Methods for producing polarizing laminate film and polarizing plate

A manufacturing method and a laminated film technology, which can be applied to polarizing elements, coatings, nonlinear optics, etc., and can solve problems such as the difficulty in realizing the thinning of polarizing films, bending and bending at the ends of substrate films, etc.

Active Publication Date: 2013-07-10
SUMITOMO CHEM CO LTD
View PDF6 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, in the method of manufacturing a polarizing film by stretching, dyeing, and cross-linking a film made of a polyvinyl alcohol-based resin, it is difficult to handle a thin film of 50 μm or less because it is prone to breakage and wrinkles. Therefore, it is difficult to realize the thinning of the polarizing film
[0007] In the method of applying a solution containing a polyvinyl alcohol-based resin on the surface of a base film to form a resin layer, the resin layer tends to shrink due to drying shrinkage of the solution containing a polyvinyl alcohol-based resin, and as a result, bases may sometimes occur. The phenomenon that both ends of the material film are warped toward the resin layer side. If the base film with the resin layer is kept flowing continuously in this state, it will cause the end of the base film to bend in the drying furnace or at the outlet of the drying furnace. bad condition
[0008] In the method of producing a laminated film by co-extruding a protective film resin and a polyvinyl alcohol-based resin, the polyvinyl alcohol-based resin is usually melted together with a solvent and extruded. Defective conditions that cause the edge of the base film to bend

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Methods for producing polarizing laminate film and polarizing plate
  • Methods for producing polarizing laminate film and polarizing plate
  • Methods for producing polarizing laminate film and polarizing plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0148]

[0149] Completely saponified polyvinyl alcohol resin (trade name: PVA124) powder sold by Kuraray Co., Ltd. was dissolved in warm water at 90°C to prepare a polyvinyl alcohol resin aqueous solution with a solid content concentration of 10 wt%. The obtained polyvinyl alcohol resin aqueous solution was applied to a thickness of about 400 μm by a lip coating method on a PET substrate subjected to a release treatment. After drying at 50° C. for 10 minutes, the polyvinyl alcohol-based resin film was peeled off from the PET substrate, and further dried at 80° C. for 5 minutes to obtain a polyvinyl alcohol-based resin film without curl. The thickness after drying was 41 μm.

[0150]

[0151] Polyvinyl alcohol powder and a crosslinking agent were dissolved in hot water to prepare an aqueous adhesive solution having the following composition. In addition, corona discharge treatment was performed on a 110 μm thick base film formed of polypropylene resin (trade name: FLX80E4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A method for producing a polarizing laminate film including a base film and a polarizer layer formed on one surface of the base film involves, in the following order: a resin film laminating step of laminating a resin film made of a polyvinyl alcohol resin and having a thickness of 50 [mu]m or less onto one surface of a base film, to thereby obtain a laminate film; a stretching step of uniaxially stretching the laminate film; and a dyeing step of dyeing the resin film of the uniaxially stretched laminate film with a dichroic dye, to thereby form a polarizer layer. The present invention can provide a method for producing a polarizing laminate film having a thin polarizer layer without giving rise to the problem that the ends of the base film are folded inside.

Description

technical field [0001] The present invention relates to a method for manufacturing a polarizing laminated film and a polarizing plate. Background technique [0002] A polarizing plate is widely used as a polarized light supply element and the like in display devices such as liquid crystal display devices. As the polarizing plate, a polarizing plate in which a polarizer layer made of a polyvinyl alcohol-based resin and a protective film such as triacetyl cellulose are laminated has been conventionally used. The polarizer layer (polarizing film) is not only required to have high optical performance, but also has been required to be thinner and lighter in recent years with the development of liquid crystal display devices in mobile devices such as notebook PCs and mobile phones. [0003] As an example of a method for producing a polarizing plate, a method is known in which a polarizing film is produced by stretching a film made of a polyvinyl alcohol-based resin alone, or perf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/30B29C41/12B29C55/06G02F1/1335
CPCB29C55/023B29C55/06B29C55/065B29K2029/04B29K2995/0034G02B5/3025
Inventor 九内雄一朗
Owner SUMITOMO CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com