A kind of cross-linked polypropylene microporous foam material and its production method

A technology of microporous foaming material and cross-linked polypropylene, which is applied in the coating and other directions, can solve the problems of small elastic recovery and inability to adapt to the rebound performance, and achieve the effect of good resilience and delicate hand feeling

Active Publication Date: 2016-01-06
ZHEJIANG XINHENGTAI ADVANCED MATERIAL
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is that the existing non-crosslinked polypropylene foaming material is easy to produce irreversible plastic deformation when stressed due to its internal non-network structure, and the elastic recovery is small, so it cannot adapt to the requirements of relatively high resilience performance. high field, thereby providing a cross-linked polypropylene microcellular foam material and a production method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cross-linked polypropylene microporous foam material and its production method
  • A kind of cross-linked polypropylene microporous foam material and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A cross-linked polypropylene microporous foam material comprises the following components: 100 parts by weight of polypropylene resin, 0.5 parts by weight of radiation sensitizer, and 0.1 part by weight of antioxidant.

[0028] Wherein the polypropylene resin adopts long-chain branched polypropylene with a melt index of 1.5g / 10min, the radiation sensitizer is trimethylolpropane triacrylate, and the antioxidant is tri(3,5-di-tert-butyl- 4-Hydroxybenzyl) isocyanurate.

[0029] The production method adopted by the above-mentioned cross-linked polypropylene microcellular foaming material comprises the following steps:

[0030] a): raw material mixing: melt and mix polypropylene resin, radiation sensitizer and antioxidant through a twin-screw extruder, and extrude to obtain a polypropylene foamed substrate;

[0031] b): CO 2 Gas-impregnated substrate: put the polypropylene foamed substrate produced in step a) into a high-pressure foaming mold, close the foaming mold and he...

Embodiment 2

[0037] A cross-linked polypropylene microporous foam material comprises the following components: 100 parts by weight of polypropylene resin, 1 part by weight of radiation sensitizer, and 0.2 part by weight of antioxidant.

[0038] Wherein the polypropylene resin adopts long-chain branched polypropylene with a melt index of 1.7g / 10min, the radiation sensitizer is neopentyl glycol dimethacrylate, and the antioxidant is tetrakis (3,5-di-tert-butyl -4-hydroxy)pentaerythritol phenylpropionate.

[0039]The production method adopted by the above-mentioned cross-linked polypropylene microcellular foaming material comprises the following steps:

[0040] a): raw material mixing: melt and mix polypropylene resin, radiation sensitizer and antioxidant through a twin-screw extruder, and extrude to obtain a polypropylene foamed substrate;

[0041] b): CO 2 Gas-impregnated substrate: put the polypropylene foamed substrate produced in step a) into a high-pressure foaming mold, close the foa...

Embodiment 3

[0047] A cross-linked polypropylene microporous foam material comprises the following components: 100 parts by weight of polypropylene resin, 1.5 parts by weight of radiation sensitizer, and 0.5 parts by weight of antioxidant.

[0048] Wherein the polypropylene resin adopts long-chain branched polypropylene with a melt index of 2g / 10min, the radiation sensitizer is 1,6-hexanediol diacrylate, and the antioxidant is tri(2,4-di-tert-butyl phenyl) phosphite.

[0049] The production method adopted by the above-mentioned cross-linked polypropylene microcellular foaming material comprises the following steps:

[0050] a): raw material mixing: melt and mix polypropylene resin, radiation sensitizer and antioxidant through a twin-screw extruder, and extrude to obtain a polypropylene foamed substrate;

[0051] b): CO 2 Gas-impregnated substrate: put the polypropylene foamed substrate produced in step a) into a high-pressure foaming mold, close the foaming mold and heat up to the foamin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a cross-linked polypropylene microcellular foam material. The cross-linked polypropylene microcellular foam material comprises the following raw materials in parts by weight: 99-100 parts of polypropylene resin, 0.1-2 parts of irradiation sensitizer and 0.1-3 parts of antioxidant and is produced through the following steps: mixing the raw materials; dipping a substrate with CO2 gas; foaming the substrate; performing irradiation treatment on the foam material; performing high-temperature annealing; detecting the foam material. The cross-linked polypropylene microcellular foam material has the advantages that the polypropylene resin, the irradiation sensitizer and the antioxidant are subjected to the steps of mixing the raw materials, dipping the substrate with CO2 gas, foaming the substrate, performing irradiation treatment on the foam material, performing high-temperature annealing and detecting the foam material in sequence to obtain a high-resilience polypropylene microcellular foam product with small cell size and high cell density; the cross-linked polypropylene microcellular foam material prepared by the method has the characteristics of good resilience, fine handfeel, no toxicity and no smell, and can be widely applied to the fields with high requirements on the resilience and the sanitation level of the foam material.

Description

technical field [0001] The invention relates to a cross-linked polypropylene microporous foam material and a production method thereof. Background technique [0002] Polypropylene microporous foam material refers to the pore size less than 100μm and the pore density greater than 1.0×10 6 piece / cm 3 The porous polypropylene foam material, a large number of micron-sized cells in the material endows the polypropylene foam material with excellent properties such as light weight, high strength, low thermal conductivity, and high diffuse reflectivity, so the polypropylene microcellular foam material has a wide range of applications. field of application. [0003] Using supercritical CO 2 As a foaming agent, the solid-state foaming technology makes polypropylene foam in the deformable region lower than its melting point, which is an effective means to form a large number of tiny cells in the polypropylene matrix. By using supercritical CO 2 The polypropylene microcellular foam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F255/02C08L51/06C08K5/134C08K5/526C08K5/3492C08J9/12C08J9/36C08J3/28C08J3/24
Inventor 陈春平
Owner ZHEJIANG XINHENGTAI ADVANCED MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com