Preparation method of nanometer fibril enteromorpha cellulose

A nanofibrillation, cellulose technology, applied in fiber raw material processing, textile and papermaking, etc., to achieve high conversion rate, low density, improve tensile strength and elastic modulus

Active Publication Date: 2015-03-04
QINGDAO UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the raw materials of Enteromorpha enteromorpha have not been efficiently utilized after the polysaccharides are extracted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nanometer fibril enteromorpha cellulose
  • Preparation method of nanometer fibril enteromorpha cellulose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: a kind of preparation method of enteromorpha nanofibril cellulose, specifically finish according to the following steps:

[0030] 1. After collecting Enteromorpha, sort and remove miscellaneous algae and other small shellfish, wash, freeze-dry, crush and sieve to obtain 60 mesh Enteromorpha algae dregs powder;

[0031] 2. Mix 5 g of Enteromorpha algal residue powder with 300 mL of distilled water, perform cell crushing pretreatment with an ultrasonic power of 500 W for 20 minutes, and extract polysaccharides in a constant temperature water bath at 65°C for 4 hours;

[0032] 3. Centrifuge the obtained polysaccharide-extracted mixed solution at 3500 rpm for 5 minutes, pour off two-thirds of the liquid, then add distilled water and repeat the above centrifugal cleaning for 5 times to obtain the precipitated waste residue after extracting the crude polysaccharide;

[0033] 4. Add KOH aqueous solution to the precipitated waste residue obtained after extracting ...

Embodiment 2

[0041] Embodiment 2: a kind of preparation method of enteromorpha nanofibril cellulose, specifically finish according to the following steps:

[0042] 1. After collecting Enteromorpha, pick and remove miscellaneous algae and other small shellfish, wash, freeze-dry, crush and sieve to obtain 100 mesh Enteromorpha algae dregs powder;

[0043] 2. Mix 3 g of Enteromorpha algal residue powder with 300 mL of distilled water, perform cell crushing pretreatment with an ultrasonic power of 1000 W for 20 minutes, and extract polysaccharides in a constant temperature water bath at 90°C for 2 hours;

[0044] 3. Centrifuge the obtained mixed solution of polysaccharide extracted at 5500rpm for 5 minutes, pour off 2 / 3 of the liquid, add distilled water and repeat the above centrifugal cleaning 5 times, and obtain the precipitated waste residue of extracted crude polysaccharide;

[0045] 4. Add NaOH aqueous solution to the precipitated waste residue after extracting the crude polysaccharide f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of nanometer fibril enteromorpha cellulose. By taking marine biomass enteromorpha as a raw material, waste residue after polysaccharide extraction is subjected to a chemical treatment, and is then subjected to a nanometer fibril treatment after desalination, deproteinization and depigmentation, thus preparing enteromorpha algae nanometer fibril. The enteromorpha cellulose nanometer fibril prepared by the preparation method is long and uniform in fiber diameter distribution. The prepared cellulose nanometer fibril can have great application prospects in biological scaffolds, inorganic templates, optical transparent flexible films, drug controlled release, water purification, efficient heat insulation and sound insulation materials, rechargeable batteries, super-capacitors, catalysts and carriers, gas filtering materials, adsorption materials, cosmetics, food additives and the like.

Description

technical field [0001] The invention relates to a preparation method of nano-fibrillated enteromorpha cellulose, in particular to a method for successfully preparing nano-fibrillated cellulose from the large seaweed enteromorpha that causes the "green tide" at sea. Background technique [0002] The algae of Enteromorpha are composed of a single layer of cells, which are tubular, hollow or flat, and the length of the algae can reach more than 1m. The crude fiber content in the raw materials of Enteromorpha is 9-12%, while the cellulose content in the waste residue after extracting polysaccharides is as high as 30-50%, which is much higher than that of most natural wood, and the waste residue of Enteromorpha is rich in wood Cellulose has a low crystallinity and is an ideal precursor of nanofibrillated cellulose. However, most of the raw materials of Enteromorpha enteromorpha have not been efficiently utilized after the polysaccharides are extracted. Therefore, there is an ur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21C5/00C08B37/00
Inventor 杨东江佘希林李建江
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com