A method for measuring the saturation magnetostriction coefficient of a flexible magnetic film

A technology of magnetostrictive coefficient and magnetic thin film, which is applied in the measurement of magnetostrictive performance and magnetic performance, etc., can solve the problems of complex, no measurement method, and complicated measurement system circuit, and achieve the effect of low cost and fast measurement.

Active Publication Date: 2015-10-14
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method has high measurement accuracy, the circuit of the measurement system is complicated and the correction is difficult.
[0008] In summary, the current measurement system for the saturation magnetostriction coefficient of magnetic thin films is relatively complicated; moreover, there is no special measurement method for the magnetostriction coefficient of flexible magnetic films

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for measuring the saturation magnetostriction coefficient of a flexible magnetic film
  • A method for measuring the saturation magnetostriction coefficient of a flexible magnetic film
  • A method for measuring the saturation magnetostriction coefficient of a flexible magnetic film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]In this embodiment, the flexible magnetic film is FeGa(10nm) / IrMn(20nm) / Ta(30nm) / PET exchange bias film, that is, Ta film layers with a thickness of 30nm and a thickness of The IrMn film layer of 20nm and the FeGa film layer of 10nm in thickness, the measurement of the saturation magnetostriction coefficient of this film comprises the steps:

[0040] (1) Place the film sample on the surface of the plane mold 301, such as Figure 2a As shown, the mold 301 does not apply strain to the film sample to obtain a strain-free film sample 302; the plane mold 301 is installed on the MOKE testing system, and the magnetization curve of the unstrained film sample 302 placed on the surface of the mold 301 is obtained using the longitudinal mode. Measurement, the hard-axis magnetization curve is shown as the solid line in Figure 2, and the anisotropy field H of the unstrained thin film sample 302 is obtained k1 =170Oe;

[0041] (2) Use a non-magnetic ceramic mold 303 with a convex sh...

Embodiment 2

[0046] In the present embodiment, the flexible magnetic film is FeGa (20nm) / PET film, promptly grows the FeGa film layer that thickness is 20nm on the flexible PET substrate, and the saturation magnetostriction coefficient measurement of this film comprises the following steps:

[0047] (1) Similar Figure 2a As shown, the film sample is placed on the surface of the plane mold, and the mold does not apply strain to the film sample to obtain a strain-free film sample; the plane mold is installed on the MOKE test system, and the unstrained film placed on the plane mold surface is used in the longitudinal mode The magnetization curve of the sample is measured, and the hard-axis magnetization curve is shown as the solid line in Figure 3, and the anisotropy field H of the unstrained film is obtained k1 =250Oe;

[0048] (2) Similar Figure 2b As shown, using a convex non-magnetic mold with a fixed radius of curvature ρ=7.4cm, the film sample is placed on the curved surface of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for measuring a flexible magnetic film saturated magnetostriction coefficient. The method comprises the steps of: adopting a nonmagnetic mould which is made of a nonmagnetic material and has a fixed radius of curvature to generate strain on a flexible magnetic film so as to obtain a stress difference deltasigma between the condition of applied stress and the condition of no stress; then utilizing a magneto-optic kerr effect testing system to measure variable quantity deltaHK of an anisotropy field of the flexible magnetic film sample at the presence of strain and at the absence of the strain; and directly calculating to obtain a saturated magnetostriction coefficient gammas of the flexible magnetic film through a saturated magnetostriction coefficient formula gammas=deltaHkMs / (3deltasigma). Compared with the conventional magnetostriction coefficient measurement method of the magnetic film, the method for measuring the flexible magnetic film saturated magnetostriction coefficient, disclosed by the invention, has the advantages of high measurement precision, simple and practicable performances, low cost and good application foreground.

Description

technical field [0001] The invention relates to the technical field of measuring the magnetostriction coefficient of magnetic materials, in particular to a method for measuring the saturation magnetostriction coefficient of a flexible magnetic film. Background technique [0002] Different magnetic substances have different deformation amounts under the action of a magnetic field, and the magnetostriction coefficient λ is usually used to characterize the deformation amount, that is, λ=ΔL / L. The saturation magnetostriction coefficient λs of ordinary magnetic materials is about 10 -5 , the saturation magnetostriction coefficient of the giant magnetostrictive amorphous film can reach 10 -4 . Therefore, the magnetostrictive effect of the giant magnetostrictive film is much larger than that of ordinary magnetic materials, and it has a good application prospect in the stress sensing and magnetic driving of microelectromechanical systems (MEMS). [0003] Magnetostrictive films ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01R33/18
Inventor 詹清峰张晓山刘宜伟代国红李润伟
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com