Water-permeable reclaimed asphalt mixture paving brick and preparation method thereof
A technology for recycling asphalt and pavement bricks, applied in the field of pavement maintenance materials, can solve problems such as environmental pollution, waste of resources, etc., and achieve the effects of changing acid-base conditions, saving costs, and facilitating maintenance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0026] 100 parts of recycled asphalt mixture, 2 parts of water, 3 parts of emulsified asphalt, 2 parts of cement, 1 part of polyvinyl acetate emulsion, water permeability coefficient = 1.3mm / s, Kentaburg scattering loss = 18.7%, splitting strength = 0.64 MPa, maximum compressive strength = 10.2MPa.
example 2
[0028] 90 parts of recycled asphalt mixture, 10 parts of new aggregate, 3 parts of water, 4 parts of emulsified asphalt, 1 part of cement, 1 part of mineral powder, 1 part of polyvinyl acetate emulsion, water permeability coefficient = 1.7mm / s, Kentaburg Scattering loss = 17.5%, splitting strength = 0.67MPa, maximum compressive strength = 12.6MPa.
example 3
[0030] 80 parts of recycled asphalt mixture, 20 parts of new aggregate, 4 parts of water, 5 parts of emulsified asphalt, 2 parts of cement, 2 parts of mineral powder, 3 parts of polyvinyl acetate emulsion, water permeability coefficient = 1.4mm / s, Kentaburg Scattering loss = 15.3%, splitting strength = 0.72MPa, maximum compressive strength = 14.1MPa.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com