China hemp native fiber multicomponent blended yarn and preparing method thereof

A hemp primary fiber and multi-component technology, applied in the direction of yarn, textiles and papermaking, can solve the problems of high hard sliver rate of ultra-long fibers, poor spinnability, thick and short fibers, etc., to achieve improved evenness, Less hairiness and better evenness

Active Publication Date: 2013-06-05
江苏悦达棉纺有限公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high rigidity, fast moisture dissipation, thick and short fibers and high content of short fibers, ultra-long fibers and high sliver ratio, the raw hemp fibers have poor spinnability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • China hemp native fiber multicomponent blended yarn and preparing method thereof
  • China hemp native fiber multicomponent blended yarn and preparing method thereof
  • China hemp native fiber multicomponent blended yarn and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0114] 1. Spinning process

[0115] 1. Main performance indicators of raw materials:

[0116] The length of hemp fiber is 55.34mm, the linear density of hemp fiber is 3.01D, the metric count is 2695Nm, the rate of hard strips is 1.5%, the rate of hemp grains is 35 grains / g, the rate of extra long fibers is 1.8%, and the moisture regain rate is 8.7%. The hemp viscose is selected from Shandong Hailong Co., Ltd. 1.5D×38mm cotton-type staple fiber, the long-staple cotton is selected from 137A Xinjiang long-staple cotton, the filament is selected from 20D polyester filament, and 32S blended yarn is spun with embedded spinning.

[0117] 2. Process flow:

[0118] ① Hemp raw fiber health pretreatment → cleaning and carding pretreatment: FA002A cotton grabbing machine (hemp raw fiber is fed separately) → A035E mixed cotton opener → FA106 cotton opener → A092A cotton feeder → A076C lapping machine → A186D Carding machine (not into sliver, collecting cotton web for packing) →

[0119]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a China hemp native fiber multicomponent blended yarn. The China hemp native fiber multicomponent blended yarn is high in brute force, good in evenness, and anti-pilling, has a soft and smooth yarn body, and is obvious in characteristic and stable in quality. The China hemp native fiber multicomponent blended yarn is blended of 25% of filaments, 15% of China hemp native fibers, 40% of China hemp viscose fibers and 20% of long stapled cotton and made through embedding spinning technique. The invention further provides a preparing method of the China hemp native fiber multicomponent blended yarn. The preparing method comprises the following steps: a, maintenance pretreatment of the China hemp native fibers is conducted, and softening antistatic oiling agents are spayed on the China hemp native fibers; b, blowing and carding of the China hemp native fibers are conducted; c, the processed China hemp native fibers and the long stapled cotton are combed and blended into strips; d, the China hemp viscose fibers are processed into strips independently; and e, the blending combining strips of the China hemp native fibers and the long stapled cotton, and the China hemp viscose fibers are pre-drawn and mixed, then roving and embedding finespinning are conducted, and the filaments are combined during embedding finespinning.

Description

technical field [0001] The invention relates to a blended yarn, in particular to a multi-component blended yarn of hemp primary fiber and a preparation method thereof. Background technique [0002] Hemp is one of the earliest textile fibers used by humans. Hemp has excellent moisture absorption and perspiration properties, natural antibacterial and health care properties, good softness and comfort, excellent UV resistance, excellent high temperature resistance, and unique wave absorption. Adsorption performance and natural rough style, known as the "king of hemp", and widely used in clothing, home textiles, hats, shoe materials, socks, etc. Hemp textiles are especially suitable for sun protection clothing and various work clothes with special needs, as well as sun umbrellas, camping tents, fishing nets, ropes, car seat cushions, lining materials, etc. In addition to being used for clothing, hemp textiles can also be used for interior decoration, which can reduce noise. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04
Inventor 凌良仲刘云王冬成周卫东
Owner 江苏悦达棉纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com