A kind of thermoplastic resin composite material, preparation method and application thereof

A thermoplastic resin and composite material technology, which is applied in the field of thermoplastic resin composite materials and preparation, can solve the problems of difficult recycling and reuse, difficult to repair damage, poor impact resistance, etc., and achieves easy acquisition, easy repair, and good impact resistance. Effect

Active Publication Date: 2015-10-14
滁州格美特科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, SMC doors still have some defects, such as poor impact resistance, difficult repair of damage, environmental pollution caused by the use of a large amount of solvents during production, and difficulty in recycling and reuse, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermoplastic resin composite material, preparation method and application thereof
  • A kind of thermoplastic resin composite material, preparation method and application thereof
  • A kind of thermoplastic resin composite material, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Continuous Glass Fiber Reinforced Polypropylene Composites for Minivan Doors

[0051] formula:

[0052] Continuous glass fiber (fiber length: 120 meters): 10 kg (40% by weight)

[0053] Polypropylene resin: 7.5 kg (30% by weight)

[0054] Flame retardant decabromodiphenylethane: 3.5 kg (14% by weight)

[0055] Flame retardant antimony trioxide: 1 kg (4% by weight)

[0056] Anti-ultraviolet agent UV531: 2.25 kg (9% by weight)

[0057] Antioxidant 168: 0.75 kg (3% by weight)

[0058] Such as figure 1 As shown, the thermoplastic resin composite material, that is, the unidirectional glass fiber polypropylene impregnated tape, was prepared first. Unwind the continuous glass fiber roll 1 and pull out the continuous glass fiber bundle 2, through the godet roller 3 and the godet roller 4 rely on the action of tension to make the glass fiber bundle open and flatten to form a unidirectional glass fiber cloth. The number of required fiber bundles is 60. Mix polypropylene r...

Embodiment 2

[0064] Continuous glass fiber reinforced polypropylene composite freight train door

[0065] formula:

[0066] Continuous glass fiber (fiber length 250 meters): 30 kg (60% by weight)

[0067] Polypropylene resin: 12.5 kg (25% by weight)

[0068] Flame retardant decabromodiphenylethane: 3.5 kg (7% by weight)

[0069] Flame retardant antimony trioxide: 1 kg (2% by weight)

[0070] Anti-ultraviolet agent UV531: 1.25 kg (2.5% by weight)

[0071] Anti-ultraviolet agent light stabilizer 944: 1 kg (2.0% by weight)

[0072] Antioxidant 1010: 0.75 kg (1.5% by weight)

[0073] First, a thermoplastic resin composite material, that is, a unidirectional glass fiber polypropylene impregnated tape, is prepared. Unwind the continuous glass fiber roll and pull out the continuous glass fiber bundles, through the godet roller and the godet roller rely on the action of tension to make the glass fiber bundles open and flatten to form a unidirectional glass fiber cloth. The number of require...

Embodiment 3

[0079] Carbon fiber reinforced nylon 66 high strength bulletproof door

[0080] formula:

[0081] Carbon fiber T300 (fiber length 300 meters): 16 kg (80% by weight)

[0082] Nylon 66: 4 kg (20% by weight)

[0083] Flame retardant: 0

[0084] Anti-UV agent: 0

[0085] Antioxidant: 0

[0086]Firstly, a thermoplastic resin composite material, that is, a unidirectional carbon fiber polypropylene impregnated tape, is prepared. Unwind the continuous carbon fiber roll and pull out the continuous carbon fiber bundle, through the godet roller and the godet roller rely on the action of tension to make the carbon fiber bundle open and flatten to form a unidirectional carbon fiber cloth. The number of required fiber bundles was 50. Nylon 66 is melted and extruded by a screw extruder and injected into the dipping tank, and then the unidirectional carbon fiber cloth after the stretched yarn is laid flat is passed through the dipping tank to impregnate the unidirectional carbon fiber c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention falls into the technical field of resin material, and discloses thermoplastic resin composite material and a preparation method and application thereof. The thermoplastic resin composite material comprises 40-80 wt.% of continuous fibers, 20-30 wt.% of thermoplastic resin, 0-18 wt.% of a flame retardant, 0-9 wt.% of an anti-ultraviolet agent and 0-3 wt.% of an antioxidant. The preparation method of the thermoplastic resin composite material includes unreeling, spreading and laying fibers; impregnating unidirectional fiber fabrics; cooling and flattening; and coiling and forming. Also disclosed is a method for manufacturing an automobile door from the thermoplastic resin composite material, which includes laying impregnated unidirectional fiber tapes; molding the impregnated tapes under heating and pressing into composite sheet material; preheating the composite material; and press molding the composite material in a mold. The inventive composite automobile door has the advantages of integral molding, excellent overall properties, good impact resistance, resistance to damage, resistance to permanent deformation, etc.

Description

technical field [0001] The invention belongs to the technical field of resin materials, and in particular relates to a thermoplastic resin composite material, a preparation method and an application thereof. Background technique [0002] Thermoplastic resin composites, especially continuous fiber-reinforced thermoplastic resin composites, have many outstanding performance advantages, such as good impact resistance, easy repair after damage, long-term storage of prepregs, and recycling and reuse of products. Therefore, it has been greatly developed in recent years, and the corresponding preparation technology has also obtained great breakthroughs. However, since our country's thermoplastic composite materials are still in the initial stage of research, the variety is relatively single, and the molding process is not very mature, and the scope of application needs to be further broadened. [0003] At present, most of the doors of vehicles in our country are made of steel. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L101/00C08L23/12C08K13/04C08K7/14C08L77/06C08K7/06B29C70/50B29C43/24B29C43/30
Inventor 赵磊
Owner 滁州格美特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More