Flash welding forming method of stainless steel thin-wall ring member

A technology of stainless steel and thin-walled rings, which is applied in welding equipment, resistance welding equipment, welding/welding/cutting items, etc., can solve the problems of scrapped welded parts, affecting continuous welding and weld quality, and flash stop, etc., to achieve good performance Effect

Active Publication Date: 2013-02-20
GUIZHOU ANDA AVIATION FORGING
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of welding thin-walled rings such as stainless steel thin-walled rings by flash welding, if the distance between the two ends of the ring blank weld is not well controlled, the flash will stop, which will affect the continuous process of welding and the quality of the weld. In severe cases, the weldment will be scrapped

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flash welding forming method of stainless steel thin-wall ring member
  • Flash welding forming method of stainless steel thin-wall ring member
  • Flash welding forming method of stainless steel thin-wall ring member

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0037] The main chemical element content (percentage by weight) of the alloy is: C content 0.10%-0.16%, Cr content 10.50%-12.00%, Ni content 1.40%-1.80%, W content 1.50%-2.00%, Mo content is 0.35%-0.50%, V content is 0.18%-0.30%, Mn content is ≤0.60%, Si content is ≤0.60%, S content is ≤0.025%, P content is ≤0.030%, and the balance is Fe.

[0038] The flash welding forming process steps of the alloy thin-walled ring are as follows:

[0039] Step 1: Install the computer. Such as figure 1As shown, the 1Cr11Ni2W2MoV alloy D-shaped ring blank with openings is loaded into a flash butt welding machine with a power of 1000KVA. The side of the opening 110 corresponding to the left straight side 101 has a left end surface 111 , and the side corresponding to the right straight side 102 has a right end surface 112 . When installing, put the left straight edge 101 of the D-shaped ring blank into the left clamping device 10 of the flash butt welding machine, and the upper clamp 11 and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flash welding forming method of a stainless steel thin-wall ring member. The method comprises the steps of: loading a D type ring blank with an opening in a welder, starting the welder to close the opening of the preheated ring blank, applying a 7-18V voltage between two poles of the welder to ensure that the left end face and the right end face of the opening of the ring blank are heated and molten through a flash current with the current density of 15A / mm<2>-220A / mm<2> to form a lintel, exploding to form a flash, wherein the flash burning loss speed of the ring blank is 4.0mm-8.0mm / s; driving the right end face of the ring blank to make an accelerated feeding movement towards the left end face at an initial speed of 3.0mm / s-5.0mm / s and an acceleration of 1.0mm / s<2>-2.0mm / s<2> so as to ensure that the distance between the left end face and the right end face is not more than 7mm; and after the flash is completed, driving a right straight side of the ring blank to move at a high speed towards a left straight side of the ring blank to ensure that the left end face and the right end face collide with each together under the action of an upsetting force of 11kN-16kN to form the flash welding thin-wall ring member, and keeping the pressure for 10s-30s under the action of the upsetting force. The method can ensure that the flash process is continuously and stably carried out, thereby improving the weld quality.

Description

technical field [0001] The invention relates to a welding method, in particular to a flash welding forming method of a stainless steel thin-walled ring. Background technique [0002] With the increasing demand for rings in industries such as aviation, aerospace, ships, gas turbines, wind energy, nuclear energy, and bearings, rings formed by traditional rolling methods not only waste a lot of materials due to large machining allowances and low material utilization , but also keeps the cost of ring parts high. The ring parts produced by the flash welding process have less machining allowance, high material utilization rate, and greatly reduce the cost, which is conducive to the development of ring forming technology in the direction of precision forming technology. [0003] The Chinese invention patent specification CN 1233548A published on November 3, 1999 discloses a flash welding process for aluminum alloy wheels of automobiles and motorcycles. The technological process ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K11/04B23K103/04
Inventor 魏志坚王超江飞龙邹伟邓远翔韩森霖王建立
Owner GUIZHOU ANDA AVIATION FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap