A kind of chlorinated alkyd resin and preparation method thereof

A technology of chlorinated alkyd and alkyd resin, which is applied in the direction of anti-corrosion coatings, polyester coatings, coatings, etc., can solve the problems of high production and use costs of anti-corrosion coatings, achieve excellent paint-making performance and anti-corrosion performance, low cost, The effect of cheap and easy-to-obtain raw materials

Active Publication Date: 2016-03-02
山东齐鲁漆业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem of high production and use costs of anti-corrosion coatings, the invention provides a chlorinated alkyd resin with low price, excellent paint-making performance and anti-corrosion performance and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1), pre-feed CO into the empty reactor 2 6min, the gas flow rate is 3m 3 / h;

[0034] (2), sequentially add 36.0kg of glycerin, 46.0kg of phthalic anhydride, 104.0kg of soybean oil fatty acid, 5.0kg of rosin, and 15.0kg of xylene, stir and heat up to 180°C for 90 minutes, then heat up to 240°C for 5 hours. The acid value is equal to 16mgKOH / g;

[0035] (3) Cool down to 160°C, transfer the reactant to the dilution kettle, add 180.0kg of xylene, and when the temperature drops to 115°C, filter with a filter bag with a specification of ≦20 μm.

[0036] (4), gained alkyd resin is transferred to reaction kettle after being down to room temperature, feeds chlorine gas, and gas flow rate is 0.08m 2 / h reaction to iodine value 3gI 2 / 100g to obtain chlorinated alkyd resin.

Embodiment 2

[0038] (1), pre-feed CO into the empty reactor 2 6min, the gas flow rate is 3m 3 / h;

[0039] (2), sequentially add 42.0kg of pentaerythritol, 46.0kg of phthalic anhydride, 104.0kg of soybean oil fatty acid, 3.0kg of rosin, and 12.0kg of xylene, stir and heat up to 180°C for 90 minutes, then heat up to 240°C for 5 hours. The acid value is equal to 17mgKOH / g;

[0040] (3) Cool down to 160°C, transfer the reactant to the dilution kettle, add 185.0kg of xylene, and when the temperature drops to 115°C, filter with a filter bag of ≦20 μm.

[0041] (4), gained alkyd resin is transferred to reaction kettle after being down to room temperature, feeds chlorine gas, and gas flow rate is 0.06m 2 / h react until the iodine value is 4gI 2 / 100g to obtain chlorinated alkyd resin.

Embodiment 3

[0043] (1), pre-feed CO into the empty reactor 2 6min, the gas flow rate is 4m 3 / h;

[0044] (2), sequentially add 50.0kg of glycerin, 52.0kg of phthalic anhydride, 120.0kg of soybean oil fatty acid, 8.0kg of rosin, and 20.0kg of xylene, stir and heat up to 180°C for 90 minutes, heat up to 240°C for 4 hours, The acid value is equal to 18mgKOH / g;

[0045] (3) Cool down to 160°C, transfer the reactant to the dilution kettle, add 240.0kg of 200# solvent oil, and filter with a filter bag with a specification of ≦20μm when the temperature drops to 115°C.

[0046] (4), after the obtained alkyd resin is lowered to room temperature, it is transferred to the reaction kettle, and chlorine gas is introduced, and the gas flow rate is 0.1m 2 / h reaction to iodine value 2gI 2 / 100g to obtain chlorinated alkyd resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to chlorinated alkyd resin and a preparation method thereof. The preparation method comprises the following steps: preparing alkyd resin by taking glycerinum, pentaerythritol, phthalic anhydride, soya bean oil fatty acid and rosin as raw materials; after dilution, introducing chlorine to chlorinate to obtain the chlorinated alkyd resin. The chlorinated alkyd resin provided by the invention has the advantages of low cost, good paint-making performance, good preservative effect, flame retardance and the like. The preparation process of the chlorinated alkyd resin is simple and convenient, mild in condition and suitable for industrialized production; the chlorinated alkyd resin has a wide application prospect in the field of coating.

Description

Technical field: [0001] The invention relates to a chlorinated alkyd resin and a preparation method thereof. The chlorinated alkyd resin has good corrosion resistance. Background technique: [0002] Alkyd resin has become the largest and most widely used synthetic resin in the coatings industry because of its wide source of synthetic raw materials, flexible formula, simple process, excellent comprehensive performance of coating film, and can be endowed with various performance characteristics through various modifications. Alkyd paint formulated by alkyd resin is still one of the most important paint varieties in the paint market so far, and its output accounts for about 20% to 25% of the total paint industry. Alkyd paint based on alkyd resin has the advantages of good self-drying property, low price, diverse and simple construction, and is widely used as decorative anti-corrosion materials on indoor and outdoor buildings, steel equipment, machines and other equipment. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/91C09D167/08C09D5/08
Inventor 孙洪源孙亮亮孙文俊王庆军段洪东尹晓聪
Owner 山东齐鲁漆业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com