Microgel finishing agent for improving wearing comfort of fabrics

A microgel finishing agent, a technology for comfortable wearing, applied in fiber treatment, textiles and papermaking, etc., can solve the problems that the wearing comfort needs to be improved, and achieve the effect of improving comfort and improving comfort

Inactive Publication Date: 2014-04-02
常熟市天赢印染有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The wearing comfort of existing fabrics needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A microgel finishing agent for improving the wearing comfort of fabrics, made by reacting the following raw materials:

[0021] 1g / L lauryltrimethylammonium sulfate,

[0022] 15g / L of citric acid,

[0023] 8g / L of N-isopropylacrylamide,

[0024] 200g / L deionized water,

[0025] 7g / L of glacial acetic acid,

[0026] 1g / L of N,N-methylenebisacrylamide,

[0027] 8g / L hypophosphite,

[0028] 1g / L ammonium persulfate,

[0029] 3g / L chitosan,

[0030] 1g / L of hydroxypropyl methylcellulose,

[0031] 1g / L of triethanolamine.

Embodiment 2

[0033] A microgel finishing agent for improving the wearing comfort of fabrics, made by reacting the following raw materials:

[0034] 2g / L lauryltrimethylammonium sulfate,

[0035] 20g / L of citric acid,

[0036] 9g / L of N-isopropylacrylamide,

[0037] 200g / L deionized water,

[0038] 8g / L of glacial acetic acid,

[0039] 2g / L of N,N-methylenebisacrylamide,

[0040] 9g / L hypophosphite,

[0041] 2g / L ammonium persulfate,

[0042] 4g / L chitosan,

[0043] 2g / L of hydroxypropyl methylcellulose,

[0044] 2g / L of triethanolamine.

Embodiment 3

[0046] A microgel finishing agent for improving the wearing comfort of fabrics, made by reacting the following raw materials:

[0047] 1.2g / L lauryltrimethylammonium sulfate,

[0048] 18g / L of citric acid,

[0049] 8.9g / L of N. isopropylacrylamide,

[0050] 200g / L deionized water

[0051] 7.8g / L of glacial acetic acid,

[0052] 1.2g / L of N,N.methylenebisacrylamide,

[0053] 8.9g / L hypophosphite,

[0054] 1.2g / L ammonium persulfate,

[0055] 3.4g / L chitosan,

[0056] 1.2g / L hydroxypropyl methylcellulose,

[0057] 1.2g / L of triethanolamine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a microgel finishing agent for improving wearing comfort of fabrics. The microgel finishing agent is prepared from the following raw materials by reaction: 1-2g / L of dodecyl trimethyl ammonium sulfate, 15-20g / L of citric acid, 8-9g / L of N-isopropylacrylamide, 200g / L of deionized water, 7-8g / L of glacial acetic acid, 1-2g / L of N,N-methylene bisacrylamide, 8-9g / L of hypophosphorous acid salt, 1-2g / L of ammonium persulfate, 3-4g / L of chitosan, 1-2g / L of hydroxypropyl methyl cellulose and 1-2g / L of triethanolamine. By adopting the microgel finishing agent provided by the invention, the hydrophilia, the wettability and the water vapor permeability can be adjusted, so as to improve the wearing comfort of fabrics.

Description

technical field [0001] The invention relates to a microgel finishing agent for improving the wearing comfort of fabrics. Background technique [0002] The wearing comfort of the existing fabric needs to be improved. Contents of the invention [0003] The object of the present invention is to provide a microgel finishing agent for improving the wearing comfort of fabrics, which can adjust hydrophilicity, wettability and water vapor transmission rate, thereby improving the wearing comfort of fabrics. [0004] In order to achieve the above object, the technical solution of the present invention is to design a microgel finishing agent that improves the wearing comfort of fabrics, which is made by reacting the following raw materials: [0005] 1-2g / L lauryltrimethylammonium sulfate, [0006] 15-20g / L citric acid, [0007] 8-9g / L N-isopropylacrylamide, [0008] 200g / L deionized water [0009] 7-8g / L of glacial acetic acid, [0010] 1-2g / L of N,N-methylenebisacrylamide, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/207D06M13/463D06M13/41D06M13/188D06M11/70D06M11/50D06M15/03D06M15/09D06M13/368
Inventor 瞿志忠
Owner 常熟市天赢印染有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap