A kind of spray-coated coke-polishing/powdering treatment agent for synthetic leather and preparation method thereof

A technology for synthetic leather and treatment agent, which is applied in fiber treatment, textiles and papermaking, etc., can solve the problems of large amount of organic matter in treatment agent, low contrast of product coke feeling, and low degree of fine powder feeling, and achieves good glossy effect and leather. The effect of superior flour feel and excellent color development

Active Publication Date: 2016-09-07
JIANGSU BAOZE POLYMER MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The amount of organic matter used in the treatment agent of this patent is large, and the organic waste gas generated in the production is more discharged, which causes serious environmental pollution, and the contrast of the burnt feeling of the product is not high, the degree of fineness of the powdery feeling is low, and the leather simulation effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of spray-coated coke-polishing/powdering treatment agent for synthetic leather and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The synthetic leather is made up of the components of the following proportions: 23 parts by weight of modified polyurethane, 18 parts by weight of dimethylformamide, 20 parts by weight of butyl ester, 25 parts by weight of ethylene dichloride, 5 parts by weight of wax powder, 5 parts by weight of silica matting powder, 1 part by weight of water repellent, 1 part by weight of modified phenyl silicone oil, and 0.5 part by weight of dispersant.

[0026] The preparation method of the above-mentioned synthetic leather with spraying coke polishing / powder rubbing treatment agent is: under normal temperature and pressure, 11.5 parts by weight of modified polyurethane and 18 parts by weight of dimethylformamide, 20 parts by weight of butyl ester, 25 parts by weight Dichloroethane in parts by weight, wax powder in 5 parts by weight, silica matting powder in 5 parts by weight and dispersant in 0.5 parts by weight are stirred evenly; Stir the modified phenyl silicone oil evenly; f...

Embodiment 2

[0028] The synthetic leather is made up of the components of the following proportions: 25 parts by weight of modified polyurethane, 19 parts by weight of dimethylformamide, 18 parts by weight of butyl ester, 24 parts by weight of ethylene dichloride, 6 parts by weight of wax powder, 7 parts by weight of silica matting powder, 2 parts by weight of water repellent, 2 parts by weight of modified phenyl silicone oil, and 0.1 part by weight of dispersant.

[0029] The preparation method of the above-mentioned synthetic leather with spraying burnishing / powder rubbing treatment agent is: under normal temperature and pressure, 12.5 parts by weight of modified polyurethane and 19 parts by weight of dimethylformamide, 18 parts by weight of butyl ester, 24 parts by weight Parts by weight of dichloroethane, 6 parts by weight of wax powder, 7 parts by weight of silica matting powder and 0.1 parts by weight of dispersant are stirred evenly; add 2 parts by weight of water repellent and 2 par...

Embodiment 3

[0031] The synthetic leather is made up of the components of the following proportions: 26 parts by weight of modified polyurethane, 20 parts by weight of dimethylformamide, 19 parts by weight of butyl ester, 22 parts by weight of ethylene dichloride, 5 parts by weight of wax powder, 6 parts by weight of silica matting powder, 2 parts by weight of water repellent, 2 parts by weight of modified phenyl silicone oil, and 0.4 parts by weight of dispersant.

[0032] The preparation method of the above-mentioned synthetic leather with spraying burnishing / powder rubbing treatment agent is: under normal temperature and pressure, 13 parts by weight of modified polyurethane and 20 parts by weight of dimethylformamide, 19 parts by weight of butyl ester, 22 parts by weight Parts by weight of dichloroethane, 5 parts by weight of wax powder, 6 parts by weight of silica matting powder and 0.4 parts by weight of dispersant are stirred evenly; add 2 parts by weight of water repellent and 2 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a spraying burnishing / chalking treatment agent for synthetic leather and a preparation method thereof. The treatment agent contains the following components: modified polyurethane, dimethylformamide, butyl ester, dichloroethane, wax powder, silica matting powder, water repellant, modified phenyl silicone oil, and dispersant. The spraying burnishing / powder rubbing treatment agent for synthetic leather of the present invention is a new type of material used for post-printing of synthetic leather. The treatment agent obviously makes the leather flour feel of synthetic leather superior, and after wiping or polishing, the burnt feeling is strong. The leather surface has a good glossy effect and a good overall effect.

Description

technical field [0001] The present invention relates to the field of spraying burnishing / chalking treatment agent for synthetic leather, in particular, it relates to a spraying burnishing / chalking treatment agent for synthetic leather used in the back-end process of synthetic leather, and the present invention also relates to the synthetic leather The invention relates to a preparation method of spraying burnishing / powder rubbing treatment agent. Background technique [0002] Synthetic leather is usually laminated by polyurethane resin composition on non-woven fabric, woven fabric or woven fabric and other combined products, and its structure generally includes a polyurethane resin surface layer attached to the base fabric. The surface layer is mainly for decoration and the appearance achieves the effect of imitating natural leather. The synthetic leather surface treatment agent can be used for surface finishing according to the product category, which can improve the brigh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/564D06M13/402D06M13/224D06M13/08D06M11/79D06M15/643
Inventor 陈勇刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com