Fireproof cement foam insulation board

A fireproof insulation board and cement foaming technology, applied in the field of cement building materials, can solve the problems of high cost, difficult to control the foaming effect, complex production process, etc., and achieve the effect of fast time, fine air bubbles and good heat preservation effect

Active Publication Date: 2014-01-15
镇江市蓝图建筑工程有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing cement-foamed fire-proof insulation boards use cement and fly ash to add surfactants, and use foaming machines for physical foaming. The production process is complicated, the cost is high, and the foaming effect is difficult to control.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Take 1kg of stearic acid, 0.1kg of sodium carbonate, 1kg of ammonia water, 0.1g of sodium fluoride, 1kg of potassium hydroxide, and 85kg of water to prepare a waterproofing agent.

[0011] Take 38kg of sulfoaluminate cement, 28kg of fly ash, 0.28kg of wood anti-cracking fiber, 2.9kg of waterproofing agent, 0.55kg of calcium stearate, 0.18kg of polycarboxylate superplasticizer and 25kg of water, mix well, add GM-A After stirring, 2.0kg of foaming agent is quickly poured into the template, obtained after curing and demoulding, and then cut and packaged as required. Among them, the wooden anti-cracking fiber adopts polypropylene fiber, and the polycarboxylate superplasticizer adopts BRJ-T200 polycarboxylate superplasticizer of Jiangsu Bairuiji New Material Co., Ltd.

[0012] The prepared product index is: dry density is 220kg / m 3 , the foaming height is 33cm, the compressive strength is 0.65MPa, the bonding strength is 0.45MPa, the thermal conductivity is 0.4 w / (m?k),...

Embodiment 2

[0019] Take 5kg of stearic acid, 0.5kg of sodium carbonate, 5kg of ammonia water, 1g of sodium fluoride, 5kg of potassium hydroxide, and 95kg of water to prepare a waterproofing agent.

[0020] Take 45kg of sulfoaluminate cement, 33kg of fly ash, 0.35kg of wood anti-cracking fiber, 3.5kg of waterproofing agent, 0.75kg of calcium stearate, 0.25kg of polycarboxylate superplasticizer and 30kg of water, mix well, add GM-A 3.0 kg of foaming agent is stirred and quickly poured into the template, obtained after curing and demoulding, and then cut and packaged as required.

[0021] The prepared product index is: dry density is 250kg / m 3 , the foaming height is 37cm, the compressive strength is 0.85MPa, the bonding strength is 0.5MPa, the thermal conductivity is 0.45 w / (m?k), the water absorption rate (V / V) is 7%, and the combustion level is A1.

Embodiment 3

[0023] Take 3kg of stearic acid, 0.3kg of sodium carbonate, 3kg of ammonia water, 0.5g of sodium fluoride, 3kg of potassium hydroxide, and 90kg of water to prepare a waterproofing agent.

[0024] Take 40kg of sulfoaluminate cement, 30kg of fly ash, 0.3kg of wood anti-cracking fiber, 3kg of waterproofing agent, 0.6kg of calcium stearate, 0.2kg of polycarboxylate superplasticizer and 28kg of water, mix well, add GM-A hair 2.5 kg of foaming agent is stirred and quickly poured into the formwork, obtained after curing and demoulding, and cut and packaged as required.

[0025] The prepared product index is: dry density is 230kg / m 3 , the foaming height is 35cm, the compressive strength is 0.7MPa, the bonding strength is 0.5MPa, the thermal conductivity is 0.45 w / (m?k), the water absorption rate (V / V) is 7%, and the combustion level is A1.

[0026] The determination of product indicators is carried out in accordance with "GB8624-2006 Classification of Combustion Performance of Build...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
heightaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof cement foam insulation board, comprising the following components in parts by weight: 38-45 parts of sulphate aluminium cement, 28-33 parts of fly ash, 0.28-0.35 part of wooden anti-crack fiber, 2.9-3.5 parts of waterproof agent, 0.55-0.75 parts of calcium stearate, 0.18-0.25 parts of polycarboxylate superplasticizer, 2.0-3.0 parts of GM-A foaming agent, and 25-30 parts of water. The fireproof cement foam insulation board disclosed by the invention is simple in manufacturing technique, good in insulation and waterproof effects of products, and inflammable.

Description

technical field [0001] The invention belongs to the field of cement building materials, and in particular relates to a cement foam fireproof and thermal insulation board. Background technique [0002] As the country pays more and more attention to building energy-saving technology for roof and wall insulation, various types of external wall insulation materials continue to appear in the market. However, currently commonly used insulation materials such as polystyrene board, extruded board and foamed phenolic resin have disadvantages such as flammability, aging, high cost and short service life. Especially in recent years, fire accidents ignited by building exterior wall insulation materials have occurred frequently, and the fire safety of building exterior wall insulation systems has been valued by relevant national ministries and commissions. [0003] The existing cement-foamed fire-proof insulation board adopts adding surfactant to cement and fly ash, and uses a f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B28/06
Inventor 王兴文孙忠韦伟
Owner 镇江市蓝图建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com