A technology of white ceramics and natural zeolite, applied in the field of ceramic materials, can solve the problems of low technical content, poor strength and hardness, and low added value of products, and achieve expanded application fields, high Shore hardness, good mechanical properties and physical chemistry performance effect

Inactive Publication Date: 2012-02-15
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The second is to sell zeolite powder, which is used as an additive for water treatment, feed and fertilizer or as a chemical filler. The technical content is low and the added value of the product is not high.
[0004] Using natural zeolite powder as raw material, the ceramics directly prepared are brick red, the R457 whiteness value is only 24, and the strength and hardness are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of method utilizing natural zeolite to prepare white pottery, it comprises the steps:

[0024] 1) Natural clinoptilolite (produced in No. 2 mining area of ​​Dashi particle clinoptilolite rock mining area, Nenjiang County, Heilongjiang Province) was crushed and ground to 100 mesh to obtain clinoptilolite powder.

[0025] 2) Mix 25g of clinoptilolite powder, 1.7g of NaCl, and 13.25g of NaOH, add 75mL of distilled water, ultrasonically disperse, heat in a water bath at 90°C, supplemented by electric stirring for 12h, then stand for 48h, wash and dry to obtain modified zeolite powder .

[0026] 3) Mix the clinoptilolite powder and the modified zeolite powder at a mass ratio of 2:1 (that is, the content of the modified zeolite powder in the raw material is 33.33%), press into tablets under a pressure of 20MPa, sinter at 700°C, and keep warm for 5h. The heating rate is 5°C / min, and the white zeolite ceramics are obtained by cooling with the furnace.

[0027] The wash...

Embodiment 2

[0034] A kind of method utilizing natural zeolite to prepare white pottery, it comprises the steps:

[0035] 1) Natural clinoptilolite (produced in No. 2 mining area of ​​Dashi particle clinoptilolite rock mining area, Nenjiang County, Heilongjiang Province) was crushed and ground to 100 mesh to obtain clinoptilolite powder.

[0036] 2) Mix 25g of clinoptilolite powder, 15g of NaCl, and 13.25g of NaOH, add 75mL of distilled water, and other conditions are the same as in Example 1. The R457 whiteness value recorded is 69.90, the Shore hardness is 79, and the acid resistance is 50.15%. Basicity is 48.46%, and phase is identical with embodiment 1.

Embodiment 3

[0038] A kind of pottery that utilizes natural zeolite to prepare, it comprises the steps:

[0039] 1) Natural clinoptilolite (produced in No. 2 mining area of ​​Dashi particle clinoptilolite rock mining area, Nenjiang County, Heilongjiang Province) was crushed and ground to 100 mesh to obtain clinoptilolite powder.

[0040] 2) Mix 25 g of clinoptilolite powder, 5 g of NaCl, and 4.3 g of NaOH, add 75 mL of distilled water, and other conditions are the same as in Example 1. The measured R457 whiteness value is 69.48, the Shore hardness is 68, the acid resistance is 60.34%, and the alkali resistance Degree is 59.6%, and phase is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
acid resistanceaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing white ceramic by the use of natural zeolite. The method for preparing white ceramic by the use of natural zeolite is characterized by comprising the following steps of: 1) crushing the natural zeolite, and grinding to 100 meshes to obtain a zeolite powder; 2) preparing a modified zeolite powder by adopting one of the following two method: (1) mixingthe zeolite powder, sodium chloride, sodium hydroxide and water according to the mass ratio of 10: (0.6-10): (2-10): 30-45, heating and stirring for 12 hours, staying for 48 hours, washing by the useof water, and drying to obtain the modified zeolite powder; (2) mixing the zeolite powder, a waste alkali liquor in caustic soda industry and water according to the mass ratio of (10-15): (6-12): 45,heating and stirring for 12 hours, staying for 48 hours, washing by the use of water, and drying to obtain the modified zeolite powder; 3) mixing the zeolite powder and the modified zeolite powder with the modified zeolite powder being 10-90 wt% of the zeolite powder and the modified zeolite powder, tabletting for moulding, and sintering at high temperature to obtain the white ceramic. By the adoption of the method, the white ceramic has high R457 white value, high acid fastness, high alkali fastness and high Shore hardness.

Description

technical field [0001] The invention relates to a ceramic material, in particular to a method for preparing white ceramics by using natural zeolite. Background technique [0002] Zeolite is a family of hydrous aluminosilicate minerals with a framework structure, the chemical formula is: A m B p o 2p ·nH 2 O, the structural formula is A (x / q) [(AlO 2 ) x (SiO 2 ) y ]n(H 2 O), wherein: A is Ca, Na, K, Ba, Sr and other cations, B is Al and Si, q is the valence of cations, m is the number of cations, n is the number of water molecules, x is the number of Al atoms, and y is Si The number of atoms, (y / x) is usually between 1 and 5, and (x+y) is the number of tetrahedrons in the unit cell. Its chemical composition is mainly Al 2 o 3 , SiO 2 、H 2 O and alkali or alkaline earth metals, of which Al 2 o 3 +SiO2 2 About 80%. [0003] At present, most of the zeolite is used as cement mixture, which is used in the construction industry. In addition, it is also used to pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B35/622C04B35/64
Inventor 李珍金成国李飞沈毅吴剑芳孙炜
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap