Halogen-free flame-retardant nylon 66 composite material and preparation method thereof

A composite material, flame-retardant technology, applied in the field of polymers, which can solve problems such as toxicity and restrictions

Active Publication Date: 2012-02-01
古道尔工程塑胶(深圳)有限公司 +1
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional halogenated flame retardants are limited in application due to their toxicity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant nylon 66 composite material and preparation method thereof
  • Halogen-free flame-retardant nylon 66 composite material and preparation method thereof
  • Halogen-free flame-retardant nylon 66 composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] In addition, the present invention also provides a preparation method of a halogen-free flame-retardant nylon 66 composite material, comprising the following steps:

[0032] Weigh each component by weight as follows:

[0033]

[0034]

[0035] Among them, the halogen-free flame retardant is a mixture of halogen-free organic phosphine flame retardants and intumescent phosphorus-nitrogen flame retardants;

[0036] After mixing the above-mentioned raw materials except glass fiber evenly, extrude to granulate, and add glass fiber during extrusion, wherein the temperature during extrusion is controlled at 200-250°C.

[0037] The above-mentioned halogen-free flame-retardant nylon 66 composite material is made of nylon 66 resin, halogen-free flame retardant, glass fiber, nucleating agent and other additives through high-temperature extrusion and granulation. The material has a good flame-retardant effect and can reach UL-94. V-0 level, in line with flame retardant requi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a halogen-free flame-retardant nylon 66 composite material. The composite material is prepared from the following components in parts by weight: 53-67 parts of nylon 66 resin, 0.3-0.4 part of coupling agent, 17-21 parts of halogen-free flame retardant, 0.2-0.4 part of nucleating agent, 0.3-0.4 part of antioxidant, 0.2-0.3 part of lubricant and 15-25 parts of fiberglass, wherein the halogen-free flame retardant is a mixture of a halogen-free organic phosphorus flame retardant and an expandable phosphorus-nitrogen flame retardant. The halogen-free flame-retardant nylon 66 composite material is prepared from nylon 66 resin, the halogen-free flame retardant, fiber glass, the nucleating agent and other auxiliary agents by high-temperature extrusion and granulation, thus the material has good flame-retardant effect, can reach V-0 level in UL-94 and meets the flame-retardant requirements; and at the same time, the flame retardant is prepared by mixing the halogen-free organic phosphorus flame retardant and the expandable phosphorus-nitrogen flame retardant, thus the composite material has no pollution, meets the environmental protection requirements, has excellent comprehensive properties and can be widely popularized and applied. In addition, the invention also relates to a preparation method of the halogen-free flame-retardant nylon 66 composite material.

Description

【Technical field】 [0001] The invention relates to the field of polymers, in particular to a halogen-free flame-retardant nylon 66 composite material and a preparation method thereof. 【Background technique】 [0002] Nylon is an excellent engineering plastic with excellent mechanical properties, heat resistance, wear resistance, self-lubrication and good processability. Its application ranks first among the five major engineering plastics and is widely used in automobiles, home appliances, Toys and other related industries. With the rapid development of science and technology, people's requirements for materials are becoming more and more stringent, and the requirements for materials' flame retardancy and environmental protection are getting higher and higher. The application of traditional halogenated flame retardants is limited due to their toxicity. 【Content of invention】 [0003] Based on this, it is necessary to provide an environmentally friendly and non-toxic haloge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/06C08K13/04C08K7/14C08K5/49B29B9/06B29C47/92B29C48/92
CPCB29C48/04
Inventor 刘辉刘卫东
Owner 古道尔工程塑胶(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com