Loaded non-metallocene catalyst, its preparation method and application

A non-metallocene, non-metallocene ligand technology, applied in the field of non-metallocene catalysts, can solve the problems of low catalytic activity, difficult to control the carrier molding process and particle shape, easy to break, etc., and achieve the effect of simple preparation method

Active Publication Date: 2013-09-18
CHINA PETROLEUM & CHEM CORP +1
View PDF23 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of catalyst adopts vacuum drying or solvent precipitation during the carrier forming process, and it is difficult to control the carrier forming process and particle shape, so the shape of the polymer is difficult to control
[0009] Catalysts supported on anhydrous magnesium chloride show high catalytic activity in olefin polymerization, but such catalysts are very brittle and break easily in the polymerization reactor, resulting in poor polymer morphology
Silica-supported catalysts have good fluidity and can be used in gas-phase fluidized bed polymerization, but silica-supported metallocene and non-metallocene catalysts show low catalytic activity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Loaded non-metallocene catalyst, its preparation method and application
  • Loaded non-metallocene catalyst, its preparation method and application
  • Loaded non-metallocene catalyst, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

no. 1 approach

[0156] In the context of the present invention, unless otherwise clearly defined, or the meaning is beyond the scope of understanding of those skilled in the art, hydrocarbon or hydrocarbon derivative groups with more than 3 carbon atoms (such as propyl, propoxy, butyl , butane, butene, butenyl, hexane, etc.) all have the same meaning as when the prefix "positive" is not prefixed. For example, propyl is generally understood as n-propyl and butyl is generally understood as n-butyl.

[0157] The invention relates to a preparation method of a supported non-metallocene catalyst, comprising the following steps: contacting a porous support, a Grignard reagent, a halogenating reagent and a non-metallocene ligand optionally subjected to heat activation treatment in the presence of a solvent, The step of obtaining the modified composite carrier; and the step of reacting a chemical treatment agent selected from Group IVB metal compounds with the modified composite carrier to obtain the ...

Embodiment 1

[0336] The Grignard reagent adopts methylmagnesium chloride (MeMgCl), the solvent for dissolving the Grignard reagent adopts tetrahydrofuran, the halogenated reagent adopts chlorobutane, and the porous carrier adopts silicon dioxide, i.e. silica gel, the model is ES757 of Ineos Company, chemical treatment agent Using titanium tetrachloride, the non-metallocene ligand adopts the structure compound of.

[0337] Firstly, the silica gel was continuously fired at 600° C. under nitrogen atmosphere for 4 hours to thermally activate it.

[0338] Weigh 2 g of the non-metallocene ligand, dissolve it in a halogenated reagent at room temperature to prepare a homogeneous solution for use. Add the heat-activated porous carrier into the Grignard reagent solution at room temperature, and stir at room temperature to form a uniform slurry. Add the mixed solution of the non-metallocene ligand and the halogenating reagent dropwise to the homogeneous slurry at room temperature, and the dropping...

Embodiment 2

[0343] The Grignard reagent uses ethylmagnesium chloride (EtMgCl), the solvent used to dissolve the Grignard reagent is ether, the halogenated reagent uses ethyl chloride, and the non-metallocene ligand uses The porous carrier was changed to 955 type silica gel of Grace Company, and it was continuously calcined at 400° C. for 8 hours under a nitrogen atmosphere to be thermally activated. The chemical treatment agent adopts zirconium tetrachloride (ZrCl 4 ).

[0344]Weigh 4.7 g of the non-metallocene ligand, add it into the Grignard reagent solution at room temperature, and then add the heat-activated porous carrier at room temperature to prepare a slurry. Weigh the halogenated reagent, and dissolve it in the solvent for dissolving the Grignard reagent (accounting for half of the total amount) at normal temperature to prepare a solution. The halogenated reagent solution was added dropwise to the aforementioned slurry at room temperature, and the dropping time was 30 minutes....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The inside diameter ofaaaaaaaaaa
Login to View More

Abstract

The invention relates to a loaded non-metallocene catalyst and its preparation method. The loaded non-metallocene catalyst has the characteristics of simple and feasible preparation process, controllable non-metallocene component content, and substantial copolymerization effect, etc. The invention also relates to application of the loaded non-metallocene catalyst in olefin homopolymerization / copolymerization. Compared with the prior art, during application, the loaded non-metallocene catalyst has high olefin polymerization catalytic activity, small size and uniform distribution, and the obtained polymer has a high bulk density.

Description

[0001] This application is based on the ongoing research project of "National Eleventh Five-Year Support Program Topics". The project has been highly valued and strongly supported by the Ministry of Science and Technology of the People's Republic of China. Its goal is to form a new generation of polyolefin catalyst technology with independent intellectual property rights, improve the homogeneity of domestic related products, improve the grade of polyolefin varieties in my country, and promote its development. Development in the direction of diversification, serialization, specialization and high performance. technical field [0002] The present invention relates to a non-metallocene catalyst. Specifically, the present invention relates to a supported non-metallocene catalyst, its preparation method and its application in olefin homopolymerization / copolymerization. Background technique [0003] The non-metallocene catalysts that appeared in the mid-to-late 1990s are also call...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F10/00C08F4/658C08F4/646C08F4/654C08F4/653C08F4/651C08F4/02
Inventor 李传峰任鸿平郭峰阚林柏基业马忠林陈韶辉王亚明杨爱武
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com