Halogen-free flame-retarding polystyrene composite material and preparation method thereof

A polystyrene and composite material technology, which is applied in the field of polystyrene composite flame retardant materials, can solve the problems affecting the physical and mechanical properties and processing properties of the flame retardant materials, and the addition amount is large, and achieves an obvious charring effect and is not easy to achieve. Ignition, good compatibility

Inactive Publication Date: 2015-03-25
TAIYUAN UNIV OF TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic flame retardants have flame retardant and smoke suppression effects at the same time, and do not produce toxic and corrosive gases when burned, but they are added in large amounts, so they seriously affect the physical and mechanical properties and processing properties of the flame retardant materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The first step is to prepare the raw materials

[0021] The raw materials for preparing the halogen-free flame-retardant polystyrene composite material were weighed according to the following parts by weight: 4.5 parts of polystyrene, 1.8 parts of polyphenylene ether, and 3.7 parts of expanded graphite;

[0022] Step two, drying

[0023] Drying the polyphenylene ether at 118°C for 5.5 hours, while drying the expanded graphite at 80°C for 4 hours;

[0024] The third step, high mix

[0025] Mix the expanded graphite and polyphenylene ether evenly with a high-speed mixer to obtain a powder mixture;

[0026] The fourth step, extrusion molding

[0027] The polystyrene is fed into the twin-screw extruder from the main feeding port and the powder mixture is fed into the twin-screw extruder from the side feeding port for melt extrusion molding. The extrusion parameters of the twin-screw extruder are: the screw speed is 300r / min, the barrel temperature is 228°C, the head te...

Embodiment 2

[0029] The first step is to prepare the raw materials

[0030] The raw materials for preparing the halogen-free flame-retardant polystyrene composite material were weighed according to the following parts by weight: 6.4 parts of polystyrene, 1.6 parts of polyphenylene ether, 2 parts of composite nitrogen-phosphorus flame retardant; in the composite nitrogen-phosphorus flame retardant, melamine, The weight ratio of pentaerythritol and ammonium polyphosphate is 4:8:4.5;

[0031] Step two, drying

[0032] Dry the polyphenylene ether at 120°C for 4 hours, and at the same time dry the composite nitrogen-phosphorus flame retardant at 83°C for 5.5 hours;

[0033] The third step, high mix

[0034] Use a high-speed mixer to mix the composite nitrogen-phosphorus flame retardant and polyphenylene ether evenly to obtain a powder mixture;

[0035] The fourth step, extrusion molding

[0036] The polystyrene is fed into the twin-screw extruder from the main feeding port and the powder mi...

Embodiment 3

[0038] The first step is to prepare the raw materials

[0039] The raw materials for preparing the halogen-free flame-retardant polystyrene composite material were weighed according to the following parts by weight: 5.2 parts of polystyrene, 1.3 parts of polyphenylene ether, 3.5 parts of composite nitrogen-phosphorus flame retardant; melamine, The weight ratio of pentaerythritol and ammonium polyphosphate is 4:8:7;

[0040] Step two, drying

[0041] Dry the polyphenylene ether at 132°C for 3.5 hours, and at the same time dry the composite nitrogen-phosphorus flame retardant at 90°C for 3 hours;

[0042] The third step, high mix

[0043] Use a high-speed mixer to mix the composite nitrogen-phosphorus flame retardant and polyphenylene ether evenly to obtain a powder mixture;

[0044] The fourth step, extrusion molding

[0045] The polystyrene is fed into the twin-screw extruder from the main feeding port and the powder mixture is fed into the twin-screw extruder from the sid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a halogen-free flame-retarding polystyrene composite material and a preparation method thereof, which belong to the technical field of polystyrene composite flame-retarding materials and aim at solving the technical problems and providing a smoke-free composite material formed by polystyrene and a halogen-free flame retardant and a method for preparing the smoke-free composite material. The technical scheme is that the halogen-free flame-retarding polystyrene composite material is formed by compositing, by weight, 4-7 parts of the polystyrene, 1-2 parts of polyphenyl ether and 2-4 parts of intumescent flame retardant. The preparation method of the composite material comprises the steps of 1 preparing raw materials, 2 drying, 3 high-mixing and 4 extruding and molding. The fire retardant treatment is performed to the polystyrene by means of the halogen-free flame retardant, the flame retardant is compatible with a base body well, produced flame-resistant polystyrene is not easily ignited, the char forming effect is obvious, smoke and melting-drop phenomenon are not caused, heat stability is good, and limiting oxygen index can reach to 30.2%.

Description

technical field [0001] The invention discloses a halogen-free flame-retardant polystyrene composite material and a preparation method thereof, belonging to the technical field of polystyrene composite flame-retardant materials. Background technique [0002] Flame retardants can be divided into inorganic flame retardants and organic flame retardants. Inorganic flame retardants have flame retardant and smoke suppression effects at the same time, and do not produce toxic and corrosive gases when burned, but they are added in large amounts, so they seriously affect the physical and mechanical properties and processing properties of the flame retardant materials. Among the organic flame retardants, the halogen-based flame retardants have good flame-retardant effects. During the combustion process, the halogen-containing flame retardants will produce a large amount of smoke and harmful gases such as hydrogen halide, which will have adverse effects on the human body and the environ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K13/02B29C48/92
CPCB29C47/92B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895B29C2948/92904
Inventor 晏泓张猛王慧芳董波魏丽乔许并社
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com