Oil-proof paper and production method thereof

A production method and oil-proof paper technology, which is applied in papermaking, paper coating, textiles and papermaking, etc., can solve the problems of reducing paper degradation performance and complicated papermaking process, and achieve excellent degradability, reduced consumption, and reduced costs.

Active Publication Date: 2014-03-26
广东悦声纸业科技有限公司
View PDF5 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Special CN201210272313.3 (Gao Xiaoming. A production process of oil-proof paper: China, CN201210272313.3 [P].2012-11-7) discloses a production process of oil-proof paper. The safety hazards that may be brought about by the extensive use of oil-repellents in oil-proof paper greatly reduce the amount of oil-repellents used, but wax emulsions need to be added in this process, which reduces the degradation performance of paper, and the papermaking process is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-proof paper and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The preparation method of greaseproof paper 110 of the present invention, its steps are as follows:

[0021] (1) Provide the initial base paper 100 .

[0022] (2) Preparation of composite oil-proof coating

[0023] Using starch, plasticizer, coalescent, fluoropolymer and water, the temperature of the water bath heated in the water bath is 70-95°C

[0024] The starch and the film-forming aid are dissolved under the condition of 5-30 minutes, and the starch, the plasticizer, the film-forming aid, the fluorine-containing compound and water are mixed under the condition of stirring for 5-30 minutes to prepare a composite oil-proof coating.

[0025] (3) Coating a composite oil-repellent coating on the surface of the base paper 100 and drying it with hot air at a drying temperature of 70-105° C. to form an oil-repellent coating 101 . A coating machine is used to apply the composite oil-repellent coating to the surface of the base paper 100 . After drying, the moisture in t...

example 1

[0030] Base paper 100 is made of transparent paper with a basis weight of 20 g / m 2 .

[0031] Composite oil-proof coating: 100 parts of starch, 10 parts of plasticizer, 100 parts of film-forming aid, 20 parts of fluorine-containing compound. The starch is natural starch. Described plasticizer is glycerol. The film-forming aid is polyvinyl alcohol. The fluorine-containing compound is perfluoropolyether phosphate, and the solid content of the coating is 5%.

[0032] Dissolve starch and film-forming aids under the condition that the water bath temperature of the water bath is 70°C, and then mix the starch, plasticizer, film-forming aids, fluorine-containing compounds and water at a speed of 80 r / min. Stir for 5 minutes to prepare a composite oil-proof coating.

[0033] Use a composite oil-repellent coating to form an oil-repellent coating on the surface of base paper 100 by roll coating, with a coating weight of 9.5 g / m 2 , and use hot air to dry at a drying temperature of ...

example 2

[0036] The base paper 100 is translucent paper with a basis weight of 32 g / m 2 .

[0037] Composite oil-proof coating: 100 parts of starch, 40 parts of plasticizer, 50 parts of film-forming aid, 30 parts of fluorine-containing compound. The starch is modified starch. Described plasticizer is sorbitol. The film-forming aid is cellulose. The fluorine-containing compound is perfluoropolyether phosphate, and the solid content of the paint is 15%.

[0038] Dissolve the starch and film-forming aids under the condition that the temperature of the water bath heated by the water bath is 95°C, and then mix the starch, plasticizer, film-forming aids, fluorine-containing compounds and water at a speed of 200 r / min. Stir for 30 minutes to prepare a composite oil-proof coating.

[0039] Use a composite oil-repellent coating to form an oil-repellent coating on the surface of base paper 100 by roll coating, with a coating weight of 1 g / m 2 , and dried with hot air at a drying temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses oil-proof paper and a production method thereof, and belongs to the technical field of oil-proof paper. The production method comprises the following steps: coating or sizing the base paper with composite oil-proof paint; and drying to obtain the finished paper, wherein the composite oil-proof paint comprises the following components in parts by weight: 100 parts of starch, 10-40 parts of a plasticizer, 5-100 parts of a coalescing agent and 1-30 parts of a fluorine-containing compound; the solid content of the paint is 5-15%. The composite oil-proof paint comprises the starch, the plasticizer, the coalescing agent and the fluorine-containing compound. The oil-proof paper disclosed by the invention has the advantages of relatively low cost and excellent oil-proof property.

Description

technical field [0001] The invention belongs to the technical field of greaseproof paper, in particular to a production method of greaseproof paper. technical background [0002] At present, as the application fields of paper become more and more extensive, many applications require paper to have a certain oil resistance, such as various food packaging paper, outer packaging cardboard, release paper, carbonless copy paper and various art papers. Research and development of new and efficient greaseproof paper will become the mainstream of the development of greaseproof paper field. [0003] At present, the oil-proof paper sold in the market is basically coated with fluoropolymer on the surface of the paper, but the use of fluoropolymer is large, the cost is high, and the fluoropolymer with high carbon chain has environmental problems. Special CN201210272313.3 (Gao Xiaoming. A production process of oil-proof paper: China, CN201210272313.3 [P].2012-11-7) discloses a productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/14D21H21/14
Inventor 陈港蒋轩方志强
Owner 广东悦声纸业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com