Phosphorus-containing boric acid ester water-based lubricant

A technology of water-based lubricants and boric esters, applied in lubricating compositions, additives, petroleum industry, etc., can solve problems such as unsatisfactory product performance and stability, and achieve good cleaning performance, good anti-rust effect, and biodegradation good sex effect

Active Publication Date: 2014-04-02
无锡纳润特科技有限公司 +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Guangzhou Institute of the Chinese Academy of Sciences once included this project in the 2005 science and technology plan, but there has been no major breakthrough so far, and its product performance and stability are not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorus-containing boric acid ester water-based lubricant
  • Phosphorus-containing boric acid ester water-based lubricant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Put boric acid, raw material A, and glycerol into the reaction kettle, and conduct the reaction under vacuum and constant stirring. The reaction temperature is 80°C and the reaction time is 120 minutes;

[0027] (2) Turn off the vacuum, cool the temperature in the reactor to below 50℃, then slowly add phosphorus pentoxide to the reactor, keep stirring, control the reaction temperature below 90℃, and stir for 1 hour after the addition is complete;

[0028] (3) Control the temperature below 90℃, add pure water to the reactor and stir for 60 minutes;

[0029] (4) Lower the temperature of the reaction kettle to room temperature and discharge.

Embodiment 2

[0031] (1) Put boric acid, raw material A, and glycerol into the reaction kettle, and conduct the reaction under vacuum and continuous stirring. The reaction temperature is 120°C and the reaction time is 60 minutes;

[0032] (2) Turn off the vacuum, cool the temperature in the reactor to below 50℃, then slowly add phosphorus pentoxide to the reactor, keep stirring, control the reaction temperature below 90℃, and stir for 50 minutes after the addition is complete;

[0033] (3) Control the temperature below 90℃, add pure water to the reactor and stir for 70 minutes;

[0034] (4) Lower the temperature of the reaction kettle to room temperature and discharge.

Embodiment 3

[0036] (1) Put boric acid, raw material A, and glycerol into the reaction kettle, and conduct the reaction under vacuum and constant stirring. The reaction temperature is 100°C and the reaction time is 100 minutes;

[0037] (2) Turn off the vacuum, cool the temperature in the reactor to below 50℃, then slowly add phosphorus pentoxide into the reactor, keep stirring, control the reaction temperature below 90℃, and stir for 70 minutes after the addition is complete;

[0038] (3) Control the temperature below 90℃, add pure water to the reactor and stir for 80 minutes;

[0039] (4) Lower the temperature of the reaction kettle to room temperature and discharge.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a phosphorus-containing boric acid ester water-based lubricant. A preparation method for the lubricant comprises the following steps of: (1) adding boric acid, a raw material A and glycerol into a reaction kettle, and performing reaction under vacuum and with stirring; (2) closing and vacuumizing the reaction kettle, cooling the reaction kettle till the internal temperature is below 50DEG C, slowly adding phosphorus pentoxide into the reaction kettle, continuously stirring with the reaction temperature between 90 DEG C, and stirring after the addition of the materials; (3) adding pure water into the reaction kettle and stirring with the temperature below 90 DEG C; and (4) cooling the reaction kettle to room temperature and discharging. A raw material A is one of TX-(4 to 9) or AEO (4 to 9) and the lubricant comprises 70 to 85 weight percent of the raw material A, 2.5 to 4 weight percent of boric acid, 2 to 6.5 weight percent of glycerol, 4 to 7 weight percent of phosphorus pentoxide, and 3 to 17 weight percent of pure water. The lubricant with high boiling point is insusceptible to volatilization, is noncorrosive to metals and has high wear resistance. And the lubricant is safe and odorless.

Description

Technical field [0001] The invention relates to the technical field of lubricants, in particular to a water-based extreme pressure lubricant synthesized from organic borate and phosphate. Background technique [0002] Lubricant is a product commonly used in the metal processing industry and has a large market use. In recent years, as countries around the world pay more and more attention to environmental protection, the widely used mineral oil-based lubricant products have become the focus of discussion and attention due to their poor biodegradability and easy environmental pollution. Development of green and environmentally friendly fully synthetic Lubricants have become the main development direction of lubricant research in the field of metal processing, and the development of water-based lubricants is one of the main research contents. The Guangzhou Institute of Chinese Academy of Sciences once included this project in the 2005 science and technology plan, but there has been...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M139/00C10M173/02C10N30/06
Inventor 宋小林
Owner 无锡纳润特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap