A kind of color toner and preparation method thereof

A technology of color toner and compound wax, which is applied in the fields of electrography, optics, instruments, etc., can solve the problems of poor copy resolution and color, difficulty in recycling and cleaning color toner, etc., and achieves good gloss and hardness. , the effect of easy processing

Inactive Publication Date: 2016-01-20
KINGFA SCI & TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantage of the "suspension polymerization method" is that the wide particle size distribution of the color toner makes the printing and copying resolution and color poor, and the color toner particles are too round, which leads to the recovery and cleaning of the color toner remaining on the photoreceptor. difficulty
Zhou Xueliang, Zhang Weigang, Zhou Dongliang, etc. used in-situ emulsion polymerization to prepare color toner for printers and copiers. By selecting styrene, butyl acrylate, polyester resin, polypropylene wax, azo pigments, charge regulators, and azobis Raw materials such as isobutylcyanide, surfactant and silicon dioxide are made of color toner through steps such as reaction, separation, cleaning, drying and modification; however, there are few literatures and reports on the research of wax in emulsion polymerization. In particular, the complex wax is mixed evenly in the emulsion preparation stage, thereby improving the printing durability of the color toner, and finally improving the quality of the color toner. There are few reports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below through specific embodiments. The following examples are preferred implementation forms of the present invention, but the implementation manners of the present invention are not limited by the following examples.

[0034] The raw materials used in the examples and comparative examples are now described as follows, but not limited to these materials:

[0035] The black pigment used is imported pigment black R330R, the yellow pigment is permanent transparent yellow PY83, the blue pigment is phthalocyanine blue PB15:3, and the red pigment is permanent bright red PR170.

[0036] The surfactant used is the CO-436 surfactant produced by the Wuxi production base of the French company Rhodia;

[0037] Described molecular weight regulator is the dodecyl mercaptan of Guangzhou Sanwang Chemical Material Co., Ltd.;

[0038] The charge regulator used is the DL-N28 metal complex produced by Hubei Dinglong Chemical Co., Ltd.;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a color toner, which comprises the following components in parts by weight: 60-80 parts of styrene; 15-25 parts of butyl acrylate; 3-7 parts of composite wax; 3-6 parts of pigment; 0.2~1.5 parts of agent; 1~2 parts of ammonium persulfate; 0.1~2 parts of molecular weight regulator; 1.0~3.0 parts of surfactant; 1~4 parts of silicon dioxide; or two or more of C80 paraffin waxes; the present invention can properly reduce the polymerization speed by adding composite wax in the emulsion preparation stage, compared with the use of a single wax, so that its toughness and printing durability are improved; in addition, the composite wax It can reduce the cost and make the color toner have better emulsification, better gloss, better hardness and better stability; and the particle size distribution is narrow, the average particle size D50 is 5~8μm, making the particle size diameter is easy to control.

Description

technical field [0001] The invention relates to the application field of electrostatic imaging technology, in particular to a color toner for copiers and printers and a preparation method thereof. Background technique [0002] Color toner is a key consumable for color laser printing and color digital copying, mainly composed of resin, pigment, additives, etc. With the development of information technology, network technology, office automation and modernization, as well as the popularization of laser printers, laser digital copiers, and digital cameras, and the development in the direction of digitization and colorization, the demand for color toner is increasing. Quality requirements are also getting higher and higher. [0003] At present, the preparation methods of color toner mainly fall into two categories: physical method and chemical polymerization method. The physical method, also known as "melting method", is to heat and knead resin (mainly styrene-butyl acrylate c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03G9/08
Inventor 欧阳春平袁绍彦陈平绪曾祥斌周英辉欧阳晓岳饶湘
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products