A circulating cooling deslagging method in continuous hot dip of zinc-aluminium alloys

A circulating cooling and hot-dip galvanizing technology, applied in hot-dip galvanizing process, metal material coating process, coating, etc., can solve problems affecting production efficiency, difficult to remove bottom dross, increase production cost, etc., to reduce downtime The time for slag removal, the effect of improving heat exchange capacity and improving production efficiency

Active Publication Date: 2011-08-31
CHANGZHOU UNIV
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, a serious problem on the hot-dip galvanizing production line is the zinc slag problem. Compared with the zinc pool, the composition of the zinc pool changes greatly, especially when silicon and other elements are added to the zinc-aluminum pool, which will make the phase relationship more complicated; the zinc slag phase in the zinc-aluminum-zinc pool contains Zinc FeAl3 and Fe-Al-Si intermetallic compound, compared with hot-dip pure zinc zinc pool density, zinc-aluminum pool density is smaller, 55% Al-Zn zinc-aluminum pool is about 1/2 of pure zinc plating; therefore, it is easier to form suspended dross and bottom dross in zinc-aluminum pools, and the causes and influencing factors of zinc dross are much more complicated than those in hot-dip pure zinc-zinc pools; Many production lines have zinc dross problems that plague people. For example, Bluescope Steel in Australia has three Galvalume production lines that have serious zinc dross problems. Many domestic Galvalume production lines also have zinc dross problems.
[0004] The main problems of zinc-aluminum products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A circulating cooling deslagging method in continuous hot dip of zinc-aluminium alloys
  • A circulating cooling deslagging method in continuous hot dip of zinc-aluminium alloys
  • A circulating cooling deslagging method in continuous hot dip of zinc-aluminium alloys

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] Introduce this embodiment in detail below in conjunction with the accompanying drawings: this embodiment is implemented under the premise of the technical solution of the present invention, and detailed implementation methods and processes are provided, but the protection scope of the present invention is not limited to the following implementation example.

[0040] to combine Figure 1 ~ Figure 4 As shown, the method for circulating cooling and cooling and deslagging in continuous hot-dip galvanized aluminum of the present invention comprises a galvanized zinc pot 1 and a circulating cooling and cooling and deslagging device 6, and the installation position of the circulating cooling and cooling and deslagging device 6 is lower than that The height of the zinc liquid level 17 of the zinc-zinc pot 1 is h, and the height difference is 20 to 40 cm. The hot-dip galvanizing process of the steel plate is completed in the galvanized zinc pot 1, and the circulating cooling coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method in the field of metal smelting technology, particularly to a circulating cooling deslagging method in continuous hot dip of zinc-aluminium alloys. The method is characterized by placing a circulating cooling deslagging apparatus in zinc-aluminium liquid in a galvanized zinc pot, wherein the apparatus has an internal temperature lower than the temperature of the zinc-aluminium liquid in the galvanized zinc pot and is provided with a circuitous groove inside and a zinc dross collector at the bottom, with the circuitous groove being open-ended at two ends, provided with a zinc-aluminium liquid driving device at an inlet and embedded with a honeycomb-shaped cooling pipe equipped with an inlet and an outlet; driving the zinc-aluminium liquid to enter the circuitous groove from the inlet of the circuitous groove, pressing molten metal liquid with low temperature and low melting point in the honeycomb-shaped cooling pipe to cool the zinc-aluminium liquid in the circuitous groove when the zinc-aluminium liquid flows through the circuitous groove, reducing the temperature of the zinc-aluminium liquid for the precipitation and growth of the zinc dross from the zinc-aluminium and deposition of the zinc dross in the zinc dross collector at the bottom, and completing the deslagging and purifying of the zinc-aluminium liquid after the zinc-aluminium liquid, from which the zinc dross is precipitated, flows back to the galvanized zinc pot through the outlet of the circuitous groove. The method in the invention can effectively remove the zinc dross in a zinc bath.

Description

technical field [0001] The invention relates to a method in the technical field of metal smelting, in particular to a method for removing slag by circulating cooling in continuous hot-dip galvanized aluminum. Background technique [0002] Hot-dip galvanizing is a more effective and convenient steel anti-corrosion method. Its coating has excellent sacrificial anti-corrosion effect; hot-dip aluminum coating is compact and has a long service life; The characteristics and cathodic protection characteristics of zinc, the performance of the coating is superior to that of a single element coating, and the anti-corrosion performance is several times higher than that of pure zinc coating, so it is widely used. Because galvanized aluminum sheets, such as Galvalume coated steel sheets, have excellent comprehensive properties and Beautiful appearance, there is a tendency to replace aluminum-coated sheets and some galvanized steel sheets with this coated sheet abroad, forming a zinc-alum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C2/00
Inventor 苏旭平彭浩平王建华涂浩王鑫铭
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products