Modified asphalt and preparation method thereof

A technology of modified asphalt and matrix asphalt, which is applied in building components, building insulation materials, buildings, etc., can solve problems such as environmental pollution and waste of resources, and achieve low price, reduce road rutting, and good technical performance

Inactive Publication Date: 2014-09-03
RES INST OF HIGHWAY MINIST OF TRANSPORT
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Based on the serious problems such as environmental pollution and waste of resources caused by the waste toner in the above-mentioned printer (copier), therefore, a technical problem that needs to be solved urgently is: how to innovatively propose an effective measure that will print ( The waste toner in the photocopier turns waste into treasure, realizes resource recycling, protects the environment, and at the same time improves the performance of the base asphalt and saves construction costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified asphalt and preparation method thereof
  • Modified asphalt and preparation method thereof
  • Modified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of modified asphalt provided by the present embodiment, Qilu No. 70 matrix asphalt and Ricoh brand printer waste toner, the added quality of this toner accounts for 2% of the modified asphalt, aluminate coupling agent and stearic acid synergist The added mass accounts for 0.5% and 0.125% of the modified asphalt respectively. The preparation method of this modified asphalt comprises the following steps:

[0033] Put Qilu No. 70 base asphalt in an oven at 160°C to preheat until softened, weigh the carbon powder in proportion, preheat it to 100°C, add the preheated carbon powder to Qilu No. 70 base asphalt while stirring, and then put the Put the container with asphalt into a constant temperature heating mantle for high-speed shearing. The shearing temperature is 160°C, the shearing rate is 3800r / min, and the shearing time is 25min. Then weigh the aluminate coupling agent in proportion and add it to In asphalt, the shear temperature is 160°C, the shear rate is 3800...

Embodiment 2

[0042]A kind of modified asphalt provided by the present embodiment, Qilu No. 70 matrix asphalt and Ricoh brand printer waste carbon powder and aluminate coupling agent and stearic acid synergist, the added quality of this carbon powder accounts for 8% of modified asphalt , the addition of aluminate coupling agent and stearic acid synergist accounts for 1.5% and 0.75% of the modified asphalt respectively. The preparation method of this modified asphalt comprises the following steps:

[0043] Put Qilu No. 70 base asphalt into an oven at 160°C to preheat until softened, weigh the carbon powder in proportion, preheat it to 105°C, add the weighed carbon powder into Qilu No. 70 base asphalt while stirring, and then put the The container with asphalt is put into a constant temperature heating mantle for high-speed shearing, the shearing temperature is 163°C, the shearing rate is 4000r / min, and the shearing time is 30mins, then the aluminate coupling agent is weighed in proportion an...

Embodiment 3

[0051] A kind of modified asphalt provided by the present embodiment, Qilu No. 70 base asphalt and brother brand printer waste toner, aluminate coupling agent and stearic acid synergist, the added quality of this carbon powder accounts for 12% of the modified asphalt , the added mass of aluminate coupling agent and stearic acid synergist accounted for 2% and 1.5% of the modified asphalt, respectively. The preparation method of this modified asphalt comprises the following steps:

[0052] Put Qilu No. 70 base asphalt in an oven at 160°C to preheat until softened, weigh the carbon powder in proportion, preheat it to 110°C, add the weighed carbon powder to Qilu No. 70 base asphalt while stirring, and then put the Put the asphalt container into a constant temperature heating mantle for high-speed shearing. The shearing temperature is 165°C, the shearing rate is 4500r / min, and the shearing time is 35min. Then weigh the aluminate coupling agent in proportion and add it to In asphal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides modified asphalt, the modified asphalt comprises the following raw materials: a matrix asphalt, waste powdered carbon obtained from a printer or a copy, aluminic acid ester and stearic acid; a preparation method of the modified asphalt comprises the following steps: 1)respectively preheating the matrix asphalt and the waste powdered carbon; 2)mixing the preheated waste powdered carbon and the matrix asphalt to obtain a mixture; 3)simultaneously stirring or shearing the mixture while heating; 4)adding an aluminic acid ester coupling agent and continuously stirring or shearing; and 5)adding a stearic acid synergist and stirring or shearing to obtain the modified asphalt. The modified asphalt has the advantages of good technology performance and low price, the waste powdered carbon in a toner cartridge of the printer or a copy machine can be reused, the modified asphalt has good social, economic and environmental protection benefits; the softening point of the matrix asphalt can be increased by 3-8 DEG C, so that the high temperature stabilization performance of the asphalt mixture can be increased, pavement track is reduced, water stabilization performance is increased, and the low temperature performance grade of the modified asphalt can be kept or improved.

Description

technical field [0001] The invention relates to a modified asphalt, in particular to a method for preparing the modified asphalt by blending waste carbon powder after use of a printer or copy, an aluminate coupling agent and a stearic acid synergist. Background technique [0002] Printer is one of the most common equipment in daily office. The laser printer commonly used in the office is actually a "big household" of environmental pollution. The harm it brings to your body is comparable to that of cigarettes. According to statistics, in 2008, more than 45 million ink cartridges and 4 million toner cartridges were discarded in my country, with a total volume of more than 400,000 cubic meters. If these discarded consumables were loaded into train carriages, it would be enough to fill 5,000 cartridges. According to the calculation of the environmental protection department, one drop of residual ink pollutes 60 cubic meters of water, and one discarded ink cartridge pollutes 1 cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L25/14C08K13/02C08K3/22C08K3/04C08K5/09C08K5/10
Inventor 李闯民李健廖建胜
Owner RES INST OF HIGHWAY MINIST OF TRANSPORT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com