Environment-friendly dual-curing vacuum coating primer special for automobile wheel hub

A dual-curing technology for automobile wheels, which is applied in the direction of epoxy resin coatings, coatings, polyurea/polyurethane coatings, etc., can solve the problems of uncurable shadow parts and weak metal surface adhesion, etc., to achieve strong adhesion and Good plating performance, good leveling and covering effect

Inactive Publication Date: 2011-08-31
YIXING HONGTAI CHEM
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Only one layer of primer can cover the defects of the material well; the coating is good and can withstand high temperature of 170 ℃; the shadow part can be cured by itself through isocyanate, which solves the problem of poor adhesion of ordinary UV primer on the metal surface. The problem that the shadow part cannot be cured

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly dual-curing vacuum coating primer special for automobile wheel hub
  • Environment-friendly dual-curing vacuum coating primer special for automobile wheel hub
  • Environment-friendly dual-curing vacuum coating primer special for automobile wheel hub

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention will be further elaborated below with specific examples, which are only for illustration and do not limit the scope of the invention.

[0028] Preparation of primer:

[0029] (1) Put reactive diluent, aliphatic epoxy acrylate, aliphatic urethane diacrylate and novolac epoxy acrylate into the reaction kettle, heat and stir at 45°C for 1 hour to dissolve;

[0030] (2) Add isocyanate-containing urethane acrylate and photoinitiator into the reactor, and stir for 0.5h;

[0031] (3) Finally, add the additives into the reaction kettle, stir at high speed for 0.5h, filter with a 500-mesh filter cloth, and finally pack it in barrels.

[0032] The following examples were all prepared as above.

[0033] Primer formulation:

[0034] Each embodiment carries out batching according to the mass ratio in Table 1 and Table 2 respectively and prepares the dual curing vacuum coating primer special for environment-friendly type automobile hub of the present inventio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly dual-curing vacuum coating primer special for an automobile wheel hub, which is prepared from the following components in percentage by mass: 25-35% of NCO-containing polyurethane acrylate, 5-10% of aliphatic polyurethane diacrylate, 5-10% of phenolic epoxy acrylate, 10-20% of aliphatic epoxy acrylate, 20-35% of reactive diluent, 1-5% of photoinitiator and 0.1-1% of assistant. The primer has the advantages of energy saving, environment friendliness, strong adhesive force on the metal surface, excellent leveling property and high gloss; the primer can well cover defects on the material only after one primer coating is applied, thereby having favorable covering power; the primer has favorable adhesive force with both the wheel hub material and the vacuum coating layer; after the primer is baked at 170 DEG C for 2 hours, the surface looks no difference; and the primer also has recoating property.

Description

technical field [0001] The invention belongs to the dual curing technology in the field of ultraviolet curing coatings, in particular to a dual curing vacuum electroplating primer specially used for automobile wheel hubs. Background technique [0002] With the rapid development of my country's automobile industry, the demand for automobile wheels will increase sharply as an accessory product for automobiles. Hub materials mainly include steel materials, alloy materials, and composite materials. The surface treatment methods are mainly coating (water electroplating and vacuum electroplating). Among them, the water electroplating method has disadvantages such as complex process, high cost, high energy consumption, and serious environmental pollution, and it is bound to be eliminated by wheel hub manufacturers. The vacuum coating method can not only overcome the shortcomings of the electroplating method, but also obtain a bright, heat-resistant, and decorative surface, and wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D163/10
Inventor 吴玉民戴梁锋
Owner YIXING HONGTAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products