A kind of bright red color crystal bead embryo and preparation method thereof

A technology for crystal bead embryo and color, which is applied in the field of bright red crystal bead embryo and its preparation, can solve the problems of environmental pollution, uneven color, poor coloring and the like, and achieves the effects of good production efficiency, good colorability and bright color.

Active Publication Date: 2016-05-25
浙江鑫伟兴水晶有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The bright red color crystal bead embryo is used to prepare the semi-finished product of the bright red color crystal product. The existing bright red color crystal bead embryo technology is manufactured in a crucible, which has poor coloring, uneven color, patterns, unstable product quality, and low production efficiency. Not suitable for continuous mass production, and burning with coal will cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of bright red color crystal bead embryo of the present invention, this bright red color crystal bead embryo is made up of following proportioning composition by weight: 100 parts of quartz sands, 12 parts of zinc oxide, 29 parts of soda ash, 18 parts of potassium carbonate, 12 parts of boric acid, 3 parts of calcium carbonate, 1 part of aluminum hydroxide, 1 part of table salt, 0.2 part of cadmium yellow, 0.6 part of selenium powder and 1 part of cadmium red.

[0018] The preparation process of the bright red color crystal bead embryo is as follows:

[0019] 1) Extract 100 parts of quartz sand, 12 parts of zinc oxide, 29 parts of soda ash, 18 parts of potassium carbonate, 12 parts of boric acid, 3 parts of calcium carbonate, 1 part of aluminum hydroxide, 1 part of table salt, and 0.2 parts of cadmium yellow according to the proportion by weight. , 0.6 parts of selenium powder and 1 part of cadmium red are mixed evenly;

[0020] 2) Granulate the uniformly mixed b...

Embodiment 2

[0025] It differs from Example 1 in that the bright red color crystal bead embryo is composed of the following proportioning ingredients in parts by weight: 150 parts of quartz sand, 18 parts of zinc oxide, 54 parts of soda ash, 27 parts of potassium carbonate, 18 parts of boric acid, carbonic acid 5 parts of calcium, 2 parts of aluminum hydroxide, 2 parts of table salt, 2.5 parts of cadmium yellow, 1.8 parts of selenium powder and 5 parts of cadmium red.

Embodiment 3

[0027] It differs from Example 1 in that the bright red color crystal bead embryo is composed of the following proportioning ingredients in parts by weight: 112 parts of quartz sand, 14 parts of zinc oxide, 31 parts of soda ash, 22 parts of potassium carbonate, 15 parts of boric acid, carbonic acid 4 parts of calcium, 1 part of aluminum hydroxide, 2 parts of table salt, 0.8 parts of cadmium yellow, 1.1 parts of selenium powder and 2 parts of cadmium red.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a bright red color crystal pearl blank and a preparation method thereof. The bright red color crystal pearl blank comprises, by weight, 100-150 parts of quartz sand, 12-18 parts of zinc oxide, 29-54 parts of soda ash, 18-27 parts of potassium carbonate, 12-18 parts of boric acid, 3-5 parts of calcium carbonate, 1-2 parts of aluminum hydroxide, 1-2 parts of gravy salt, 0.2-2.5 parts of cadmium yellow, 0.6-1.8 parts of selenium powder, and 1-5 parts of cadmium red. According to the present invention, during bright red color crystal pearl blank preparing, oxidation reduction balance of copper ions during a melting process maintains a stable state so as to obtain good colorability; and the lead-containing raw material is not used, and advantages of good gloss, bright and uniform color, no color difference, no pattern, high yield, no lead, no pollution and good production benefit are provided.

Description

technical field [0001] The invention relates to a bright red color crystal bead embryo and a preparation method thereof. Background technique [0002] The bright red color crystal bead embryo is used to prepare the semi-finished product of the bright red color crystal product. The existing bright red color crystal bead embryo technology is manufactured in a crucible, which has poor coloring, uneven colors, patterns, unstable product quality, and low production efficiency. It is not suitable for continuous mass production, and burning with coal causes environmental pollution. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a bright red color crystal bead embryo with good coloring reproducibility, consistent color, no color difference, no pattern, stable product quality, high production efficiency, and suitable for continuous tank kiln production operations. [0004] In order to solve the above problems, the prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/06C03C4/02
Inventor 杨鑫法
Owner 浙江鑫伟兴水晶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap