Ardealite road base course material and preparation method thereof

A technology of road base and phosphogypsum, applied in the field of road construction materials, can solve the problem of no patent application for phosphogypsum, and achieve the effects of broadening utilization channels, reducing production energy consumption, and widening market prospects.

Inactive Publication Date: 2012-06-13
GUIZHOU KAILIN PHOSPHOGYPSUM INTEGRATION UTILIZATION
View PDF10 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there is no patent application for using phosphogypsum as a road (road) base material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] (1) Crush phosphogypsum so that its particle size is below 5mm;

[0022] (2) Mix 200kg of phosphogypsum, 100kg of gravel, and 100kg of water-quenched slag according to the ratio of 1:0.5:0.5 to obtain 400kg of material A;

[0023] (3) Mix 1 kg of polycarboxylate superplasticizer with material A according to the ratio of 1:400 to obtain 401 kg of material B;

[0024] (4) 4 kg of diethylaminopropylamine was added to material B, and mixed uniformly to obtain 405 kg of material C;

[0025] (5) Add 80kg of water to the material C and stir evenly to get the finished product—485 kg of phosphogypsum road base material in total.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an ardealite road base course material and a preparation method thereof. The ardealite road base course material is prepared from the following raw materials in parts by weight: 40-80 parts of ardealite, 0.5-5 parts of diethylaminopropylamine, 0.1-0.5 part of a polycarboxylic acid water reducing agent, 10-40 parts of sandstone and 5-40 parts of water quenching slag. The preparation method comprises the following steps of: (1) dehydrating ardealite and crushing; (2) uniformly mixing the ardealite, sandstone and water quenching slag to obtain a material A; (3) uniformly mixing the polycarboxylic acid water reducing agent with the material A to obtain a material B; (4) adding the diethylaminopropylamine into the material B to obtain a material C; and (5) adding water into the material C, and stirring uniformly to obtain a finished product. In the method, the ardealite is taken as a major raw material, so that the utilization way of ardealite is expanded, the environmental protection stress is relieved, comprehensive utilization production energy consumption of ardealite is lowered, and the ardealite road base course material has a wide market prospect and is consistent with the requirements of recycling economy and sustainable development. The ardealite road base course material has the advantages of reasonable formula, simple preparation method and durability, and is suitable for road construction in ardealite-containing regions.

Description

technical field [0001] The invention relates to a phosphogypsum road base material and a preparation method thereof, belonging to the field of road construction materials. Background technique [0002] Phosphogypsum is an industrial by-product produced in the production process of wet-process phosphoric acid. It belongs to chemical gypsum and is an air-hardening material. Its characteristic is to soften when it meets water. Phosphogypsum has a large amount and pollutes the environment. At present, there are two types of phosphogypsum utilization, one is to fry hemihydrate gypsum first, then add water to change its crystal lattice to produce gypsum products; the other is to use phosphogypsum, cement or water-quenched slag, and quicklime as the main raw materials. Gypsum bricks produced by steam curing. The above two phosphogypsum utilization methods are for the production of building materials. There are certain technical difficulties and energy consumption in the productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14B09B3/00
Inventor 邓竹林杨步雷杨永彬刘敏李泽钢罗建国刘媛向前勇
Owner GUIZHOU KAILIN PHOSPHOGYPSUM INTEGRATION UTILIZATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com