the effect of low cost, simple process and suitable for large-scale production

Active Publication Date: 2017-02-15
JIANGSU SIDIKE NEW MATERIALS SCI & TECH CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the aluminum foil is often subjected to greater tension during rolling than subsequent processing, some of them only show poor shape during rolling, including incorrect roll grinding, incorrect roll shape, poor incoming material shape and incorrect shape adjustment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Process to Solve Wrinkle in Aluminum Foil Gravure Printing
  • A Process to Solve Wrinkle in Aluminum Foil Gravure Printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The invention provides a process for solving the wrinkling of aluminum foil gravure printing, which comprises the following steps:

[0028] Step 1, performing corona treatment on both sides of the PET film 1 with a thickness of 10-20 μm;

[0029] Step 2: Coating polyurethane composite glue on the corona surfaces on both sides of the PET film 1, and then attaching aluminum foils 2 and 3 with a thickness of 5 to 10 μm on the surface of the polyurethane composite glue;

[0030] Step 3, attaching a layer of silicone protective film 5 with a viscosity of 1 gf on the surface of one of the aluminum foils 2;

[0031] Step 4, printing ink 4 on the other surface of the aluminum foil 3 through the gravure printing rubber roller device, and then drying the ink;

[0032] Step 5, peeling off the silica gel protective film 5 .

Embodiment 2

[0034] The invention provides a process for solving the wrinkling of aluminum foil gravure printing, which comprises the following steps:

[0035] Step 1, performing corona treatment on both sides of the PET film 1 with a thickness of 10-20 μm;

[0036] Step 2: Coating polyurethane composite glue on the corona surfaces on both sides of the PET film 1, and then attaching aluminum foils 2 and 3 with a thickness of 5 to 10 μm on the surface of the polyurethane composite glue;

[0037] Step 3, attaching a layer of silicone protective film 5 with a viscosity of 3gf on the surface of one of the aluminum foils 2;

[0038] Step 4, printing ink 4 on the other surface of the aluminum foil 3 through a gravure printing rubber roller device, and then drying the ink 4;

[0039] Step 5, peeling off the silica gel protective film 5 .

Embodiment 3

[0041] The invention provides a process for solving the wrinkling of aluminum foil gravure printing, which comprises the following steps:

[0042] Step 1, performing corona treatment on both sides of the PET film 1 with a thickness of 10-20 μm;

[0043] Step 2: Coating polyurethane composite glue on the corona surfaces on both sides of the PET film 1, and then attaching aluminum foils 2 and 3 with a thickness of 5 to 10 μm on the surface of the polyurethane composite glue;

[0044] Step 3, attaching a layer of silica gel protective film 5 with a viscosity of 5 gf on the surface of one of the aluminum foils 2;

[0045] Step 4, printing ink 4 on the other surface of the aluminum foil 3 through a gravure printing rubber roller device, and then drying the ink 4;

[0046] Step 5, peeling off the silica gel protective film.

[0047] The table summarizes the viscosity of the silicone protective film and the wrinkle degree of the aluminum foil after the silicone protective film is r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tackinessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a technology for avoiding wrinkling occurring in aluminum foil intaglio printing. The technology includes the following steps that 1 corona treatment is conducted on the two sides of a PET film (1); 2 the corona surfaces of the two sides of the PET film (1) are coated with polyurethane composite adhesives, and aluminum foil (2 and 3) is stuck to the surfaces of the polyurethane composite adhesives; 3 one layer of silicone protective film (5) is stuck to the surface of the aluminum foil (2); 4 ink (4) is printed on the other surface of the aluminum foil (3) through an intaglio printing rubber device, and drying treatment is conducted on the ink; 5 the silicone protective film is removed. The technology can effectively avoid the situation that the surfaces of the aluminum foil wrinkle after the ink is printed on the aluminum foil through the intaglio printing rubber roller device, and the technology is simple, low in cost and suitable for large-scale production.

Description

technical field [0001] The invention relates to the technical field of printing ink, in particular to a process for solving the wrinkling of aluminum foil caused by printing ink on the surface of the aluminum foil by adopting a gravure coating method. Background technique [0002] In recent years, aluminum foil composite materials have been widely used in food, medicine, aerospace and other fields due to their light weight, good airtightness, good wrapping performance, and environmental protection. It is especially used in electronic products such as mobile phones, computers, TVs, etc. to play a role in shielding and shielding. With the requirement of uniform appearance in electronic products, many aluminum-plastic composite materials need to be printed to have the same color as the structural parts. The gravure printing method is one of the commonly used printing methods. Because aluminum foil is brittle, it will form wrinkles when the aluminum foil is rolled up or unrolle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41M7/00
Inventor 金闯禾文静
Owner JIANGSU SIDIKE NEW MATERIALS SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com