Method for firing Taoxun

A technology of pottery xun and nixing pottery clay, applied in instruments, wind instruments, musical instruments, etc., can solve the problems of easy cracking, small specific gravity, etc., and achieve the effect of being unbreakable

Active Publication Date: 2015-04-01
覃雄
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing problems: The pottery Xun made by firing low-temperature pottery clay can be molded at a relatively low temperature because of the low specific gravity of the soil itself. In this way, the wall of the pottery Xun after molding is thinner and the hardness is lower, but when using this process When the pottery xun made of high-pitched and raw materials is played at a high pitch, it is easy to crack when it is vibrated by the sound

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for firing Taoxun
  • Method for firing Taoxun

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Such as figure 1 The shown method flow chart of firing pottery Xun, this method specifically comprises the following steps:

[0016] 101. Using mud made of Nixing pottery clay with a shrinkage rate of 10%-14% to make a blank with a wall thickness of 1-1.5cm;

[0017] 102. Open a sound hole on the finished blank;

[0018] 103. Put the billet with the sound hole into the firing kiln and seal and fire it according to the preset process.

[0019] In the method for firing pottery Xun provided by the present invention, Nixing pottery clay is used as a raw material, and its molding temperature is 1100°C, which belongs to high-temperature molding pottery clay. Pottery Xun is hard and not easy to break.

[0020] The mud made of Nixing pottery clay can be purchased directly, but when making pottery xuns that can be played, it is necessary to use mud with a shrinkage rate of 10%-14% and make the wall thickness 1-1.5cm The finished product fired from the thick billet can meet t...

Embodiment 2

[0022] Such as figure 2 The shown method flow chart of firing pottery Xun, this method specifically comprises the following steps:

[0023] 201. The mud made of Nixing pottery clay with a shrinkage rate of 10%-14% is used to make a blank with a wall thickness of 1-1.2cm;

[0024] 202. Open the sound hole on the finished billet. According to the shrinkage rate of the mud used, each sound hole opened on the wet billet needs to be lowered by 150-180 cents than the standard pitch;

[0025] 203. Put the billet with the sound holes into the firing kiln, seal and continue heating and firing for 3-3.5 hours to reach 300°C, and control the heating rate of the firing kiln to 1.2-1.6°C / min;

[0026] 204. Continue heating and firing for 3-3.5 hours to reach 600°C, and control the heating rate of the firing kiln to 1.5-1.6°C / min;

[0027] 205. Continue heating and firing for 3-3.5 hours to reach 1100°C for molding, and control the heating rate of the firing kiln to 2.5-3°C / min;

[0028...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of artware processing and in particular relates to a method for firing Taoxun which is a musical instrument. The method specifically comprises the following steps of making a blank with the wall thickness of 1-1.5 cm by Nixing pottery clay with the contraction rate of 10-14 percent, forming tone holes in the blank, putting the blank with the tone holes into a firing kiln, and firing the Taoxun in a sealing manner for forming according to a preset technology. According to the method for firing the Taoxun disclosed by the invention, the finished Taoxun product manufactured by the Nixing pottery clay is hard, firm and unlikely to break and has a thick and turbulent sound; the tone is steady, firm and penetrating; the playing requirement of Taoxun can be met.

Description

technical field [0001] The invention relates to the field of handicraft processing, in particular to a method for firing pottery xun. Background technique [0002] Tao Xun is one of the oldest national musical instruments in China. The main production process is to use prepared wet clay to make a blank, dry it, tune it, and then fire it in a kiln. Due to the natural shrinkage of the clay during the firing process, the fired Xun has to be tuned for the last time to ensure the final professional pitch of the instrument. The pitch control of Tao Xun is mainly realized by adjusting the size of the sound hole. Most of the currently used pottery xuns are fired from low-temperature pottery clay whose firing temperature is below 800°C. [0003] Existing problems: The pottery Xun made by firing low-temperature pottery clay can be molded at a relatively low temperature because of the low specific gravity of the soil itself. In this way, the wall of the pottery Xun after molding is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/32G10D7/00
Inventor 覃雄谢寿孟
Owner 覃雄
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com