A technology of automatic inflation and tire repair fluid, applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of slow tire repair speed, ozone layer destruction, poor antifreeze effect, etc., and achieve fast spraying speed and frost resistance Good, long shelf life effect

Inactive Publication Date: 2011-05-25
ZHEJIANG UNIV OF TECH
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some traditional tire repair aerosols can only temporarily inflate the deflated tires, and even cause chronic deflation after a period of ti...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automatic inflation tyre-repairing solution
  • Automatic inflation tyre-repairing solution
  • Automatic inflation tyre-repairing solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 60 parts of natural rubber latex

[0042] Polyvinyl formal 6 parts

[0043] 8 parts of ethylene glycol

[0044] 2 parts propylene glycol

[0045] 3 parts sodium lauryl sulfate

[0046] 0.5 parts of diethylamine

[0047] 0.5 parts of ethylenediamine

[0048] 10 parts distilled water

[0049] HFC-134a 100 parts

Embodiment 2

[0051] 60 parts of natural rubber latex

[0052] Polyvinyl formal 6 parts

[0053] 5 parts of ethylene glycol

[0054] Propylene Glycol 5 parts

[0055] Sodium Lauryl Sulfate 2 parts

[0056] Sodium dodecylbenzenesulfonate 1.5 parts

[0057] 0.3 parts of diethylamine

[0058] 0.2 parts of ethylenediamine

[0059] 10 parts distilled water

[0060] HFC-134a 100 parts

Embodiment 3

[0062] 60 parts of natural rubber latex

[0063] Polyvinyl formal 6 parts

[0064] 10 parts of ethylene glycol

[0065] Sodium Lauryl Sulfate 3.5 parts

[0066] 0.2 parts of diethylamine

[0067] 0.3 parts of ethylenediamine

[0068] 10 parts distilled water

[0069] HFC-134a 100 parts

[0070] Each embodiment is all to adopt following preparation method to make,

[0071]a. Preparation of polyvinyl formal: mix polyvinyl alcohol, 10% hydrochloric acid, 37% formaldehyde solution, 10% sodium hydroxide solution and distilled water in the reactor according to the weight ratio of 12:0.3:10:0.4:77.3 made by reaction;

[0072] b. Under stirring at room temperature, sequentially add concentrated natural latex and polyvinyl formal into the reaction kettle, and stir for 70 minutes;

[0073] c. Add water, ethylene glycol, propylene glycol, diethylamine, ethylenediamine, surfactant in another reaction kettle, and stir at room temperature for 70 minutes;

[0074] d. Mix and stir th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Caliberaaaaaaaaaa
Login to view more

Abstract

The invention relates to an automatic inflation tyre-repairing solution. The solution comprises the following raw material components in parts by weight: 50-70 parts of natural latex, 3-10 parts of emulsifier, 10-20 parts of antifreezing agent, 3-5 parts of surfactant, 0.3-1 part of stabilizer, 10-20 parts of distilled water and 100 parts of propellant. The automatic inflation tyre-repairing solution uses natural concentrated latex as main raw material and also uses various main agents such as antifreezing agent, foaming agent, stabilizer and polymerization inhibitor; the product cost is low, the shelf life is long, the period of validity is up to 6 months, the freezing resistance is good so that the solution can be used at -20 DEG C; and the jet velocity is high, the tyre-repairing effect is good, the preparation method is simple and the economic and social benefits are remarkable.

Description

technical field [0001] The invention relates to a self-inflating and leak-trapping mixture for rubber tires and a preparation method thereof. Background technique [0002] Most of the tires used at this stage are pneumatic tires. After being punctured by nails or hard objects on the road surface, it will cause acute deflation. The traditional tire sealant needs to go through a series of processes such as unloading the wheel, removing the tire, and repairing the tire. The procedures are complicated, laborious and time-consuming. Especially when driving in the wild, there is no condition for tire repair. After the tire is punctured, it is impossible to continue driving. [0003] In order to solve the above problems, some people have invented tire repair glue, most of which adopt polyvinyl acetate emulsion or polyvinyl alcohol solution, together with starch, cellulose and inorganic fillers, etc., the sealing composition is relatively simple, fluidity, stability, oxidation resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K3/12C08L7/02
Inventor 张诚贺攀叶银鹏吕翠玉
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka