Creep-resistant polyester and its preparation method

A technology of creep resistance and polyester, applied in the direction of single-component copolyester rayon, conjugated synthetic polymer rayon, etc., to improve hydrolysis resistance, increase relative molecular weight, and expand application range Effect

Active Publication Date: 2015-04-01
JIANGSU HENGLI CHEM FIBER
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few studies on creep resistance of polyester

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Creep-resistant polyester and its preparation method
  • Creep-resistant polyester and its preparation method
  • Creep-resistant polyester and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0051] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 1.5% of 15mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl) ethylene] diphenol mass, at room temperature Stir the reaction for 16 hours; then cool to room temperature, then add 5mol / L of 30% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol Sodium hydroxide solution, the sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 10 h; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick like liquid, which was added to absolute ethanol for recrystallization to obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]dip...

Embodiment 2

[0056] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0057] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 2.0% 10mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol mass, at room temperature Stir the reaction for 18 hours; cool to room temperature, then add 40% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol of 3mol / L Sodium hydroxide solution, sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 15 hours; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick liquid, add it to absolute ethanol for recrystallization, and obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl Crys...

Embodiment 3

[0062] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0063] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 1.8% of 12mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol mass, at room temperature Stir the reaction for 17h; cool to room temperature, then add 35% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol of 4mol / L Sodium hydroxide solution, sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 13h; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick liquid, add it to absolute ethanol for recrystallization, and obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl Crystals of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to creep-resistant polyester and its preparation method. According to the preparation method, polyester is mixed with a fluorine-containing epoxy compound or a fluorine-containing epoxy compound is added during the synthesis process of polyester. Then, the creep-resistant polyester can be obtained. By the use of the fluorine-containing epoxy compound for blocking modification of the polyester, creep-resistant performance of the polyester can be improved to some extent, and hydrolysis resistance and performance stability of the polyester can be raised. Fiber prepared from the creep-resistant polyester can be used in a hot and humid environment for a long time, and has a huge prospect in the fields of plastic packing, waterproof fabric, ropes, cables, marine fiber and the like.

Description

technical field [0001] The invention relates to a creep-resistant polyester and a preparation method thereof, in particular to a creep-resistant polyester modified by using a fluorine-containing epoxy compound as an end-capping agent and a preparation method thereof. Background technique [0002] Polyester (PET) is one of the most widely used synthetic polymers by humans. It has high strength, high modulus and good heat resistance. It is the earliest linear thermoplastic polymer to achieve industrial applications. It is used in plastic packaging, film And chemical fiber and other fields have been widely used. [0003] The molecular chain structure of polyester is a linear macromolecule containing a benzene ring structure, the functional groups on the molecular chain are arranged neatly, there are no branches, and the flexibility of the macromolecular chain is poor. Compared with other polymer materials, it is more difficult for the molecular chain of polyester to slip, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/84D01F8/14C08G81/00C08G63/682
Inventor 高亮王丽丽李文刚汤方明孙晓华
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap