Magic tape with magnetic health care function and manufacture method thereof

A manufacturing method and technology of Velcro, which can be used in textiles, papermaking, fiber processing, etc., and can solve problems such as the inability to meet the multi-faceted needs of users.

Inactive Publication Date: 2013-01-09
WUXI PAIHO TEXTILES CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a magnetic health-care function hook and loop and its manufacturing method, aiming to solve the problem that the existing hook and loop only has the function of a fastener and cannot meet the multi-faceted needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1: carry out as follows:

[0040] 1) Put the Velcro into the exhaust dyeing machine for cleaning, and the formula of the cleaning working solution for every 200kg of fabric processed is:

[0041] Emulsifier E1300 900 g

[0042] Caustic soda PJ 300 g

[0043] Water 3800 kg.

[0044] 2) Use a mixer to mix titanate and magnetic powder evenly. The weight percentage of titanate and magnetic powder is:

[0045] Titanate coupling agent TMC-981 10%

[0046] Magnetic powder 90%.

[0047] 3) Mix polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin evenly with a mixer to make a film-forming agent. The weight percentage of polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin is:

[0048] Polyurethane resin YC-1900NDS 30%

[0049] MEK 45%

[0050] Acrylic resin SK7011 10%

[0051] Cross-linking agent CA-861 15%

[0052] 4) In the mixer, add the modified magnetic powder and silane coupling agent to the film-forming...

Embodiment 2

[0057] Embodiment 2: carry out as follows:

[0058] 1) Put the Velcro into the exhaust dyeing machine for cleaning, and the formula of the cleaning working solution for every 195kg of fabric processed is:

[0059] Emulsifier E1300 800 g

[0060] Caustic soda PJ 250 g

[0061] Water 3400 kg

[0062] 2) Use a mixer to mix titanate and magnetic powder evenly. The weight percentage of titanate and magnetic powder is:

[0063] Titanate coupling agent TMC-981 8%

[0064] Magnetic powder 92%

[0065] 3) Mix polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin evenly with a mixer to make a film-forming agent. The weight percentage of polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin is:

[0066] Polyurethane resin YC-1900NDS 25%

[0067] MEK 50%

[0068] Acrylic resin SK7011 15%

[0069] Cross-linking agent CA-861 10%

[0070]4) In the mixer, add the modified magnetic powder and silane coupling agent to the film-forming age...

Embodiment 3

[0075] Embodiment 3: carry out as follows:

[0076] 1) Put the Velcro into the exhaust dyeing machine for cleaning, and the formula of the cleaning working solution for every 190kg of fabric processed is:

[0077] Emulsifier E1300 700 g

[0078] Caustic soda PJ 200 g

[0079] Water 3000 kg

[0080] 2) Use a mixer to mix titanate and magnetic powder evenly. The weight percentage of titanate and magnetic powder is:

[0081] Titanate coupling agent TMC-981 5%

[0082] Magnetic powder 95%

[0083] 3) Mix polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin evenly with a mixer to make a film-forming agent. The weight percentage of polyurethane resin, methyl ethyl ketone, crosslinking agent and acrylic resin is:

[0084] Polyurethane resin YC-1900NDS 20%

[0085] MEK 45%

[0086] Acrylic resin SK7011 20%

[0087] Cross-linking agent CA-861 15%

[0088] 4) In the mixer, add the modified magnetic powder and silane coupling agent to the film-forming ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is suitable for the field of magic tape production and provides a magic tape with a magnetic health care function and a manufacture method thereof. The method comprises the steps of utilizing a stirrer to evenly mixing titanate with magnetic powder; utilizing the stirrer to evenly mixing polyurethane resin, methyl ethyl ketone, cross-linking agents and acrylic resin to prepare film-forming agents with high strength and elasticity in the stirrer, adding modified magnetic powder and silane coupling agents into the film-forming agents, and mixing evenly to obtain magnetic slurry; and performing coating finishing on the back face of the magic tape through the magnetic slurry to form a magnetic slurry film on a fabric, and drying the magic tape at the temperature of 100-105 DEG C after the coating finishing is performed. The magic tape with the magnetic health care function has the function of a fastening part and further has the health care function.

Description

technical field [0001] The invention belongs to the production field of hook and loop fasteners, and in particular relates to a magnetic health-care functional hook and loop fastener and a manufacturing method thereof. Background technique [0002] Velcro is widely used in clothing, medical equipment, sports equipment, travel product fasteners, with the continuous improvement of people's quality of life and the rapid development of clothing, medical equipment, sports equipment, travel products, people are increasingly demanding these Fasteners not only have the function of fasteners, but also have health care functions. Contents of the invention [0003] The purpose of the present invention is to provide a magnetic health-care function hook and loop fastener and its manufacturing method, aiming to solve the problem that the existing hook and loop fastener only has the function of a fastener and cannot meet the multi-faceted needs of users. [0004] The purpose of the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/564D06M15/263D06M13/513D06M11/00D06M13/50
Inventor 郑国烟王其刘昌杰施奕良
Owner WUXI PAIHO TEXTILES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com