Sound-absorbing composite and preparation method thereof

A sound-absorbing composite material, polyurethane sponge technology, applied in the direction of noise suppression, chemical instruments and methods, lamination devices, etc., can solve the problems of unfavorable application, high density of lead plate, increase of vehicle weight, etc., and achieve excellent sound absorption and drop Noise performance, small density, small thermal conductivity effect

Active Publication Date: 2013-03-13
ZHUZHOU TIMES NEW MATERIALS TECH
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the above-mentioned air-conditioning noise reduction device, the sponge, lead plate, sponge and recycled rubber are arranged in sequence to form the upper noise reduction device and the side noise reduction device. Although the sound insulation performance of the lead plate is fully utilized, the noise of the air conditioner is greatly reduced. However, the density of the lead plate in the air-conditioning noise reduction device is high, and when applied to the vehicle field, the weight of the vehicle will be significantly increased, which is not conducive to application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound-absorbing composite and preparation method thereof
  • Sound-absorbing composite and preparation method thereof
  • Sound-absorbing composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The present invention also provides a method for preparing a sound-absorbing composite material, comprising the following steps:

[0044] The double-sided adhesive is placed between the polyurethane sponge and the melamine sponge, and then heat-compressed to obtain a semi-finished sound-absorbing composite material. The thickness ratio of the melamine sponge to the polyurethane sponge is 1:1.5 to 1:5;

[0045] An adhesive is coated on the melamine sponge of the semi-finished sound-absorbing composite material to form an adhesive layer to obtain a sound-absorbing composite material.

[0046] In the present invention, firstly, double-sided adhesive is placed between the melamine sponge and the polyurethane sponge with a thickness ratio of 1:1.5 to 1:5, and then heat-compressed and compounded to obtain a semi-finished sound-absorbing composite material.

[0047] The present invention uses polyurethane sponge as a raw material. The polyurethane sponge is a kind of soft poly...

Embodiment 1

[0064] figure 1 The flow chart for the preparation of the sound-absorbing composite material provided in Example 1 of the present invention. see figure 1 , the melamine sponge block is peeled off and cut into a melamine sponge sheet with a thickness of 10mm, the polyurethane sponge block is peeled and cut into a polyurethane sponge sheet with a thickness of 15mm, the double-sided adhesive is placed between the polyurethane sponge sheet and the melamine sponge sheet, and then Carry out hot-press lamination to obtain a semi-finished sound-absorbing composite material; the temperature of the hot-press lamination is 50°C, the pressure is 5MPa, and the time is 60s;

[0065] Apply adhesive on the melamine sponge of the semi-finished sound-absorbing composite material to form an adhesive layer with a thickness of 0.05mm, and then use a cutting machine to cut and trim the edge to obtain the finished sound-absorbing composite material, melamine sponge The thickness ratio with polyure...

Embodiment 2

[0073] The melamine sponge block is peeled off and cut into a melamine sponge sheet with a thickness of 10mm, the polyurethane sponge block is peeled and cut into a polyurethane sponge sheet with a thickness of 25mm, the double-sided adhesive is placed between the polyurethane sponge sheet and the melamine sponge sheet, and then Hot-pressing composite to obtain a semi-finished sound-absorbing composite material; the temperature of the hot-pressing composite is 80°C, the pressure is 1MPa, and the time is 20s;

[0074] Apply adhesive on the melamine sponge of the semi-finished sound-absorbing composite material to form an adhesive layer with a thickness of 0.05mm, and then use a cutting machine to cut and trim the edge to obtain the finished sound-absorbing composite material, melamine sponge The thickness ratio with polyurethane sponge is 1:2.5.

[0075] After the sound-absorbing composite material is obtained, its sound-absorbing performance is tested according to the method d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a sound-absorbing composite and a preparation method of the sound-absorbing composite. The method comprises the steps of placing a double-faced adhesive tape between a polyurethane sponge and a melamine sponge, conducting hot pressing composition, obtaining a semifinished sound-absorbing composite, coating an adhesive on the melamine sponge of the semifinished sound-absorbing composite, and obtaining the sound-absorbing composite after an adhesive layer is formed, wherein the thickness ratio of the melamine sponge to the polyurethane sponge is 1:1.5-1:5. The sound-absorbing composite is prepared by hot pressing composition with the polyurethane sponge and the melamine sponge, so that the sound-absorbing composite has a smaller density and an excellent sound absorption reduction performance, and the effective noise reduction treatment can be conducted relative to the noise spectrum characteristic by adjusting the thickness ratio of the melamine sponge to the polyurethane sponge. In addition, the sound-absorbing composite is small in heat conductivity and has an excellent thermal insulation property, and the effective utilization ratio of energy sources can be increased when the sound-absorbing composite is used for vehicle-mounted air conditioners and air duct systems.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a sound-absorbing composite material and a preparation method thereof. Background technique [0002] With the development of my country's transportation industry and the improvement of people's living standards, people have put forward higher and higher requirements for the ride comfort of vehicles. However, in the field of rail vehicles and commercial passenger vehicles, the noise problem of the on-board air conditioner and its air duct system affects the comfort of the entire compartment, such as compressor noise and aerodynamic noise are continuously transmitted into the compartment through the air duct system. Therefore, research on noise reduction or sound absorption for vehicles is becoming more and more important. [0003] At present, the prior art discloses a variety of noise reduction methods. For example, the Chinese patent document with the authorized anno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F24F13/24B32B5/18B32B37/12B32B37/06B32B37/10
Inventor 徐波谭亮红罗仡科郭名中姜莹黄磊张凤桥
Owner ZHUZHOU TIMES NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka