Light and color glazed tile for building

A glazed tile and building technology, applied in the field of architectural decoration, can solve the problems of insufficient glaze gloss, insufficient smoothness, easy fading, etc., and achieve the effects of good thermal insulation and sound insulation, bright and bright colors, and smooth and tidy surface.

Inactive Publication Date: 2013-03-06
CHINA CHANGSHU CONSTR GRP
View PDF1 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing glazed tiles are usually fired with a mixture of various mud materials. The glaze layer is generally thick and produces stress. The quality is heavy, and it is easy to cause cracks and cracks on the glazed surface of the product.
Not smooth enough, and the mud is prone to pollution in the production process, high cost and energy consumption, the quality of the product is not stable enough, the gloss of the glaze is not enough, and the color is not rich and stable enough. Fades easily in sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of light colored glazed tile for building, described light colored glazed tile for building is to add 0.4kg magnesia to the magnesium chloride solution with concentration of 45% per kilogram, stir for 6 minutes, then add 0.05kg magnesium silicate, 0.03kg Urea-formaldehyde resin, 0.1g of ammonium carbonate, 2g of trisodium phosphate and 2g of color material were stirred for 25 minutes, then the stirred material was poured on glass fiber cloth, flattened and compacted, and cured and dried at 30°C.

[0019] Wherein, the bottom of the glass fiber cloth is provided with a layer of plastic film.

Embodiment 2

[0021] A kind of light colored glazed tile for building, described light colored glazed tile for building is to add 0.6kg magnesia to the magnesium chloride solution with concentration of 45% per kilogram, stir for 8 minutes, then add 0.1kg magnesium silicate, 0.02kg Urea-formaldehyde resin, 0.06g of ammonium carbonate, 3g of trisodium phosphate and 3g of color material were stirred for 30 minutes, then the stirred material was poured on glass fiber cloth, flattened and compacted, cured and dried at 35°C.

[0022] Wherein, the bottom of the glass fiber cloth is provided with a layer of plastic film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light and color glazed tile for a building, which is obtained by the following steps: adding 0.4 to 0.6 kg of magnesium oxide to each kilo of a magnesium chloride solution; agitating the mixture for 6 to 8 minutes; successively adding 0.05 to 0.1 kg of magnesium silicate, 0.02 to 0.03 kg of urea-formaldehyde resin, 0.06 to 0.1 g of ammonium carbonate, 2 to 3 g of trisodium phosphate and 2 to 3 g of pigment; agitating the obtained mixture for 20 to 30 minutes; pouring the agitated mixture to a glass fiber cloth; scraping and compacting the poured mixture; and performing natural cure and drying to obtain the light and color glazed tile for the building. In the way above, the light and color glazed tile for the building has the advantages of smooth and clean surface, bright color, color retention, fracture resistance, compression resistance, thermal and cooling shock resistance, acid and alkali resistance, freezing resistance, light weight, low water absorption, good thermal insulation, good sound insulation and low cost.

Description

technical field [0001] The invention relates to the technical field of architectural decoration, in particular to a lightweight colored glazed tile for architectural use. Background technique [0002] With the continuous development of my country's economy in recent years, it has promoted the development of the construction industry. With the continuous development of the current tourism industry, antique architecture is the main measure in the current tourism economic development process, and the national style antique architectural system is also constantly developing, and architectural functions and architectural structures are also constantly changing. [0003] Glazed tiles have been used as traditional Chinese building components because of their solid materials, bright colors, and smooth glaze. After successive developments and quality improvements, glazed tiles have been widely used in modern architecture due to their various excellent functions. [0004] Existing gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B111/82
Inventor 洪伟
Owner CHINA CHANGSHU CONSTR GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products